Preparation method of chlorinated polyethylene rubber

A technology of chlorinated polyethylene and rubber, which is applied in the field of rubber materials, can solve the problems of insufficient tear strength of vulcanized rubber, high reject rate, and product damage, and achieve the effect of excellent appearance, low cost, and high elongation at break

Inactive Publication Date: 2019-02-15
NANCHANG HANGKONG UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Chlorinated polyethylene rubber is a saturated polymer material with excellent heat aging resistance, weather resistance, ozone resistance, oil resistance, flame retardancy, corona resistance and processing performance; chlorinated polyethylene rubber is a non-toxic Self-reinforcing rubber, when used to manufacture wire and cable sheath rubber, the vulcanized rubber will have insufficient tear strength, and the demoulding process will often cause product damage and high scrap rate, so appropriate reinforcement must be used by adjusting the formula agent to improve its performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of chlorinated polyethylene rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Turn on the whole mixer to preheat for 10 minutes, set the temperature to 100°C, set the temperature to automatic, and turn on the air compressor with a pressure of 0.8 ， MPa, the top bolt pressure is set to automatic gear, put in 120 parts of chlorinated polyethylene rubber CPE135A and 23 parts of toughening agent POE1851, cover and mix for 2 minutes, then add 125 parts of talcum powder and 25 parts of plasticizer TP95 respectively, 3 parts of plasticizer TAIC, 1.5 parts of magnesium oxide, 1.5 parts of zinc stearate, inorganic flame retardant Sb 2 o 3 10 parts, cover and mix for 2 minutes, add 45 parts of foundry waste XJ01 reinforcing agent, 0.7 parts of coupling agent KH570, 5 parts of chlorinated paraffin, 2 parts of paraffin, discharge and cool for 350 seconds, discharge temperature 130°C .

[0014] The mixed rubber discharged from the internal mixer is added to the open mill, the roller distance is less than 3 mm, the sheet is pulled 3 times, and the thick fil...

Embodiment 2

[0023] Turn on the whole mixer to preheat for 10 minutes, set the temperature to 100°C, set the temperature to automatic, and turn on the air compressor with a pressure of 0.8 ， MPa, the top bolt pressure is set to automatic gear, put in 120 parts of chlorinated polyethylene rubber CPE135A and 23 parts of toughening agent POE1851, cover and mix for 2 minutes, then add 125 parts of talcum powder and 25 parts of plasticizer TP95 respectively, 3 parts of plasticizer TAIC, 1.5 parts of magnesium oxide, 1.5 parts of zinc stearate, inorganic flame retardant Sb 2 o 3 4 parts, cover and mix for 2 minutes, add 30 parts of casting waste XJ01 reinforcing agent, 0.7 parts of coupling agent KH570, 5 parts of chlorinated paraffin, 2 parts of paraffin, discharge and cool the sheet for 350 seconds, discharge temperature 130°C .

[0024] The mixed rubber discharged from the internal mixer is added to the open mill, the roller distance is less than 3 mm, the sheet is pulled 3 times, and the ...

Embodiment 3

[0029] Turn on the whole mixer to preheat for 10 minutes, set the temperature to 100°C, set the temperature to automatic, and turn on the air compressor with a pressure of 0.8 ， MPa, the top bolt pressure is set to automatic gear, put in 120 parts of chlorinated polyethylene rubber CPE135A and 23 parts of toughening agent POE1851, cover and mix for 2 minutes, then add 125 parts of talcum powder and 25 parts of plasticizer TP95 respectively, 3 parts of plasticizer TAIC, 1.5 parts of magnesium oxide, 1.5 parts of zinc stearate, inorganic flame retardant Sb 2 o 3 12 parts, cover and mix for 2 minutes, add 80 parts of foundry waste XJ01 reinforcing agent, 0.7 parts of coupling agent KH570, 5 parts of chlorinated paraffin, 2 parts of paraffin, discharge for 350 seconds and cool the sheet, discharge temperature 130°C .

[0030] The mixed rubber discharged from the internal mixer is added to the open mill, the roller distance is less than 3 mm, the sheet is pulled 3 times, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of chlorinated polyethylene rubber, and belongs to the field of a rubber material. The chlorinated polyethylene rubber comprises the components in parts bymass: 100 to 140 parts of chlorinated polyethylene rubber CPE135A, 10 to 30 parts of toughening agent POE1851, 20 to 30 parts of a plasticizer TP95, 2 to 4 parts of a plasticizer TAIC, 100 to 200 parts of talcum powder, 0.5 to 2 parts of a coupling agent KH570, 3 to 10 parts of a vulcanizing agent BIPB, 1 to 2 parts of magnesium oxide, 1 to 5 parts of zinc stearate, 2 to 6 parts of chlorinated paraffin, 1 to 5 parts of paraffin, 4 to 12 parts of inorganic flame retardant Sb2O3, and 30 to 80 parts of a casting waste residue XJ01 reinforcing agent; after the components are mixed, the mixture isvulcanized to obtain the product. The invention provides the chlorinated polyethylene rubber which is excellent in appearance, high and medium in hardness, good in demoulding performance, high tear resistance and high in elongation at break.

Description

technical field [0001] The invention relates to the field of rubber materials, in particular to a chlorinated polyethylene rubber. Background technique [0002] Chlorinated polyethylene rubber is a saturated polymer material with excellent heat aging resistance, weather resistance, ozone resistance, oil resistance, flame retardancy, corona resistance and processing performance; chlorinated polyethylene rubber is a non-toxic Self-reinforcing rubber, when used to manufacture wire and cable sheath rubber, the vulcanized rubber will have insufficient tear strength, and the demoulding process will often cause product damage and high scrap rate, so it is necessary to use appropriate reinforcement by adjusting the formula agent to improve its performance. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the present invention intends to develop a chlorinated polyethylene rubber with excellent appearance, medium to high hardness, good mold release pe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/28C08L91/06C08L23/08C08K13/02C08K3/22C08K5/098C08K3/34C08K5/14
CPCC08K2003/222C08L23/286C08L2205/035C08L91/06C08L23/0815C08K13/02C08K3/22C08K3/2279C08K5/098C08K3/34C08K5/14
Inventor 宋贤海
Owner NANCHANG HANGKONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap