Sealant used for hollow glass

A sealant and glass technology, applied in adhesives, adhesive additives, other chemical processes, etc., can solve the problems of insufficient fireproof and high temperature resistance of silicone glue, and can not effectively guarantee the high temperature resistance of insulating glass, so as to achieve long service life , Improve high temperature resistance, improve the effect of flame retardant performance

Inactive Publication Date: 2018-10-30
芜湖市颂晖商贸有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the glass glue used in insulating glass is ordinary silicone glue, and the fireproof and high temperature resistance of silicone glue is not enough to effectively guarantee the high temperature resistance of insulating glass. Therefore, a special glass sealant for insulating glass is needed to solve the above problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A sealant for insulating glass, calculated in parts by weight, comprising the following components:

[0024] 56 parts of organohydroxy silicone, 12 parts of organomethyl silicone, 9 parts of methyl silane, 30 parts of inorganic filler, 14 parts of high temperature resistant auxiliary material, 2 parts of nano-zirconia, 2 parts of aminosilane, 1 part of dibutyltin dilaurate 1 part, 13 parts of rubber, 1 part of starch, 8 parts of dioctyl phthalate, 2 parts of antibacterial agent and 0.4 part of ultraviolet absorber. The rubber is a combination of nitrile rubber and silicone rubber. The antibacterial agent is a mixture of chitin, mustard and copper oxide.

[0025] The preparation method of high temperature resistant auxiliary material comprises the following steps:

[0026] (1) Put the nano-magnesium aluminum hydrotalcite into the absolute ethanol solution, stir and ultrasonically disperse to obtain the dispersion A;

[0027] (2) Weigh graphene oxide in proportion and ...

Embodiment 2

[0030] A sealant for insulating glass, calculated in parts by weight, comprising the following components:

[0031] 50 parts of organohydroxy silicone, 10 parts of organomethyl silicone, 6 parts of methyl silane, 35 parts of inorganic filler, 16 parts of high temperature resistant auxiliary material, 1 part of nano zirconia, 1 part of aminosilane, 1 part of dibutyltin dilaurate 12 parts of rubber, 1 part of sodium alginate, 8 parts of dioctyl phthalate, 1 part of antibacterial agent and 0.2 part of ultraviolet absorber. The rubber is a combination of nitrile rubber and silicone rubber. The antibacterial agent is a mixture of chitin, mustard and copper oxide.

[0032] The preparation method of high temperature resistant auxiliary material comprises the following steps:

[0033] (1) Put the nano-magnesium aluminum hydrotalcite into the absolute ethanol solution, stir and ultrasonically disperse to obtain the dispersion A;

[0034] (2) Weigh graphene oxide in proportion and ad...

Embodiment 3

[0037] A sealant for insulating glass, calculated in parts by weight, comprising the following components:

[0038] 60 parts of organohydroxy silicone, 14 parts of organomethyl silicone, 12 parts of methyl silane, 25 parts of inorganic filler, 10 parts of high temperature resistant auxiliary materials, 3 parts of nano-zirconia, 3 parts of aminosilane, 2 parts of dibutyltin dilaurate 16 parts of rubber, 2 parts of starch, 10 parts of dioctyl phthalate, 3 parts of antibacterial agent and 0.6 part of ultraviolet absorber. The rubber is a combination of nitrile rubber and silicone rubber. The antibacterial agent is a mixture of chitin, mustard and copper oxide.

[0039] The preparation method of high temperature resistant auxiliary material comprises the following steps:

[0040] (1) Put the nano-magnesium aluminum hydrotalcite into the absolute ethanol solution, stir and ultrasonically disperse to obtain the dispersion A;

[0041] (2) Weigh graphene oxide in proportion and add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a sealant used for hollow glass, containing the following components in parts by weight: 50-60 parts of organic hydroxyl silicone, 10-14 parts of organic methyl silicone, 6-12 parts of methyl silane, 25-35 parts of inorganic filler, 10-16 parts of high-temperature resistant accessory, 1-3 parts of nano zirconium oxide, 1-3 parts of amino silicon, 1-2 parts of dibutyltin dilaurate, 12-16 parts of rubber, 1-2 parts of a bonding assistant, 8-10 parts of a plasticizer, 1-3 parts of an antibacterial agent, and 0.2-0.6 part of an ultraviolet absorbent; the high-temperature resistant accessory is prepared by mainly taking nanometer magnesia-alumina hydrotalcite as a matrix and graphene oxide as an assistant, and performing hot pressing and sintering at the temperature of 250-350 DEG C. The sealant has good flame retardance and high temperature resistant performances, and is long in service life.

Description

technical field [0001] The invention belongs to the technical field of sealing materials, and in particular relates to a sealant for insulating glass. Background technique [0002] Insulating glass is a new type of building material with good heat insulation, sound insulation, aesthetics and applicability, and can reduce the weight of buildings. It is a high-efficiency sound-insulating and heat-insulating glass made of two or three pieces of glass, using a high-strength and high-air-tight composite adhesive to bond the glass pieces to the aluminum alloy frame containing the desiccant. The performance of insulating glass is superior to that of ordinary double-layer glass, so it has been recognized by all countries in the world. Insulating glass is to separate two or more pieces of glass evenly with effective support and bond and seal the periphery, so that a dry gas is formed between the glass layers. Space glassware. Its main materials are glass, warm edge spacer, angle bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J183/04C09J11/04C09J11/06C09J11/08C09K3/10
CPCC08K2003/2248C08L2201/02C08L2201/08C08L2205/025C08L2205/035C08L2312/08C09J11/04C09J11/06C09J11/08C09J183/04C09K3/10C09K2003/1078C08L83/04C08L9/02C08L3/02C08L5/08C08K13/02C08K5/12C08K3/22C08K3/26C08K3/042C08K3/36
Inventor 汪泽维汪鹏
Owner 芜湖市颂晖商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com