Wear-resistant paint for bed head boards

A headboard and paint technology, applied in the direction of coating, polyester paint, etc., can solve the problems of not being able to maintain the luster of the headboard for a long time, the paint of the headboard is easy to be worn, and the headboard loses its luster. Flat, not easy to bubble, high surface gloss effect

Inactive Publication Date: 2019-02-15
湖州市南浔三亚家私有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the headboard is often rubbed by the back of the human body, the paint on the headboard is easily worn away, making the headboard easy to lose its luster
The paint layer formed by the existing paint on the headboard is relatively soft, and the paint layer is not wear-resistant. If it is used on the headboard, generally it can only maintain the luster of the headboard in the first three to five years of use, and cannot maintain the bed for a long time. The head plate is shiny
Therefore, the existing paint has the disadvantage of not being able to maintain the luster of the headboard for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Example 1. Wear-resistant headboard paint, configured by the following raw materials in parts by weight, 1.5 parts of methyl ethyl ketone peroxide, 0.25 parts of polysiloxane-polyether copolymer, 7.5 parts of glass powder, 9 parts of nano-silicon carbide powder, 12.5 parts of rutile titanium dioxide 0.3 parts of polymethylphenylsiloxane, 0.7 parts of monoglyceride stearate, 40 parts of glycol, 2 parts of polyethylene water-based wax, 17.5 parts of styrene, 0.8 parts of cobalt naphthenate, butyl acetate 65 parts of ester, 27.5 parts of alkyd resin containing hydroxyl, 0.7 part of hydroxyethyl cellulose, 6 parts of xylene.

[0017] The configuration of paint consists of the following steps,

[0018] a. Methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, monoglyceride stearate, glycol, polyethylene water-based wax, styrene, cobalt naphthenate , butyl acetate, hydroxyl-containing alkyd resin, hydroxyethyl cellulose and xylene were mix...

Embodiment 2

[0023] Example 2. Wear-resistant headboard paint, configured by the following raw materials in parts by weight, 1 part of methyl ethyl ketone peroxide, 0.2 parts of polysiloxane-polyether copolymer, 5 parts of glass powder, 8 parts of nano-silicon carbide powder, 10 parts of rutile titanium dioxide 0.2 parts of polymethylphenylsiloxane, 0.5 parts of monoglyceride stearate, 35 parts of glycol, 1 part of polyethylene water-based wax, 15 parts of styrene, 0.6 parts of cobalt naphthenate, butyl acetate 60 parts of ester, 25 parts of alkyd resin containing hydroxy, 0.5 part of hydroxyethyl cellulose, 5 parts of xylene.

[0024] The configuration of paint consists of the following steps,

[0025] a. Methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, monoglyceride stearate, glycol, polyethylene water-based wax, styrene, cobalt naphthenate , butyl acetate, hydroxyl-containing alkyd resin, hydroxyethyl cellulose and xylene were mixed and stirred...

Embodiment 3

[0030] Example 3. Wear-resistant headboard paint, configured by the following raw materials in parts by weight, 2 parts of methyl ethyl ketone peroxide, 0.3 parts of polysiloxane-polyether copolymer, 10 parts of glass powder, 10 parts of nano-silicon carbide powder, 15 parts of rutile titanium dioxide 0.4 parts of polymethylphenylsiloxane, 0.9 parts of monoglyceride stearate, 45 parts of glycol, 3 parts of polyethylene water-based wax, 20 parts of styrene, 1 part of cobalt naphthenate, butyl acetate 70 parts of ester, 30 parts of alkyd resin containing hydroxyl, 0.9 parts of hydroxyethyl cellulose, 7 parts of xylene.

[0031] The configuration of paint consists of the following steps,

[0032] a. Methyl ethyl ketone peroxide, polysiloxane-polyether copolymer, polymethylphenylsiloxane, monoglyceride stearate, glycol, polyethylene water-based wax, styrene, cobalt naphthenate , butyl acetate, hydroxyl-containing alkyd resin, hydroxyethyl cellulose and xylene were mixed and stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear-resistant paint for bed head boards. The wear-resistant paint comprises the following raw materials in parts by weight: 1-2 parts of methyl ethyl ketone peroxide, 0.2-0.3 part of polysiloxane-polyether copolymer, 5-10 parts of glass powder, 8-10 parts of nano-silicon carbide powder, 10-15 parts of rutile titanium dioxide, 0.2-0.4 part of polymethyl phenyl siloxane, 0.5-0.9 parts of monoglyceride stearate, 35-45 parts of diatomic alcohol, 1-3 parts of polyethylene water-borne wax, 15-20 parts of styrene, 0.6-1 part of cobalt naphthenate, 60-70 parts of butyl acetate, 25-30 parts of alkyd resin containing hydroxide radicals, 0.5-0.9 part of hydroxyethyl cellulose and 5-7 parts of xylene. The invention has the advantage of maintaining the gloss of a bed head board for a long term.

Description

technical field [0001] The invention belongs to the field of headboard paint, and the paint relates to a wear-resistant headboard paint. Background technique [0002] The headboard, also known as the bed support, is a part installed at the back of the bed and used to provide the back of the human body to lean on. Since the headboard is often rubbed by the back of the human body, the paint on the headboard is easily worn away, which makes the headboard easy to lose its luster. The paint layer formed by the existing paint on the headboard is relatively soft, and the paint layer is not wear-resistant. If it is used on the headboard, generally it can only maintain the luster of the headboard in the first three to five years of use, and cannot maintain the bed for a long time. The head plate is glossy. Therefore, the existing paint has the disadvantage of being unable to maintain the headboard for a long time with luster. Contents of the invention [0003] The purpose of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D183/04C09D123/06C09D101/28C09D7/61
CPCC08K2003/2241C08K2201/011C08L2205/035C09D7/61C09D167/08C08L83/04C08L23/06C08L1/284C08K13/02C08K3/40C08K3/34C08K3/22
Inventor 潘月华
Owner 湖州市南浔三亚家私有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap