High temperature-resistant bearing grease and preparation method thereof

A bearing lubrication and high temperature resistance technology, applied in the field of lubricating grease, can solve the problems of water resistance, low rust and corrosion resistance, inability to meet high-speed bearing operation, general extreme pressure and friction reduction, and achieve good high and low temperature performance. , the effect of low noise and simple preparation method

Inactive Publication Date: 2019-02-15
安徽中天石化股份有限公司
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, general bearing grease is made from lithium soap thickened with mineral base oil and added with anti-wear, anti-oxidation and other additives. Due to the limitation of the preparation process, the produced bearing grease cannot meet the operati

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] A high temperature resistant bearing grease, including base oil, thickening agent, and additives. In terms of weight percentages, the base oil accounts for 70% of the total weight, the thickener accounts for 18% of the total weight, and the additives account for 12% of the total weight.

[0023] Among them, in parts by weight, the base oil includes: 60 parts of paraffin oil, 30 parts of polyol esters, 40 parts of di-n-octyl adipate, and 20 parts of poly-alpha olefins; thickeners include: 40 parts of bentonite, composite 15 parts of calcium sulfonate; additives including: 10 parts of antioxidants, 10 parts of rust inhibitors, 9 parts of extreme pressure antiwear agents, and 6 parts of other additives. In parts by weight, the above-mentioned antioxidant includes: 4 parts of alkyl diphenylamine, 7 parts of β-naphthol, 4 parts of BHT antioxidant additives; the above-mentioned rust inhibitor includes: 10 parts of barium petroleum sulfonate, petroleum 10 parts...

Example Embodiment

[0030] Example 2

[0031] A high temperature resistant bearing grease, including base oil, thickening agent, and additives. In terms of weight percentages, the base oil accounts for 80% of the total weight, the thickener accounts for 12% of the total weight, and the additives account for 8% of the total weight.

[0032] Among them, in parts by weight, the base oil includes: 40 parts of paraffin oil, 45 parts of polyol esters, 25 parts of di-n-octyl adipate, 40 parts of polyalphaolefins; thickeners, including: 30 parts of bentonite, composite 30 parts of calcium sulfonate; additives including: 6 parts of antioxidant, 15 parts of rust inhibitor, 5 parts of extreme pressure antiwear agent, and 2 parts of other additives. In parts by weight, the above-mentioned antioxidant includes: 10 parts of alkyl diphenylamine, 3 parts of β-naphthol, 2 parts of BHT antioxidant additive; the above-mentioned rust inhibitor includes: 15 parts of barium petroleum sulfonate, petroleum 5 parts of sodiu...

Example Embodiment

[0039] Example 3

[0040] A high temperature resistant bearing grease, including base oil, thickening agent, and additives. In terms of weight percentage, the base oil accounts for 75% of the total weight, the thickener accounts for 10% of the total weight, and the additives account for 15% of the total weight.

[0041] Among them, in parts by weight, the base oil includes: 50 parts of paraffin oil, 38 parts of polyol esters, 32 parts of di-n-octyl adipate, and 30 parts of polyalphaolefin; the thickening agent includes: 35 parts of bentonite , 22 parts of complex calcium sulfonate ester; the additives include: 8 parts of antioxidant, 13 parts of rust inhibitor, 7 parts of extreme pressure antiwear agent, 4 parts of other additives. In parts by weight, the above-mentioned antioxidant includes: 7 parts of alkyl diphenylamine, 5 parts of β-naphthol, 3 parts of BHT antioxidant additives; the above-mentioned rust inhibitor includes: 13 parts of barium petroleum sulfonate, petroleum 8 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of lubricating grease, in particular to high temperature-resistant bearing grease and a preparation method thereof. The high temperature-resistant bearing grease comprises the following components in percentage by weight: 70-80% of base oil, 12-18% of a thickening agent and 8-15% of additives, wherein the base oil comprises paraffin oil, polyol ester, di-n-octyladipate and poly-alpha olefin; the thickening agent comprises bentonite and calcium sulfonate complex ester; and the additives comprises an antioxidant, a rust inhibitor, an extreme pressure wear-resistant agent and other additives. The invention furthermore discloses the preparation method of the high temperature-resistant bearing grease. The produced bearing grease produced has excellent high and low temperature properties, lubricating performance, water resistance and extreme pressure wear resistance, low noise and long service life. At the same time, the preparation method is simple and strong in operability.

Description

technical field [0001] The invention relates to the field of lubricating grease, in particular to a high-temperature resistant bearing lubricating grease and a preparation method thereof. Background technique [0002] Bearing grease is a lubricating oil formulated from low-viscosity synthetic lubricating oil and added with various additives such as anti-oxidation and anti-corrosion. It is suitable for lubricating high-temperature and heavy-duty bearings operating under harsh conditions, especially for sealed or semi-sealed bearings Lifelong lubrication; especially suitable for occasions that emphasize long-term uninterrupted operation and extended grease cycle; fully synthetic grease guarantees long service life of grease and various bearings, gears, shaft pins, slideways and other components lubricated; applicable It is suitable for high temperature, heavy load, humid and corrosive occasions in mining, iron and steel industry, paper making and wood industry. [0003] At pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/00C10N30/06C10N30/08C10N40/02
CPCC10M169/00C10M2201/041C10M2201/066C10M2201/1036C10M2205/0206C10M2205/183C10M2207/023C10M2207/2825C10M2207/2835C10M2213/062C10M2215/064C10M2215/223C10M2219/044C10M2219/0445C10M2219/066C10M2223/041C10N2030/06C10N2030/08C10N2040/02C10N2030/76C10N2010/02C10N2010/04
Inventor 高晓谋高荣权何甲生张睿智
Owner 安徽中天石化股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap