Mosquito repellent viscose fiber and preparation method thereof

A viscose fiber and mosquito repellent technology, which is applied in the field of chemical fiber processing, can solve the problems of the mosquito repellent viscose fiber's mosquito repellent performance and poor durability of the mosquito repellent effect, and achieves the effects of simple preparation and low cost.

Inactive Publication Date: 2019-02-15
SATERI JIUJIANG FIBER CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, although the mosquito repellent viscose fiber has achieved certain development, the mosquito repellent viscose fiber still has the technical problems of poor mosquito repellent performance and mosquito repellent effect durability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method of mosquito repellent viscose fiber, comprising the following steps:

[0024] (1) Preparation of mosquito repellent dispersion: add limonol to deionized water at a temperature of 20°C, the mass ratio of limonol to deionized water is 1:10, and fully stir until it becomes transparent. Mosquito repellant, and then add dispersant polyethylene glycol, wherein the mass ratio of dispersant to mosquito repellent is 1:100, and fully stir to obtain A liquid.

[0025] (2) Preparation of thickener solution: boil water first, then slowly add sodium carboxymethylcellulose thickener into the boiling water, the mass ratio of thickener to water is 1:10, keep stirring until completely dissolved . Then cooled to obtain liquid B.

[0026] (3) Heat liquid A to 40°C, and then add it to the above liquid B while stirring. The mass ratio of liquid B to liquid A is 1:20, and stir well to obtain liquid C.

[0027] (4) Continuously blend the above liquid C with the spinning...

Embodiment 2

[0029] A preparation method of mosquito repellent viscose fiber, comprising the following steps:

[0030] (1) Preparation of mosquito repellent dispersion: Add limonol to deionized water at a temperature of 20°C, the mass ratio of limonol to deionized water is 1:30, and fully stir until it becomes transparent. Mosquito repellant, and then add dispersant BerolSpin653, wherein the mass ratio of dispersant to mosquito repellent is 5:100, stir well to obtain A liquid.

[0031] (2) Preparation of thickener solution: boil water first, then slowly add sodium carboxymethylcellulose thickener into the boiling water, the mass ratio of thickener to water is 1:100, keep stirring until completely dissolved . Then cooled to obtain liquid B.

[0032] (3) Heat liquid A to 60°C, and then add it to the above liquid B while stirring. The mass ratio of liquid B to liquid A is 1:100, and stir well to obtain liquid C.

[0033] (4) Continuously blend the above liquid C with the spinning viscose c...

Embodiment 3

[0036] A preparation method of mosquito repellent viscose fiber, comprising the following steps:

[0037] (1) Preparation of mosquito repellent dispersion: add lemon eucalyptus oil to deionized water at a temperature of 65°C, the mass ratio of lemon eucalyptus oil to deionized water is 1:30, and fully stir until transparent Make mosquito repellent liquid, then add dispersant polyoxyethylene polyene polyamide compound, wherein the mass ratio of dispersant and lemon eucalyptus leaf oil solution is 5:100, and obtain A liquid after fully stirring.

[0038] (2) Preparation of thickener solution: boil water first, then slowly add sodium carboxymethylcellulose thickener into the boiling water, the mass ratio of thickener to water is 1:100, keep stirring until completely dissolved . Then cooled to obtain liquid B.

[0039] (3) Heat liquid A to 60°C, and then add it to the above liquid B while stirring. The mass ratio of liquid B to liquid A is 1:100, and stir well to obtain liquid C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of mosquito repellent viscose fiber. The preparation method comprises the following steps: preparing a l PMD (p-menthane-3,8-diol)l dispersion solution ora lemon eucalyptus leaf oil dispersion solution, preparing a sodium carboxymethyl cellulose solution and preparing a uniform mixed solution of the dispersion solution and the sodium carboxymethyl cellulose solution; continuously blending the mixed solution and a spinning viscose stock solution in a ratio of 1:50-1:20 in a pre-spinning injection device, feeding the solution in spinning equipment for spinning after uniform dispersion, and performing drafting, cut-off, desulfurizing, washing, bleaching, pickling, washing, oiling, drying and the like on fiber obtained by spinning to prepare the mosquito repellent viscose fiber. A mosquito repellent is prepared from lemon eucalyptus leaf oil and extracts of the lemon eucalyptus leaf oil, and has the characteristics of being natural and safe; the fiber is easy to prepare and low in cost; the mosquito repellent viscose fiber not only can maintain basic characteristics of viscose fiber, but also has a long-acting mosquito repelling function,can be used for preparing textiles with a mosquito repelling function, and has good industrialization and market application prospects.

Description

technical field [0001] The invention relates to the technical field of chemical fiber processing, in particular to a preparation method of mosquito repellent viscose fiber. Background technique [0002] Many diseases (malaria, filariasis, dengue fever, Japanese encephalitis, etc.) originate from mosquito bites. Because the textiles used in people's lives are in close contact with human skin, with the development of science and technology and the improvement of living standards, people There is a greater demand for textiles with mosquito repellent properties. [0003] The hygroscopicity of viscose fiber is higher than that of cotton, which is very suitable for the physiological requirements of human skin, and has been widely used in the fields of textile and clothing, non-woven fabrics and medical hygiene materials. As the temperature rises, people's outdoor activities also increase, so the development of viscose fiber with mosquito repellent function has important applicati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/08
CPCD01F2/08
Inventor 王兵汪民康顾宇鹭陈卫民徐朝辉付敏波吴金友张文涛
Owner SATERI JIUJIANG FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap