Energy-saving and environment-friendly non-sintering antique tile and preparation method thereof

An energy-saving and environmental-friendly, power plant fly ash technology, which is applied in the field of antique brick and tile preparation, can solve the problems of tile manufacturers, such as inconvenient production, failure to meet market demand, and unrealistic antique effect, to achieve low cost, good color, and realistic antique effect. Effect

Inactive Publication Date: 2019-02-22
长春市宇实仿古建材有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] It is known that the preparation process of similar products of cement tiles mostly adopts compression molding, which requires many molds, high cost and takes 24 hours to demould
In addition, the tiles made are all one-piece tiles, and the antique effect is not realistic.
Furthermore, the existing vacuum clay tile-making machines cannot produce cement tiles, which brings great inconvenience to the production of tile-making enterprises.
[0003] At present, sintered antique tiles have been used in antique projects and temples and Taoist temples in my country for many years. There is no other choice. This kind of tile making method not only wastes the construction site but also pollutes the environment. Moreover, the product quality is poor and the color is not uniform, which cannot meet the market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The present invention is described further below:

[0018] An object of the present invention is to provide an energy-saving and environment-friendly non-burning antique tile, the blank of the antique tile is formulated according to the following weight percentages: 55% of power plant fly ash, 5% of this board glue, and 0.3% of polyacrylonitrile ammonium salt , 0.2% magnesium oxide, 0.1% reinforcing agent, 25% cement, 13% water, 0.3% color paste, 0.5% hydroxypropyl methylcellulose, 0.2% dispersible latex powder and 0.4% aluminum hydroxide.

[0019] Another object of the present invention is to provide a method for preparing an energy-saving and environmentally friendly non-burning antique tile, which includes the following steps:

[0020] Step 1, take raw materials by weight ratio as follows:

[0021] Power plant fly ash 55%, this board glue 5%, polyacrylonitrile ammonium salt 0.3%, magnesium oxide 0.2%, reinforcing agent 0.1%, cement 25%, water 13%, color paste 0.3%, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an energy-saving and environment-friendly non-sintering antique tile and a preparation method thereof. The green body of the energy-saving and environment-friendly non-sintering antique tile is prepared from components including, by weight percentage, 55% of power plant coal ash, 5% of green plate glue, 0.3% of ammonium polyacrylonitrile salt, 0.2% of magnesium oxide, 0.1%of reinforcing agent, 25% of cement, 13% of water, 0.3% of color paste, 0.5% of hydroxypropyl methyl cellulose, 0.2% of available dispersible emulsion powder and 0.4% of aluminum hydroxide. The preparation method comprises uniformly mixing the raw materials above into a sticky mixture through a mixture; then filling the mixture into a vacuum tile making machine, extruding tiles through the vacuumtile making machine, cutting and shaping the tiles, then transporting the finished tiles to a steam room for maintenance with steam of 40-50 DEG C, and 10 hours later, discharging the finished tiles for stacking. The energy-saving and environment-friendly non-sintering antique tile has the advantages of being naturally shaped, good in environmental protecting effects and the like.

Description

technical field [0001] The invention relates to the field of preparation of antique bricks and tiles, in particular to an antique tile made of raw materials such as cement and coal ash and a preparation method thereof. Background technique [0002] It is known that the preparation process of similar products of cement tiles mostly adopts compression molding, which requires many molds, high cost and can be demoulded after 24 hours. In addition, the tiles made are all one-piece tiles, and the antique effect is not realistic. Furthermore, the existing vacuum clay tile-making machines cannot produce cement tiles, which brings great inconvenience to the production of tile-making enterprises. [0003] At present, sintered antique tiles have been used in antique projects and temples and Taoist temples in my country for many years. There is no other choice. This kind of tile production method wastes construction sites and pollutes the environment. Moreover, the product quality is p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B2111/00594C04B2111/547C04B18/08C04B24/2652C04B22/066C04B24/26C04B22/06C04B2103/0068C04B2103/54C04B24/383
Inventor 国永红赵宝军
Owner 长春市宇实仿古建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products