PMMA coating slurry, PMMA compound coating diaphragm and preparation method thereof

A composite coating and coating paste technology, applied in electrical components, circuits, battery pack components, etc., can solve the problems of PVDF coating adhesion that is difficult to meet customer requirements, insufficient adhesion, etc., and is conducive to Mass production, reduced interface resistance, and improved adhesion

Active Publication Date: 2019-02-22
HEBEI GELLEC NEW ENERGY MATERIAL SCI&TECHNOLOY CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adhesion of pure PVDF coatings is sometimes difficult to meet customer requirements, that is, insufficient adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PMMA coating slurry, PMMA compound coating diaphragm and preparation method thereof
  • PMMA coating slurry, PMMA compound coating diaphragm and preparation method thereof
  • PMMA coating slurry, PMMA compound coating diaphragm and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] Some embodiments of the present invention propose a method for preparing the above-mentioned PMMA composite coating diaphragm, comprising: coating the PMMA coating slurry on the surface of the base coating diaphragm to form a water-based coating, and then at a temperature of 30-60 ° C dry under conditions. Wherein, the coating method includes spray coating.

[0030] The base coat separator is obtained by forming water-based boehmite slurry on a polyolefin base film. In some embodiments of the present invention, the PMMA composite coating is obtained by coating one side or both sides of the PMMA coating on the substrate coating diaphragm, and the PMMA coating is compounded with the boehmite coating, and the PMMA composite coating is arranged on The PMMA composite coating separator was thus prepared on the polyolefin base film.

[0031] The above water-based boehmite slurry is prepared in the following manner: add 5-15 parts of boehmite and 0.05-0.2 parts of dispersant ...

Embodiment 1

[0040]Add 10kg of boehmite powder and 100g of vinyl bisstearamide to 8kg of deionized water, mix and stir for 1 hour to disperse evenly, then add 2kg of polyvinyl alcohol and 1.0kg of polyether-modified polydimethylsiloxane emulsion, Stir 0.8kg of polyacrylate evenly to obtain water-based boehmite slurry; apply the above-mentioned water-based boehmite slurry to one side of the polyolefin base film by micro-gravure roll coating to form 2-3um boehmite The coating is then baked and dried in an oven at 30° C. for 5 minutes to obtain a base coating separator.

[0041] Add 2.5 kg of PMMA, 1.5 kg of polyvinyl alcohol and 0.05 g of sodium lauryl sulfate to 10 kg of deionized water, mix and stir for 1 h to obtain a PMMA spray coating slurry. A certain amount of PMMA slurry is sprayed on one side of the boehmite-coated diaphragm by a spraying process to form a 2-3um PMMA coating, and the PMMA composite-coated diaphragm is obtained through an oven at 60° C. for 1 min.

Embodiment 2

[0043] Add 5kg boehmite powder and 50g stearamide to 5kg deionized water, mix and stir for 0.8h to disperse evenly, then add 1kg polyethylene glycol, 0.5kg polyether modified polydimethylsiloxane emulsion, 0.5kg Stir the polyacrylate evenly to obtain the water-based boehmite slurry; apply the above-mentioned water-based boehmite slurry on both sides of the polyolefin base film by micro-gravure roll coating to form a 1-2um boehmite coating , and then passed through an oven at 40° C., and baked and dried for 4 minutes to obtain a base-coated separator.

[0044] Add 1.0 kg of PMMA, 1.0 kg of polyethylene glycol and 0.01 g of sodium dodecylbenzenesulfonate to 5 kg of deionized water, mix and stir for 1 h to obtain a PMMA spray coating slurry. A certain amount of PMMA slurry is sprayed on both sides of the boehmite-coated diaphragm by a spraying process to form a 1-2um PMMA coating, and the PMMA composite-coated diaphragm is obtained after an oven at 50°C for 2 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to PMMA coating slurry, a PMMA compound coating diaphragm and a preparation method thereof and belongs to the technical field of battery diaphragms. The PMMA coating slurry is prepared from the following raw materials in parts by weight: 1-4 parts of polymethyl methacrylate, 1.0-2.0 parts of a thickener, 0.00001-0.0001 part of a wetting agent and 5-20 parts of water. According to the PMMA coating slurry, taking water as a solvent and polymethyl methacrylate as a film forming component, water is evaporated at a certain temperature, so that the coating slurry forms a film on the surface of a base film. As the interface bonding action of polymethyl methacrylate is relatively good, so that the adhesive strength of the coating diaphragm is improved.

Description

technical field [0001] The invention belongs to the technical field of battery diaphragms, and in particular relates to a PMMA coating slurry, a PMMA composite coating diaphragm and a preparation method thereof. Background technique [0002] Coated separators are increasingly widely used in battery applications. The coating classification mainly includes: alumina coating; boehmite coating; PVDF coating; and composite coating of alumina / boehmite and PVDF. Among them, the function of alumina / boehmite coating is mainly to improve the thermal stability of the diaphragm and the wettability of the diaphragm to the electrolyte; the function of PVDF coating is mainly to improve the adhesion between the diaphragm and the pole piece and the effect of the diaphragm on the electrolyte. liquid wettability. The main function of adding a layer of PVDF coating after the inorganic coating is not only to improve the thermal stability of the separator but also to improve the adhesion between ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M2/16H01M2/14H01M50/403H01M50/414H01M50/457
CPCH01M50/403H01M50/431H01M50/411Y02E60/10
Inventor 徐锋袁海朝贾亚峰苏碧海
Owner HEBEI GELLEC NEW ENERGY MATERIAL SCI&TECHNOLOY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com