Dental implant surface treatment method

A dental implant and surface treatment technology, applied in the field of biomedicine, can solve problems such as uneven pits, achieve the effects of increasing surface roughness, increasing bone bonding ability, and improving interface bonding strength

Inactive Publication Date: 2019-03-08
佛山市佛冠义齿有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to alleviate the deficiencies of the prior art, the present invention provides a dental implant surface treatment method, which can effectively improve the uniformity of the pits on the dental implant surface and solve the problem of dental implant surface treatment. The problem of uneven pits when processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A surface treatment method for a dental implant, comprising the following process steps:

[0020] (1) Cleaning: Clean the surface of the dental implant in advance, and use alcohol and deionized water to ultrasonically clean it for 5 minutes each;

[0021] (2) Sand blasting treatment: the dental implant cleaned in step (1) is subjected to sand blasting treatment with aluminum oxide particles with a diameter of 15 μm under an air pressure of 0.4 MPa;

[0022] (3) Acid etching: The sandblasted dental implant was completely immersed in an acidic solution at 50°C for 5 minutes, then the dental implant was taken out, rinsed with deionized water immediately, and then passed through acetone, Ultrasonic cleaning with water ethanol and deionized water, and natural drying; wherein, the acidic solution is HF and HNO 3 The mixed solution, the concentration of HF is 0.1mol / L, HNO 3 The concentration is 0.08mol / L;

[0023] (4) Soaking: Soak the etched dental implant in 1mol / L ammon...

Embodiment 2

[0027] A surface treatment method for a dental implant, comprising the following process steps:

[0028] (1) Cleaning: Clean the surface of the dental implant in advance, and use alcohol and deionized water to ultrasonically clean it for 5 minutes each;

[0029] (2) Sand blasting treatment: the dental implant cleaned in step (1) is subjected to sand blasting treatment with alumina particles with a diameter of 30 μm under an air pressure of 0.5 MPa;

[0030] (3) Acid etching: The dental implants treated with sandblasting were completely immersed in the acidic solution at 70°C for 10 minutes, and then the dental implants were taken out, rinsed with deionized water immediately, and then passed through acetone, anhydrous Ultrasonic cleaning with water ethanol and deionized water, and natural drying; wherein, the acidic solution is HF and HNO 3 The mixed solution, the concentration of HF is 0.15mol / L, HNO 3 The concentration is 0.15mol / L;

[0031] (4) Soaking: Soak the etched de...

Embodiment 3

[0035] A surface treatment method for a dental implant, comprising the following process steps:

[0036] (1) Cleaning: Clean the surface of the dental implant in advance, and use alcohol and deionized water to ultrasonically clean it for 5 minutes each;

[0037] (2) Sand blasting treatment: the dental implant cleaned in step (1) is subjected to sand blasting treatment with alumina particles with a diameter of 20 μm under an air pressure of 0.45 MPa;

[0038] (3) Acid etching: The sandblasted dental implant was completely immersed in acidic solution at 60°C for 7 minutes, then the dental implant was taken out, rinsed with deionized water immediately, and then passed through acetone, Ultrasonic cleaning with water ethanol and deionized water, and natural drying; wherein, the acidic solution is HF and HNO 3 The mixed solution, the concentration of HF is 0.15mol / L, HNO 3 The concentration is 0.1mol / L;

[0039] (4) Soaking: Soak the etched dental implant in 1mol / L ammonia water;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a dental implant surface treatment method. Due to sand blasting and acid etching treatment before soaking, dental implant surface roughness is increased to some extent; further,due to calcining in a later stage, dental implant surface roughness is increased remarkably, the implant bone combination capacity can be increased, and accordingly the dental implant clinical success rate is increased. A mixed acid formed by hydrofluoric acid and nitric acid is adopted for acid etching to provide a great sand blast dental implant surface morphology, great rough surface characteristics of dental implants are achieved, and interface bonding strength of a dental implant and bone combination surface is further improved. The method is simple in operation, convenient and simple intreatment, low in cost and applicable to industrial large-scale production.

Description

technical field [0001] The invention belongs to the technical field of biomedicine, and in particular relates to a surface treatment method of a dental implant. Background technique [0002] Dental implant has become a relatively mature clinical technology with optimistic application prospects. However, as a medical device implanted in the body, its surface properties and shape are important factors affecting the quality, which largely determines whether the dental implant can be combined with the bone for a long time and perform its function. The treatment of tooth loss with metal dental implants is recognized by doctors and patients. Prolonging the service life of implants and improving the bonding strength between implants and alveolar bone have always been the goals pursued by stomatologists. At the same time, It also reflects from the side that the contact area between the dental implant and the alveolar bone is insufficient, the bonding force needs to be improved, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61C13/00
CPCA61C13/0006A61C13/0007
Inventor 刘秀兰陈沾方欧阳国明
Owner 佛山市佛冠义齿有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap