Artificial turf adhesive composition

An artificial turf and adhesive technology, applied in the direction of adhesives, adhesive additives, carboxyl rubber adhesives, etc., can solve the problems of high cost of PU back glue, low lawn pullout force, poor water resistance, etc. The effect of large-scale industrial production, improving adhesion and improving dispersibility

Inactive Publication Date: 2019-03-19
陆欣瑜
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually the grass silk and the bottom back are covered with a layer of latex to stabilize the grass silk. At present, the commonly used back glue is styrene-butadiene latex, which is low in cost, but the prepared lawn has low pull-out force and poor water resistance; higher-end Most of them have PU adhesive, which is durable and beautiful in color, and the PU adhesive has good grass pull-off performance, but the cost of PU adhesive is high, and the price of the product is usually much higher than that of styrene-butadiene latex products; in order to reduce production costs At the same time, to improve the various performances of the back glue, it is urgent to develop a kind of back glue product with low price and excellent performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment provides an artificial turf adhesive composition with excellent performance, and the adhesive composition includes the following components in parts by mass:

[0035] Water-based latex: 50 parts, phenolic resin: 20 parts, filler: 6 parts, water-based PUR dispersion: 6 parts, color paste: 10 parts, crosslinking agent: 1 part, coupling agent: 0.1 part, antifungal agent: 0.1 Parts, anti-aging agent: 0.1 part, UV absorber: 0.2 part, defoamer: 0.1 part, dispersant: 0.5 part, thickener: 5 parts, zinc oxide: 2 parts;

[0036] The filler is hollow glass microspheres; the color paste is red, orange, yellow, green, blue, purple, black color paste; the cross-linking agent is epoxy silane cross-linking agent XR-500; the coupling agent is water-based silane coupling antifungal agent is zinc pyrithione; antiaging agent is p-phenylenediamine antiaging agent; ultraviolet absorber is phenyl salicylate; defoaming agent is octanol; dispersant is sodium lauryl sulfate; Thi...

Embodiment 2

[0055] This embodiment provides an artificial turf adhesive composition with excellent performance, and the adhesive composition includes the following components in parts by mass:

[0056] Water-based latex: 100 parts, phenolic resin: 30 parts, filler: 30 parts, water-based PUR dispersion: 9 parts, color paste: 15 parts, crosslinking agent: 3 parts, coupling agent: 2 parts, antifungal agent: 0.5 Parts, anti-aging agent: 0.3 parts, UV absorber: 0.4 parts, defoamer: 0.2 parts, dispersant: 1 part, thickener: 15 parts, zinc oxide: 5 parts;

[0057] The filler is hollow glass microspheres; the color paste is red, orange, yellow, green, blue, purple, black color paste; the cross-linking agent is aziridine cross-linking agent XR-100; the coupling agent is aqueous titanic acid Ester coupling agent; antifungal agent is dichlorophenol; antiaging agent is p-phenylenediamine antiaging agent; ultraviolet absorber is phenoxytriazine; defoaming agent is silicone; dispersant is polyethylene ...

Embodiment 3

[0076] This embodiment provides an artificial turf adhesive composition with excellent performance, and the adhesive composition includes the following components in parts by mass:

[0077] Water-based latex: 80 parts, phenolic resin: 25 parts, filler: 16 parts, water-based PUR dispersion: 7 parts, color paste: 13 parts, crosslinking agent: 2 parts, coupling agent: 1 part, antifungal agent: 0.3 Parts, anti-aging agent: 0.2 parts, UV absorber: 0.3 parts, defoamer: 0.15 parts, dispersant: 0.8 parts, thickener: 10 parts, zinc oxide: 3 parts;

[0078] The filler is hollow glass microspheres; the color paste is red, orange, yellow, green, blue, purple, black color paste; the crosslinking agent is triethylenetetramine; the coupling agent is water-based silane coupling agent; The anti-aging agent is methyl formate; the anti-aging agent is p-phenylenediamine anti-aging agent; the ultraviolet absorbing agent is trimethoxybenzoate; the defoaming agent is tributyl phosphate; the dispersi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an artificial turf adhesive composition. The artificial turf adhesive composition is prepared from the following components in parts by weight: 45-100 parts of water-based latex, 20-30 parts of phenolic resin, 1-30 parts of filler, 6-9 parts of aqueous polyurethane (PUR) dispersion, 1-3 parts of cross-linking agent, 0.1-2 parts of coupling agent, 0.1-0.3 part of anti-ageingagent, 0.2-0.4 part of ultraviolet absorbent, 0.1-0.2 part of defoaming agent, 0.5-1 part of dispersing agent, and 2-5 parts of zinc oxide. The artificial turf adhesive composition provided by the invention is uniform in particle size, stable in property, good in weather resistance and water resistance, strong in ageing resistance, simple and feasible in preparation method and low in cost.

Description

technical field [0001] The invention belongs to the field of adhesive preparation, and in particular relates to an artificial turf adhesive composition with excellent performance. Background technique [0002] In recent years, artificial turf has developed vigorously and has been widely used in sports, leisure, decoration and other fields. In the prior art of lawn production, an important technical indicator is exactly the pull-out force of the grass silk on the lawn. Usually the grass silk and the bottom back are covered with a layer of latex to stabilize the grass silk. At present, the commonly used back glue is styrene-butadiene latex, which is low in cost, but the prepared lawn has low pull-out force and poor water resistance; higher-end Most of them have PU adhesive, which is durable and beautiful in color, and the PU adhesive has good grass pull-off performance, but the cost of PU adhesive is high, and the price of the product is usually much higher than that of styre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J109/08C09J113/02C09J125/14C09J161/06C09J175/08C09J11/04C09J11/06
CPCC09J109/08C08K2003/2296C08L2201/08C08L2205/035C09J11/04C09J11/06C08L13/02C08L25/14C08L61/06C08L75/08C08K13/04C08K3/22C08K7/28C08K5/5435
Inventor 陆欣瑜
Owner 陆欣瑜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap