A kind of high-nickel positive electrode material and preparation method thereof

A positive electrode material, high-nickel technology, applied in nanotechnology for materials and surface science, battery electrodes, nanotechnology, etc., can solve problems that have not been considered, and achieve reduced surface impedance, stable crystal structure, and cycle stability Good results

Active Publication Date: 2022-05-10
HEFEI GUOXUAN HIGH TECH POWER ENERGY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above two mainstream methods demonstrated the impact of water washing on the surface morphology, crystal structure and electrochemical performance of materials from an academic point of view, and did not consider how to reduce the loss of material gram capacity on the basis of lowering pH after water washing, so that Ensure material energy density and corresponding cycle performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-nickel positive electrode material and preparation method thereof
  • A kind of high-nickel positive electrode material and preparation method thereof
  • A kind of high-nickel positive electrode material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Precursor Ni 0.83 co 0.12 mn 0.05 (OH) 2 and lithium hydroxide monohydrate in a high-speed mixer according to the molar ratio of Li / (Ni+Co+Mn) of 1.05, and then sintered at 790° C. for 15 hours in a pure oxygen atmosphere to obtain a base material.

[0030] Nano Al 2 o 3 (0.05wt%), nano ZrO 2 (0.1wt%) mixed with the base material at high speed and then annealed at 720°C for 5 hours to obtain a primary modified powder. During annealing, high-purity oxygen was introduced to ensure the sintering atmosphere. The deionized water and primary modified powder were dispersed and stirred for 5 minutes according to the mass ratio of 2:1, and then suction filtered, and the filtered material was dried in a vacuum oven at 120°C for 12 hours, and N 2 Perform atmosphere replacement.

[0031] TiO 2 (0.1wt%) and the washed and dried primary modified powder were uniformly mixed with a high-speed mixer, and then sintered at 600°C for 5 hours in a pure oxygen atmosphere to obtain a ...

Embodiment 2

[0034] Precursor Ni 0.83 co 0.12 mn 0.05 (OH) 2and lithium hydroxide monohydrate in a high-speed mixer according to the molar ratio of Li / (Ni+Co+Mn) of 1.05, and then sintered at 790° C. for 15 hours in a pure oxygen atmosphere to obtain a base material.

[0035] Nano Al 2 o 3 (0.1wt%), nano ZrO 2 (0.1wt%) mixed with the base material at high speed and then annealed at 720°C for 5 hours to obtain a primary modified powder. During annealing, high-purity oxygen was introduced to ensure the sintering atmosphere. The deionized water and primary modified powder were dispersed and stirred for 5 minutes according to the mass ratio of 2:1, and then suction filtered, and the filtered material was dried in a vacuum oven at 120°C for 12 hours, and N 2 Perform atmosphere replacement.

[0036] Will B 2 o 3 (0.1wt%) and the washed and dried primary modified powder were uniformly mixed with a high-speed mixer, and then sintered at 500°C for 5 hours in a pure oxygen atmosphere to obt...

Embodiment 3

[0039] Precursor Ni 0.83 co 0.12 mn 0.05 (OH) 2 and lithium hydroxide monohydrate in a high-speed mixer according to the molar ratio of Li / (Ni+Co+Mn) of 1.05, and then sintered at 790° C. for 15 hours in a pure oxygen atmosphere to obtain a base material.

[0040] Nano Al 2 o 3 (0.1wt%), nano ZrO 2 (0.2wt%) mixed with the base material at high speed and then annealed at 720°C for 5 hours to obtain a primary modified powder. During annealing, high-purity oxygen was introduced to ensure the sintering atmosphere. The deionized water and primary modified powder were dispersed and stirred for 5 minutes according to the mass ratio of 2:1, and then suction filtered, and the filtered material was dried in a vacuum oven at 120°C for 12 hours, and N 2 Perform atmosphere replacement.

[0041] TiO 2 (0.05wt%) and the washed and dried primary modified powder were uniformly mixed with a high-speed mixer, and then sintered at 500°C for 5 hours in a pure oxygen atmosphere to obtain a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-nickel positive electrode material and a preparation method thereof. The base material of the high-nickel positive electrode material is Li x (Ni a co b mn c )O 2 Type NCM ternary material, wherein 1.0≤x≤1.06, a+b+c=1, a≥0.8, characterized in that the base material is coated with a surface-modified nano-metal oxide passivation layer , the substance used in the surface modification is a low melting point inorganic salt. The base material is covered with a layer of nano-metal oxide passivation layer modified by low-melting point inorganic salt surface. In the ternary system with increased nickel content, the surface modification is completed by two annealing treatments to stabilize the high-nickel cathode material. crystal structure and reduce the residual alkali content on the surface of the material, the prepared high-nickel cathode material has high capacity and good cycle.

Description

technical field [0001] The invention belongs to the field of lithium ion batteries, and in particular relates to a high-nickel positive electrode material and a preparation method thereof. Background technique [0002] The general chemical formula of the high-nickel layered cathode material is Li x (Ni a co b mn c )O 2 , where 1.00≤x≤1.09, a+b+c=1, a≥0.8, especially when the Ni element content is greater than 80%, the material exhibits high capacity characteristics greater than 180mAh / g, but the residual LiOH and Li on the surface of the material 2 CO 3 During electrode preparation, it reacts with binders, (PVDF), and organic solvents (NMP), resulting in jelly-like phenomenon during the mixing process. At present, in response to this problem, Korean scholar Jaephil Cho and his research group have found that annealing after washing is beneficial to LiNi 0.83 co 0.15 Al 0.02 o 2 The pH of the material can be significantly reduced, while the residual alkali on the sur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/505H01M4/525H01M4/62H01M10/0525B82Y30/00
CPCY02E60/10
Inventor 贾凯沈中宇李道聪
Owner HEFEI GUOXUAN HIGH TECH POWER ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap