A kind of thin film preparation method and qled device

A device and thin film technology, applied in the field of thin film preparation, can solve the problem of less composite materials, achieve the effect of balancing electrons and holes, improving luminous efficiency, and improving electron transport performance

Active Publication Date: 2020-08-18
TCL CORPORATION
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few reports on the composite materials of the two, especially in the application of QLED

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thin film preparation method and qled device
  • A kind of thin film preparation method and qled device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The following is to prepare ZnO / TiO by using zinc acetate, titanium sulfate, ethanol, potassium hydroxide, and ethyl acetate 2 Films composed of core-shell nanoparticles are described in detail.

[0051] (1) First, add an appropriate amount of zinc acetate to 50mL of ethanol to form a solution with a total concentration of 0.5M. Then stir and dissolve at 60°C, add lye (prepared by dissolving potassium hydroxide in 10mL ethanol), and the dissolved OH in the solution is - : Zn 2+ =2.0:1. Stirring was continued at 60 °C for 3 h to obtain a homogeneous clear solution. Subsequently, after the solution was cooled, it was precipitated with ethyl acetate, and after centrifugation, it was dissolved with a small amount of ethanol (repeated operation, washed 3 times) to obtain ZnO nanoparticles;

[0052] (2) Add ZnO nanoparticles and appropriate amount of titanium sulfate to 30mL ethanol to form a solution with a total concentration of 0.5M, in which the molar ratio of zinc:ti...

Embodiment 2

[0055] The following is the preparation of ZnO / TiO by using zinc nitrate, titanium nitrate, methanol, ethanolamine, and heptane 2 Core-shell nanoparticles are used as an example to describe in detail.

[0056] (1) First, add an appropriate amount of zinc nitrate to 50mL of methanol to form a solution with a total concentration of 0.2M. Then stir and dissolve at 60°C, add lye (prepared by dissolving ethanolamine in 10mL methanol), and in molar ratio, ethanolamine in the solution: Zn 2+ =1.8:1. Stirring was continued at 60 °C for 2 h to obtain a homogeneous clear solution. Subsequently, after the solution is cooled, it is precipitated with heptane, and after centrifugation, it is dissolved with a small amount of methanol (repeat the operation and wash 3 times) to obtain ZnO nanoparticles;

[0057] (2) Add ZnO nanoparticles and an appropriate amount of titanium nitrate to 30mL methanol to form a solution with a total concentration of 0.2M, in which the molar ratio of zinc:tita...

Embodiment 3

[0060] The following is the preparation of ZnO / TiO by using zinc chloride, titanium tetrachloride, propanol, lithium hydroxide, octane 2 Core-shell nanoparticles are used as an example to describe in detail.

[0061] (1) First, add an appropriate amount of zinc chloride to 50mL of propanol to form a solution with a total concentration of 1M. Then stir and dissolve at 60°C, add lye (prepared by dissolving lithium hydroxide in 10mL propanol), and the dissolved OH in the solution is - : Zn 2+ =2.5:1. Stirring was continued at 60 °C for 4 h to obtain a homogeneous clear solution. Subsequently, after the solution was cooled, it was precipitated with octane, and after centrifugation, it was dissolved with a small amount of propanol (repeated operation, washed 3 times) to obtain ZnO nanoparticles;

[0062] (2) Add ZnO nanoparticles and an appropriate amount of titanium tetrachloride to 30 mL of propanol to form a solution with a total concentration of 1 M, in which the molar rati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a thin film and a QLED device. The method includes the steps of: mixing a zinc salt solution with an alkali to react to obtain ZnO nanoparticles; adding titanium salt and the above-mentioned ZnO nanoparticles to an organic solvent, and then adding alkali, Perform a hydrolysis reaction to form a precursor solution; deposit the precursor solution to form a film, and perform an annealing reaction to obtain ZnO / TiO 2 Films composed of core-shell nanoparticles. ZnO / TiO of the present invention 2 The thin film composed of core-shell nanoparticles reduces the radiation combination of electron-hole pairs, thereby improving the electron transport performance and enhancing the luminous efficiency of the device. In addition, based on ZnO / TiO 2 The QLED device with core-shell structure can regulate electron injection and prevent the non-radiative Auger recombination mechanism from quenching the luminescence of quantum dots, thereby balancing electrons and holes and improving the luminous efficiency of the device.

Description

technical field [0001] The invention relates to the technical field of QLED devices, in particular to a method for preparing a thin film and a QLED device. Background technique [0002] ZnO is a direct bandgap n-type semiconductor material with a wide bandgap of 3.37 eV and a low work function of 3.7 eV. This band structure characteristic determines that ZnO can be a suitable electron transport layer material; at the same time, its good Electrical conductivity, high visible light transmittance, excellent water-oxygen stability, and mature preparation process make it more and more outstanding in the optoelectronic devices of solution process. [0003] TiO 2 It is a widely used multifunctional material with a wide bandgap of 3.2 eV. It has unique optical, electrical and physical properties, excellent chemical stability, and can resist electrochemical corrosion of the medium. It has been widely used in coatings, Cosmetics, semiconductors, sensors, dielectric materials, cataly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L51/50H01L51/56
CPCH10K50/16H10K50/11H10K71/00
Inventor 何斯纳吴龙佳吴劲衡
Owner TCL CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com