Concrete product capable of being solidified at room temperature and preparation method and application therof

A concrete product, curing technology at room temperature, applied in the direction of chemical instruments and methods, hydraulic material layered products, layered products, etc., can solve the problems of efflorescence, capillary pollutants, etc., to improve the binding force and Effects of compactness, improved adhesion, and enhanced protection

Inactive Publication Date: 2019-07-30
成都建工预筑科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the impermeability performance is limited. It is necessary to combine the activated barium ions in the concrete with the sulfate ions infiltrated from the outside of the concrete to form an inert and stable barite,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete product capable of being solidified at room temperature and preparation method and application therof
  • Concrete product capable of being solidified at room temperature and preparation method and application therof
  • Concrete product capable of being solidified at room temperature and preparation method and application therof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0041] Mix and stir 3kg of fluorocarbon resin, 0.02kg of wetting and dispersing agent, and 1kg of solvent evenly, then add 3.6kg of pigment, disperse and stir evenly, and grind until the fineness is less than 25 microns to obtain pigment slurry. Mix and stir the pigment slurry with 10kg of fluorocarbon resin, add 0.02kg of defoamer and 0.02kg of leveling agent during the stirring process, add 1kg of solvent after stirring evenly, and set aside the mixed material after stirring; weigh 1kg of curing agent is added to the above-mentioned uniformly stirred mixture before use, and it can be stirred evenly. The fluorocarbon resin used in this preparation example is LF-200, the wetting and dispersing agent is BYK-163, the solvent is dimethyl carbonate, the pigment is carbon black, the defoamer is BYK-065, and the leveling agent is BYK-330. The curing agent adopts TKA-75.

preparation example 2

[0043] Mix and stir 2kg of fluorocarbon resin, 0.1kg of wetting and dispersing agent, and 1kg of solvent evenly, then add 2.7kg of pigment, disperse and stir evenly, and grind to a fineness of less than 25 microns to obtain a pigment slurry. Mix and stir the pigment slurry with 6kg of fluorocarbon resin, add 0.05kg of defoamer and 0.15kg of leveling agent during the stirring process, add 1.5kg of solvent after stirring evenly, and set aside after stirring; Take 0.8kg of curing agent, add it to the above-mentioned uniformly stirred mixture before use, and stir evenly. The fluorocarbon resin used in this preparation example is GK-570, the wetting and dispersing agent is BYK-2001, the solvent is ethyl acetate, the pigment is carbon black, the defoamer is BYK-066N, and the leveling agent is BYK-358. The agent uses N3300.

preparation example 3

[0045] Mix and stir 4kg of fluorocarbon resin, 0.06kg of wetting and dispersing agent, and 1.6kg of solvent evenly, then add 4.6kg of pigment, disperse and stir evenly, and grind to a fineness of less than 25 microns to obtain a pigment slurry. Mix and stir the prepared pigment slurry with 11kg of fluorocarbon resin, add 0.04kg of defoamer and 0.16kg of leveling agent during the stirring process, and then add 2kg of solvent after stirring evenly, and the mixed material after stirring is set aside ; Weigh 1.2kg of curing agent, add it to the above-mentioned uniformly stirred mixture before use, and stir evenly. The fluorocarbon resin used in this preparation example is CC-03, the wetting and dispersing agent is BYK-2050, the solvent is ethyl acetate, the pigment is carbon black, the defoamer is BYK-065, and the leveling agent is BYK-358. The agent adopts TSE-100.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a concrete product capable of being solidified at room temperature and a preparation method and application thereof, and belongs to the technical field of concrete materials.The concrete product capable of being solidified at room temperature comprises base-layer concrete and a surface layer, wherein the surface layer comprises a mortar layer and a protection layer, and the mortar layer is located between the base-layer concrete and the protection layer; the base-layer concrete is cement concrete, the mortar layer prepared from cement mortar, and the protection layeris prepared from FEVE fluorocarbon coating. The concrete product has the advantages of being resistant to contamination, easy to clean, stable in structure and durable in protection effect, and whiskering is never generated.

Description

technical field [0001] The invention relates to the technical field of concrete materials, more specifically, it relates to a normal-temperature-cured concrete product and its preparation method and application. Background technique [0002] Concrete refers to the collective name of engineering composite materials that use cementitious materials to cement aggregates into a whole. The more commonly used concrete is made of cement as cementitious material, sand and stone as aggregates, mixed with water in a certain proportion and mixed. The resulting cement concrete is widely used in civil engineering. Concrete materials can be prepared and used at the construction site, and can also be made into prefabricated products and transported to the construction site for laying or installation. At present, there are mainly two ways to prepare cement concrete and its pre-products: one is formed by mechanical pressing, and the surface density is poor; There are many capillary pores on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B13/04B32B33/00C04B28/04C04B41/65C09D127/12C09D7/61C04B111/20
CPCB32B13/04B32B33/00C04B28/04C04B41/5001C04B41/65C04B2111/00612C04B2111/2023C09D7/61C09D127/12C08K3/04C04B14/02C04B14/06C04B22/147C04B24/06C04B24/10C04B24/122C04B2103/302C04B18/141C04B14/28C04B24/2623C04B24/2641C04B2103/0045C04B24/42C04B2103/308C04B22/14C04B24/383C04B22/10C04B14/106C04B41/4842C04B41/463C04B41/4535
Inventor 李锋孔文艺范晓玲黄祥
Owner 成都建工预筑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap