Wear-resistant and high-temperature-resistant powder coating for oil well pipe

A technology of powder coating and high temperature resistance, which is applied in the direction of powder coating, anti-corrosion coating, fireproof coating, etc. It can solve the problems of poor high temperature resistance of epoxy powder coating, reduced protection effect of oil well pipe, corrosion of oil pipe, etc., and achieves good flow performance, Prevents penetration of corrosive substances and improves high temperature resistance

Inactive Publication Date: 2019-08-09
TIANJIN PRIMARY SECONDARY JIAHE CHEM CO LTD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the exploration and development of most oil wells in my country has entered the later stage. With the in-depth development of oil fields, a large number of chemical additives are used for oil displacement during oil production, and chemical additives cause corrosion to downhole tubing and sucker rods. However, the epoxy powder coating used for downhole oil pipes and sucker rods has relatively poor high temperature resistance. Under long-term high temperature conditions, the coating film decomposes, which reduces the protective effect of the paint on oil well pipes and causes corrosion of oil pipes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A wear-resistant and high-temperature-resistant powder coating for oil well pipes. In parts by weight, the raw materials include 100 parts of epoxy resin, 40 parts of phenolic resin, 10 parts of polyamide curing agent, 20 parts of graphene oxide, 30 parts of silane coupling agent, 1 part of nano-alumina, 40 parts of talcum powder, 18 parts of mica powder, 10 parts of antioxidant, wherein the antioxidant is mixed with 2-6-di-tert-butyl-4-methylphenol and trioctyl phosphate, wherein according to In parts by weight, the ratio of 2-6-di-tert-butyl-4-methylphenol: trioctyl phosphate is 3:2.

Embodiment 2

[0030] A wear-resistant and high-temperature-resistant powder coating for oil well pipes. In parts by weight, raw materials include 100 parts of epoxy resin, 45 parts of phenolic resin, 12 parts of polyamide curing agent, 17 parts of graphene oxide, 25 parts of silane coupling agent, 2 parts of nano-alumina, 35 parts of talc powder, 23 parts of mica powder, 15 parts of antioxidant, wherein the antioxidant is mixed with 2-6-di-tert-butyl-4-methylphenol and trioctyl phosphate, wherein according to In parts by weight, the ratio of 2-6-di-tert-butyl-4-methylphenol: trioctyl phosphate is 3:2.

Embodiment 3

[0032] A wear-resistant and high-temperature-resistant powder coating for oil well pipes. In parts by weight, the raw materials include 100 parts of epoxy resin, 50 parts of phenolic resin, 13 parts of curing agent, 15 parts of graphene oxide, 23 parts of silane coupling agent, nano-oxidized 3 parts of aluminum, 30 parts of talcum powder, 28 parts of mica powder, 20 parts of antioxidant, wherein the antioxidant is mixed with 2-6-di-tert-butyl-4-methylphenol and trioctyl phosphate, wherein by weight Counting, the ratio of 2-6-di-tert-butyl-4-methylphenol: trioctyl phosphate is 3:2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant and high-temperature-resistant powder coating for an oil well pipe, and belongs to the field of coatings. According to the technical scheme, the coating is prepared from, by weight, 100 parts of epoxy resin, 40-60 parts of phenolic resin, 10-16 parts of a curing agent, 10-20 parts of graphene oxide, 15-30 parts of a silane coupling agent, 1-5 parts of an anti-caking agent, 20-40 parts of talcum powder, 18-38 parts of mica powder and 10-30 parts of an antioxidant. The effect of improving high temperature resistance of the coating is achieved.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a wear-resistant and high-temperature-resistant powder coating for oil well pipes. Background technique [0002] Powder coatings are made of resin, pigments and fillers, curing agents and other additives, mixed in a certain proportion, and then processed by crushing and sieving equipment. Powder coatings are stable in storage at room temperature. After electrostatic spraying, friction spraying or fluidized bed Dip coating, reheating and baking to melt and solidify to form a flat and bright coating film. The early application of powder coatings was mainly in the anti-corrosion and electrical insulation of container pipes. After the 1950s, with the rapid development of this new technology With the development, its new varieties are constantly emerging, its performance is constantly improving and improving, and its application fields are constantly expanding, such as household appliances, tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D161/06C09D5/03C09D5/08C09D7/48C09D7/61
CPCC08K2003/2227C08K2201/011C08L2201/08C09D5/033C09D5/08C09D5/18C09D7/48C09D163/00C08L61/06C08K13/02C08K3/042C08K3/22C08K3/34C08K5/13C08K5/521
Inventor 孙飞刘彦鹏
Owner TIANJIN PRIMARY SECONDARY JIAHE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products