A biodegradable lunch box

A lunch box and modification technology, which is applied in the field of degradable lunch boxes, can solve the problems of convenience and harm, and achieve the effect of increasing carbon sequestration capacity, enhancing performance, and degrading performance

Active Publication Date: 2021-12-07
潘太孝
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

While plastics bring convenience to people's lives, they also bring unmanageable troubles to the environment. People call the disasters brought by plastics to the environment "white pollution"; convenience, but this convenience brings long-term harm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A biodegradable lunch box
  • A biodegradable lunch box
  • A biodegradable lunch box

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A degradable lunch box, made of the following raw materials in parts by weight: 45 parts of poly-β-hydroxybutyrate, 25 parts of modified polybutylene succinate, 25 parts of composite biochar, lignocellulose Airgel 15 parts, polylactic acid 15 parts, modified hydroxypropyl acetylated corn starch 8 parts, aluminate coupling agent 6 parts.

[0031] The preparation method of described modified polybutylene succinate is:

[0032] S1. Mix acetate starch and dimethyl sulfoxide with ethanol in a mass ratio of 1:0.3, and react with stirring at 60°C for 2 hours, then let stand for 24 hours to obtain modified acetate starch, the dimethyl sulfoxide Sulfone accounts for the mass of the mixed system;

[0033] S2. Add polybutylene succinate to the above-mentioned modified acetate starch, stir and react at 80°C for 3 hours to make modified polybutylene succinate; wherein, the modified acetate starch, polybutylene succinate The mass ratio of butanediol diacid is 1:2.

[0034] The pre...

Embodiment 2

[0040] This embodiment provides a degradable lunch box. Compared with Embodiment 1, the difference is that it is made of the following raw materials in parts by weight: 40 parts of poly-β-hydroxybutyrate, modified polysuccinic acid 30 parts of butanediol ester, 20 parts of composite biochar, 20 parts of lignocellulose airgel, 20 parts of polylactic acid, 5 parts of modified hydroxypropyl acetylated corn starch, and 5 parts of aluminate coupling agent.

Embodiment 3

[0042] This embodiment provides a degradable lunch box. Compared with Embodiment 1, the difference is that it is made of the following raw materials in parts by weight: 50 parts of poly-β-hydroxybutyrate, modified polysuccinic acid 20 parts of butylene glycol ester, 30 parts of composite biochar, 10 parts of lignocellulose airgel, 10 parts of polylactic acid, 10 parts of modified hydroxypropyl acetylated corn starch, and 8 parts of aluminate coupling agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a degradable lunch box, which is made of the following raw materials in parts by weight: 40-50 parts of poly-β-hydroxybutyrate, 20-30 parts of modified polybutylene succinate, compound 20-30 parts of biochar, 10-20 parts of lignocellulose airgel, 10-20 parts of polylactic acid, 5-10 parts of modified hydroxypropyl acetylated cornstarch, 5-8 parts of coupling agent; the present invention can The production cost of the degradable lunch box is low, the overall strength is good, the temperature resistance is good, and it can be degraded quickly in the natural environment.

Description

technical field [0001] The invention relates to a disposable tableware, in particular to a degradable lunch box. Background technique [0002] Disposable fast food boxes have changed from foam lunch boxes to environmentally friendly lunch boxes. The original foam lunch boxes have been eliminated because they are not resistant to high temperatures and the production process has caused damage to the environment. Plastic lunch boxes, paper lunch boxes, wooden lunch boxes, etc. Among them, plastic has become the mainstream material for manufacturing disposable fast food boxes due to its low toxicity, high melting point, strong plasticity, easy production and relatively low cost; disposable lunch boxes made of plastic are mainly There are two kinds of PP polypropylene and PS polystyrene, both of which are non-toxic, tasteless and odorless, and PP is relatively soft. Generally, the use temperature of PP is -6 degrees to +120 degrees, so it is especially suitable for hot meals and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/04C08L67/02C08L3/06C08L3/08C08L89/00C08L97/02C08K13/06C08K5/053C08K9/02C08K7/24C08K5/41C08B31/16
CPCC08B31/16C08K2201/014C08L67/04C08L2201/06C08L2201/08C08L2205/02C08L2205/035C08L67/02C08L3/06C08L3/08C08L89/00C08L97/02C08K13/06C08K5/053C08K9/02C08K7/24C08K5/41
Inventor 潘太孝
Owner 潘太孝
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com