Modified AF coating material as well as preparation method and application thereof

A modification and coating technology, which is applied in metal material coating process, coating, sputtering coating, etc., can solve problems such as not being able to meet market demand, achieve good waterproof, simple preparation process, and improve waterproof effect

Active Publication Date: 2019-08-16
重庆广正亿科技有限公司
View PDF14 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the anti-fingerprint film for the touch screen can effectively prevent the screen from being polluted by the outside world, it cannot prevent other appearance parts of the product from being polluted by the outside world. Therefore, with the rapid development of electronic products, the surfaces of electronic products are waterproof, anti-fouling, and If the fingerprint performance is too poor, it will not be able to meet the market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified AF coating material as well as preparation method and application thereof
  • Modified AF coating material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of modified AF coating material, comprises AF raw material and modifier, and the mass ratio of described AF raw material and described modifier is 20:2.5.

[0041] The AF raw material comes from Merck WR6 series coating film material in Germany. WR6 is specially designed for the production of hydrophobic and oleophobic coatings to meet the mature anti-fingerprint, anti-smudge and easy-to-clean surface treatment technology market demand in today's touch screen market , using the method of vacuum evaporation, WR6 can significantly reduce the adhesion of dust and fingerprints on the sensing surface of the touch screen, thus providing an excellent ease of operation.

[0042] The modifying agent includes fatty acid lead salt, methyl hexahydrophthalic anhydride, 4-nonylbenzene powder, nano-layer increasing agent and butylphenol, and the modifying agent is based on the mass ratio of fatty acid lead salt: methyl Hexahydrophthalic anhydride: 4-nonylbenzene powder: nano-la...

Embodiment 2

[0050] A kind of modified AF coating material, comprises AF raw material and modifier, and the mass ratio of described AF raw material and described modifier is 20:3.

[0051] The AF raw material comes from the EC300X series of PPG in the United States.

[0052] The modifying agent includes fatty acid lead salt, methyl hexahydrophthalic anhydride, 4-nonylbenzene powder, nano-layer increasing agent and butylphenol, and the modifying agent is based on the mass ratio of fatty acid lead salt: methyl Hexahydrophthalic anhydride: 4-nonylbenzene powder: 4-aminobiphenyl: butylphenol = 1:1:1:1:2.

[0053] The nano-layer increasing agent is 4-aminobiphenyl.

[0054] The butylphenol is a mixture of di-tert-butylphenol and sec-butylphenol with a mass ratio of 1:1.

[0055] The modifier also includes bicyclooctane, dioxane, di-n-octyl-bis(2-ethylhexyl mercaptoacetate) tin.

[0056] The bicyclooctane is a combination of cis isomerization and trans isomerism, and the quality of the bicycl...

Embodiment 3

[0060] A kind of modified AF coating material, comprises AF raw material and modifier, and the mass ratio of described AF raw material and described modifier is 20:3.5.

[0061] The AF raw material comes from Duen superhard waterproof membrane SH-HT9080.

[0062] The modifying agent includes fatty acid lead salt, methyl hexahydrophthalic anhydride, 4-nonylbenzene powder, nano-layer increasing agent and butylphenol, and the modifying agent is based on the mass ratio of fatty acid lead salt: methyl Hexahydrophthalic anhydride: 4-nonylbenzene powder: nano-layer enhancer: butylphenol=1:1:1:1:2.

[0063] The nano-layer increasing agent is 4-aminobiphenyl.

[0064] The butylphenol is a mixture of di-tert-butylphenol and sec-butylphenol with a mass ratio of 1:1.

[0065] The modifier also includes bicyclooctane, dioxane, di-n-octyl-bis(2-ethylhexyl mercaptoacetate) tin.

[0066] The bicyclooctane is a combination of cis-isomerization and trans-isomerization, and the mass of the bi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified AF coating material as well as a preparation method and application thereof. The modified AF coating material comprises an AF raw material and a modifier, wherein the mass ratio of the AF raw material to the modifier is 20:2.5-3.5, and the modifier comprises fatty acid lead salt, methylhexahydrophthalic anhydride, 4-Nonylphenol, a nanolayer additive and butyl-Phenol in the mass ratio of 1:1:1:1:2. According to the material, the original AF raw material is modified, the thickness of a nanolayer is increased, so that the antifouling property, the fingerprint resistance, the hydrophobicity and the adhesive force of the material are improved.

Description

technical field [0001] The invention belongs to the technical field of optical coating materials, in particular to a modified AF coating material and its preparation method and application. Background technique [0002] AF coating is based on the principle of lotus leaf, coating a layer of nano-chemical materials on the glass surface to make it have strong hydrophobicity, anti-oil, anti-fingerprint and other functions. It can easily wipe off dirt, finger prints, oil stains, etc., making the surface smoother and more comfortable to the touch, achieving the effects of waterproof, anti-fouling, and anti-fingerprints. AF coating materials are mainly used in glass coating, such as mobile phone 3D glass coating. [0003] Such as Chinese utility model patent, application number is 201120330917.X, discloses a kind of anti-fingerprint film for touch screen, tempered glass upper surface is buffer layer, the upper surface of buffer layer is AF film, buffer layer is SiO 2 , the AF fil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C14/06C23C14/24G02B1/18
CPCC23C14/06C23C14/24G02B1/18
Inventor 李通马国平孔东平秦跃权李新
Owner 重庆广正亿科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More