Three-layer composite waterproof corrugated board and preparation technology thereof

A technology of corrugated cardboard and preparation process, which is applied in the field of corrugated paper, can solve the problems of corrugated paper strength decrease, corrugated paper poor moisture resistance, corrugated paper strength low, etc., and achieve the effect of increasing strength, increasing waterproof performance, and improving waterproof and moisture-proof performance

Inactive Publication Date: 2019-08-23
广东新力德包装科技有限公司
View PDF11 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing corrugated cardboard also has some shortcomings as packaging materials: on the one hand, corrugated paper has poor moisture resistance, and it is easy to cause the st

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Three-layer composite waterproof corrugated board and preparation technology thereof
  • Three-layer composite waterproof corrugated board and preparation technology thereof
  • Three-layer composite waterproof corrugated board and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0036] Preparation example 1-3 of compound emulsified paraffin

[0037] In preparation example 1-3, the paraffin wax is selected from the 60# paraffin wax sold by Jinan Haiwei Chemical Co., Ltd., the rosin resin is selected from the rosin resin sold by Dongguan Shuangteng Rubber Sweater Co., Ltd., and the emulsified silicone oil is selected from Hebei Duoliwei Chemical. The CR100 type emulsified silicone oil sold by Co., Ltd. The dimethyl silicone oil is selected from the KF96-350CS type dimethyl silicone oil sold by Shenzhen Yichang Xingye Trading Co., Ltd., and the polyethylene is selected from the LH506 type sold by Suzhou Jinsulian Plastics Co., Ltd. Polyethylene.

[0038] Preparation Example 1: (1) According to the raw material ratio in Table 1, put 2kg of paraffin wax and 0.5kg of rosin resin into the reactor, heat to 80℃ to melt, mix well, add 0.5kg of polyethylene, and raise the temperature to 160℃, mix well;

[0039] (2) Add 0.3 kg of dimethyl silicone oil, 0.1 kg of emuls...

Example Embodiment

[0043] Preparation Example 2: (1) According to the raw material ratio in Table 1, put 2.5kg of paraffin wax and 0.8kg of rosin resin into the reactor, heat to 85°C to melt, mix well, add 0.8kg of polyethylene, and increase the temperature To 170℃, mix well;

[0044] (2) Add 0.4 kg of dimethyl silicone oil, 0.2 kg of emulsified silicone oil and 3.5 kg of 93% absolute ethanol to the product obtained in step (1), and mix them evenly.

Example Embodiment

[0045] Preparation Example 3: (1) According to the raw material ratio in Table 1, put 3.0kg paraffin wax and 1.0kg rosin resin into the reactor, heat to 90℃ to melt, mix well, add 1.0kg polyethylene, and raise the temperature To 180℃, mix well;

[0046] (2) Add 0.6 kg of dimethyl silicone oil, 0.3 kg of emulsified silicone oil and 4 kg of 95% absolute ethanol to the product obtained in step (1), and mix them evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bursting strengthaaaaaaaaaa
Water absorptionaaaaaaaaaa
Water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a three-layer composite waterproof corrugated board and a preparation technology thereof. The preparation technology of the three-layer composite waterproof corrugated board comprises the following steps: 1, preparing corrugated paper layers; 2, treating surface paper and inner paper: immersing the surface paper and inner paper in a reinforcing solution, taking out the surface paper and the inner paper after the surface paper and the inner paper are completely soaked, and drying the surface paper and the inner paper in a 45-55 DEG C environment, wherein the reinforcingsolution is prepared through mixing, by weight, 0.7-1.1 parts of modified bentonite, 0.5-0.9 part of nano-silica, 1.2-1.6 parts of ceramic powder, 5-10 parts of an acrylate emulsion and 1.3-1.6 partsof silica sol; 3, performing gluing and compounding; and 4, coating with a waterproof coating. The three-layer composite waterproof corrugated board of the invention has the advantages of high strength, good bending resistance, and good waterproof and moisture-proof performances; and the preparation technology of the invention has a simple preparation process.

Description

technical field [0001] The invention relates to the technical field of corrugated paper, more specifically, it relates to a three-layer composite waterproof corrugated board and its preparation process. Background technique [0002] As the most important packaging material, corrugated paper has the advantages of light weight and low cost compared to other packaging materials (such as wood, cardboard, etc.). The weight of three-layer corrugated cardboard is about 600g / m 2 , while the weight of a board of the same thickness is about 2000g / m 2 , It is more than 3 times that of corrugated cardboard. [0003] Corrugated paper is a composite material composed of cellulose fibers and polymer binders. Its raw material is base paper, which can be made from wood pulp (wood leftovers) and straw pulp, and can be reused conveniently. Due to the flatness of the cardboard, it can be printed conveniently, and can be folded, occupying a small space during storage and transportation. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B29/00B32B29/08B32B7/12B32B37/12D21H17/69D21H17/68D21H17/67D21H17/37D21H27/40
CPCB32B7/12B32B29/005B32B29/08B32B37/1284D21H17/37D21H17/67D21H17/68D21H17/69D21H27/40
Inventor 王坪林
Owner 广东新力德包装科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap