A composite electrode and its preparation method and application

A composite electrode and electrode technology, which is applied in chemical instruments and methods, electrolytic coatings, surface reaction electrolytic coatings, etc., can solve the problems of high energy consumption and low light utilization rate of polycyclic aromatic hydrocarbons, and achieve enhanced catalytic performance and good electricity. Chemical properties, effects of strong affinity

Active Publication Date: 2022-03-04
TIANJIN CHENGJIAN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of low light utilization rate and high energy consumption of the existing photocatalytic degradation of polycyclic aromatic hydrocarbons, the present invention provides a composite electrode, and provides its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composite electrode and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The composite electrode of this embodiment includes titanium foil, titanium dioxide nanotubes, acidified carbon nanotubes, 1-butyl-3-methylimidazolium bisulfate and phosphomolybdic acid from the inside to the outside.

[0032] The preparation method of this composite electrode is as follows:

[0033] 1. Substrate pretreatment

[0034] Grind the titanium foil with 500-mesh sandpaper to remove impurities on the surface of the titanium foil; place the polished titanium foil in acetone, ethanol, and isopropanol and ultrasonically clean the ultrasonically cleaned titanium foil with deionized water, and dry it naturally at room temperature .

[0035] 2. Preparation of titanium dioxide nanotubes

[0036] (1) Electrolyte preparation: A solution composed of ethylene glycol, deionized water and ammonium fluoride is used as the electrolyte, wherein the concentration of ammonium fluoride is 0.15mol / L, and the volume fraction of deionized water is 4%.

[0037] (2) Anodizing: use ...

Embodiment 2

[0046]The composite electrode of this embodiment comprises titanium foil, titanium dioxide nanotubes, acidified carbon nanotubes, 1-butyl-3-methylimidazole hydrochloride and phosphomolybdic acid in sequence from the inside to the outside.

[0047] The preparation method of this composite electrode is as follows:

[0048] 1. Substrate pretreatment

[0049] Grind the titanium foil with 500-mesh sandpaper to remove impurities on the surface of the titanium foil; place the polished titanium foil in acetone, ethanol, and isopropanol and ultrasonically clean the ultrasonically cleaned titanium foil with deionized water, and dry it naturally at room temperature .

[0050] 2. Preparation of titanium dioxide nanotubes

[0051] (1) Electrolyte preparation: A solution composed of ethylene glycol, deionized water and ammonium fluoride is used as the electrolyte, wherein the concentration of ammonium fluoride is 0.1mol / L, and the volume fraction of deionized water is 5%.

[0052] (2) An...

Embodiment 3

[0061] The composite electrode of this embodiment includes titanium foil, titanium dioxide nanotubes, acidified carbon nanotubes, 1-butyl-3-methylimidazolium bisulfate and phosphomolybdic acid from the inside to the outside.

[0062] The preparation method of this composite electrode is as follows:

[0063] 1. Substrate pretreatment

[0064] Grind the titanium foil with 500-mesh sandpaper to remove impurities on the surface of the titanium foil; place the polished titanium foil in acetone, ethanol, and isopropanol and ultrasonically clean the ultrasonically cleaned titanium foil with deionized water, and dry it naturally at room temperature .

[0065] 2. Preparation of titanium dioxide nanotubes

[0066] (1) Electrolyte preparation: A solution composed of ethylene glycol, deionized water and ammonium fluoride is used as the electrolyte, wherein the concentration of ammonium fluoride is 0.2mol / L, and the volume fraction of deionized water is 3%.

[0067] (2) Anodizing: use t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of photoelectric catalysis, and specifically discloses a composite electrode as well as a preparation method and application thereof. The composite electrode includes an electrode matrix, titanium dioxide nanotubes, acidified carbon nanotubes, imidazole-type ionic liquid and phosphomolybdic acid from the inside to the outside. The preparation method is to prepare titanium dioxide nanotubes on the electrode matrix, and then acidify the carbon nano The tubes are supported on the titanium dioxide nanotubes, and then the imidazole-type ionic liquid and phosphomolybdic acid are sequentially deposited. The composite electrode can efficiently degrade polycyclic aromatic hydrocarbons at a lower current density.

Description

technical field [0001] The invention relates to the technical field of photoelectric catalysis, in particular to a composite electrode and its preparation method and application. Background technique [0002] Polycyclic aromatic hydrocarbons are a class of compounds with more than two aromatic rings fused together. They are commonly found in the environment. Due to their poor water solubility and difficulty in biodegradation, these compounds accumulate continuously in the environment and are difficult to degrade. persistent organic matter. With the rapid development of China's industrialization, urbanization and agricultural intensification, the ways of polycyclic aromatic hydrocarbons entering the environment are becoming more and more extensive, and the environmental pollution caused by them has also attracted more and more attention. Polycyclic aromatic hydrocarbons are compounds with "three effects", as well as bioaccumulation, biomagnification and persistent poisoning,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J21/06C02F101/32
CPCC02F1/46109C02F1/30C02F1/4672C02F1/725C25D11/26C02F2101/32C02F2001/46133C02F2001/46142
Inventor 段庆飞卢静芳郭建博逯彩彩宋圆圆
Owner TIANJIN CHENGJIAN UNIV