A kind of environment-friendly heating material for floor and preparation method thereof

A heating material and environmental protection technology, applied in the direction of floor, building, building structure, etc., can solve the problems of low thermal conductivity, high compressive strength and good flame retardancy of thermal insulation materials, and achieve good flame retardancy and high compressive strength. , the effect of good mechanical properties

Active Publication Date: 2021-02-19
宁波昕科工贸有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the above-mentioned technical problems, the purpose of the present invention is to provide an environmentally friendly heating material for flooring and its preparation method. The polyurethane thermal insulation material prepared by adding various additives to discarded polyester bottles is more environmentally friendly. , and the insulation material has low thermal conductivity, good flame retardancy, low water absorption and high compressive strength; by adding the mixture A as a filler to the polyurethane material, the prepared environmentally friendly heating material has good mechanical properties and electrical properties, Fast heating, uniform heating, can avoid local overheating, and low cost of production raw materials, low power consumption, energy saving and environmental protection, safety and low carbon, the production process has zero pollution to the environment; at the same time, the process is simple, suitable for production, and reduces costs ;Mixture A is simple in design, fast in temperature rise, uniform in heat generation, can avoid local overheating, and has low raw material cost, low power consumption, energy saving and environmental protection, safety and low carbon, and zero pollution to the environment during the production process; phenolic resin and dextrin The mixture is a binder, which will slowly decompose during combustion to produce hydrogen, hydrocarbons, water vapor and carbon oxides. It is non-toxic and harmless, and does not hinder the contact of reactants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environment-friendly heating material for floor and preparation method thereof
  • A kind of environment-friendly heating material for floor and preparation method thereof
  • A kind of environment-friendly heating material for floor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] An environmentally friendly heating material for flooring, which is prepared from the following raw materials in parts by weight: 20 parts of heating dry powder, 1 part of binder and 80 parts of polyurethane;

[0045] Wherein, expressed in mass percent, the composition of the exothermic dry powder is: C: 85.6%, Zn: 3%, Al: 4%, Si: 1%, Ni: 2%, Ti: 4% and Ag : 0.4%;

[0046] The environmentally friendly heating material is prepared by the following method:

[0047] Step 1. Preparation of the exothermic dry powder: Weighing each raw material according to the composition of the above exothermic dry powder, then adding each raw material into a blender, stirring and mixing evenly to obtain the exothermic dry powder;

[0048] Step 2. Preparation of mixture A: Add phenolic resin and dextrin into the kneader, then slowly add the above-mentioned heat-generating dry powder into the kneader, stir while adding, and stop after the heat-generating dry powder and binder are mixed even...

Embodiment 2

[0054] An environmentally friendly heating material for flooring, which is prepared from the following raw materials in parts by weight: 30 parts of heating dry powder, 10 parts of binder and 120 parts of polyurethane;

[0055] Wherein, expressed in mass percent, the composition of the exothermic dry powder is: C: 87.9%, Zn: 3%, Al: 4%, Si: 1%, Ni: 2%, Ti: 2%, and Ag : 0.1%;

[0056] The environmentally friendly heating material is prepared by the following method:

[0057] Step 1, is identical with embodiment 1 step;

[0058] Step 2 is the same as in Example 1;

[0059] Step 3, the same step as in Example 1;

[0060] Step 4: Mix 5 parts of sucrose polyether, 3 parts of pentamethyldiethylenetriamine, N,N-dimethylcyclohexylamine and triethylenediamine mixture, 3 parts of blowing agent, 4 parts of modified flame retardant 2. Put 2 parts of dimethylsiloxane into the reaction kettle, add the yellow transparent liquid prepared above, stir and mix at high speed for 1 minute, and...

Embodiment 3

[0064] An environmentally friendly heating material for flooring, which is prepared from the following raw materials in parts by weight: 30 parts of heating dry powder, 1 part of binder and 120 parts of polyurethane;

[0065] Wherein, expressed in mass percentage, the composition of the exothermic dry powder is: C: 86%, Zn: 4%, Al: 4.7%, Si: 1%, Ni: 2%, Ti: 2% and Ag : 0.3%;

[0066] The environmentally friendly heating material is prepared by the following method:

[0067] Step 1, is identical with embodiment 1 step;

[0068] Step 2 is the same as in Example 1;

[0069] Step 3, the same step as in Example 1;

[0070] Step 4: Mix 5 parts of sucrose polyether, 1 part of pentamethyldiethylenetriamine, N,N-dimethylcyclohexylamine and triethylenediamine mixture, 3 parts of blowing agent, and 1 part of modified flame retardant 2. Put 2 parts of dimethylsiloxane into the reaction kettle, add the yellow transparent liquid prepared above, stir and mix at high speed for 1 minute, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly heating material for flooring and a preparation method thereof. The environment-friendly heating material is prepared from the following raw materials in parts by weight: 20-30 parts of heating dry powder, 1-10 parts of binder and 80-120 parts Polyurethane; the preparation of heat-generating dry powder: Weigh each raw material composed of the composition of heat-generating dry powder, then add each raw material in the agitator, stir and mix evenly, and obtain heat-generating dry powder; the present invention adds each A kind of auxiliary agent, the prepared polyurethane insulation material is more environmentally friendly, and the thermal conductivity of the insulation material is low, the flame retardancy is good, the water absorption rate is low and the compression strength is large; By adding the mixture A into the polyurethane material as a filler, the prepared The environmentally friendly heating material has good mechanical and electrical properties, fast heating and uniform heating.

Description

technical field [0001] The invention relates to the technical field of floor materials, in particular to an environment-friendly heating material for floors and a preparation method thereof. Background technique [0002] The floor is a kind of ground decoration material. There are many classifications of the floor. According to the structure, there are: natural landscape Fengshui floor, solid wood floor, reinforced composite wood floor, solid wood composite floor, bamboo wood floor, cork floor, etc.; according to the use classification: household Occasion floor, floor for commercial occasions, anti-static floor, outdoor floor, special floor for stage dance, special floor for sports hall, special floor for track and field, etc.; classified according to environmental protection level: E1 grade floor, E0 grade floor, JAS star standard The F4 star floor and so on. In the Chinese market, there are some special geothermal floors. In fact, as long as the base material is stable, n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/08C08L75/06C08L71/02C08L61/06C08L5/00C08L3/02C08K3/04C08K3/08C08K3/02C08G18/76C08G18/48C08G18/42B29C43/02B29C43/50E04F15/10B29K75/00
CPCB29C43/003B29C43/02B29C43/50B29C2043/503B29K2075/00C08G18/42C08G18/48C08G18/7664C08K2003/023C08K2003/0806C08K2003/0862C08K2003/0881C08K2003/0893C08K2003/2227C08K2003/2241C08K2003/2296C08K2201/011C08L75/06C08L75/08C08L2205/035E04F15/105C08L71/02C08L61/06C08L5/00C08L3/02C08K13/06C08K9/10C08K3/22C08K3/04C08K3/08C08K3/02
Inventor 陈盛卓胡卓杰黄奥迪
Owner 宁波昕科工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products