A metal surface high hardness anti-scratch, anti-fingerprint sealant

A metal surface, high-hardness technology, applied in the direction of anti-corrosion coatings, fire-resistant coatings, paints containing biocides, etc., can solve the problems that affect the application and development of magnesium alloys, reduce product qualification rate, product corrosion and scrapping, etc., to achieve film layer and The effect of strong paint bonding, improving the pass rate, and improving the hardness of the product

Active Publication Date: 2021-12-10
东莞市瑞欧表面处理科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of film layer is mainly composed of insoluble precipitates composed of calcium phosphate, manganese phosphate and other calcium-manganese compounds of phosphoric acid salts. However, due to the low hardness of this type of film layer, the film will not The layer is easily scratched and damaged by adjacent products to expose the magnesium alloy metal substrate, resulting in product corrosion and scrapping, which greatly reduces the pass rate of the product, causes unnecessary losses, and seriously affects the application and development of magnesium alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A metal surface high hardness anti-scratch, anti-fingerprint sealant
  • A metal surface high hardness anti-scratch, anti-fingerprint sealant
  • A metal surface high hardness anti-scratch, anti-fingerprint sealant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A high-hardness anti-scratch and anti-fingerprint sealant for metal surfaces. The raw materials include water-based resin, water-based silicone oil, fatty alcohol polyether, alkaline reagent, and solvent;

[0060] The preparation method of the sealing agent comprises the following steps: weighing each component, adding a solvent into a container, adding an alkali reagent and stirring to dissolve evenly, then adding water-based resin and water-based silicone oil, stirring and dissolving evenly, and finally adding fatty alcohol polyether, The temperature is raised to 50°C, and the sealing agent is obtained by stirring evenly;

[0061] The weight ratio of the water-based resin and fatty alcohol polyether is 1:0.05; the added mass of the solvent is 94.9% of the total mass of raw materials; the water-based resin is an anionic water-based polyurethane resin with a viscosity of 300mPa.s, purchased from Anhui Anda Huatai New Material Co., Ltd., the model is AH-1605B; the water-...

Embodiment 2

[0063] A high-hardness anti-scratch and anti-fingerprint sealant for metal surfaces. The raw materials include water-based resin, water-based silicone oil, fatty alcohol polyether, alkaline reagent, and solvent;

[0064] The preparation method of the sealing agent comprises the following steps: weighing each component, adding a solvent into a container, adding an alkali reagent and stirring to dissolve evenly, then adding water-based resin and water-based silicone oil, stirring and dissolving evenly, and finally adding fatty alcohol polyether, The temperature is raised to 30°C, and the sealing agent is obtained by stirring evenly;

[0065] The weight ratio of the water-based resin and fatty alcohol polyether is 1:0.01; the added mass of the solvent is 80% of the total mass of raw materials; the water-based resin is an anionic water-based polyurethane resin with a viscosity of 100mPa.s, purchased from Anhui Anda Huatai New Material Co., Ltd., the model is AH-1605B; the water-ba...

Embodiment 3

[0067] A high-hardness anti-scratch and anti-fingerprint sealant for metal surfaces. The raw materials include water-based resin, water-based silicone oil, fatty alcohol polyether, alkaline reagent, and solvent;

[0068] The preparation method of the sealing agent comprises the following steps: weighing each component, adding a solvent into a container, adding an alkali reagent and stirring to dissolve evenly, then adding water-based resin and water-based silicone oil, stirring and dissolving evenly, and finally adding fatty alcohol polyether, The temperature is raised to 70°C, and the sealing agent is obtained by stirring evenly;

[0069] The weight ratio of the water-based resin and fatty alcohol polyether is 1:0.1; the added mass of the solvent is 98% of the total mass of raw materials; the water-based resin is an anionic water-based polyurethane resin with a viscosity of 500mPa.s, purchased from Anhui Anda Huatai New Material Co., Ltd., the model is AH-0201D; the water-bas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of preparation of sealants, and provides a high-hardness, scratch-resistant, and fingerprint-resistant sealant on metal surfaces. The raw materials include at least water-based resin, water-based silicone oil, fatty alcohol polyether, alkali reagent, and solvent; The preparation method and use method of the sealing agent.

Description

technical field [0001] The present invention relates to the field of preparation of sealing agents, in particular to a metal surface high-hardness anti-scratch and anti-fingerprint sealing agent and its preparation method and use method. Background technique [0002] Hot-dip metal materials, including hot-dip galvanized metal materials and hot-dip galvanized metal materials, in order to prevent corrosion, a layer of anti-rust sealant will be coated on the surface of the hot-dip metal materials to form a protective film. Magnesium alloy has good light weight, machinability, corrosion resistance, shock absorption, dimensional stability and impact resistance, far superior to other materials. These characteristics make magnesium alloys have applications in a wide range of fields, such as transportation, electronic industry, medical field, military industry, etc., and this trend will only increase. Especially in the fields of 3C products (Computer, Consumer Electronic Product, C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D183/04C09D5/16C09D5/08C09D7/65
CPCC09D175/04C09D5/1687C09D5/18C09D5/08C08L2205/03C08L83/04C08L71/00
Inventor 李跃明
Owner 东莞市瑞欧表面处理科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap