ABS material for packaging and preparation method thereof

A technology for ABS material and packaging, applied in the field of ABS material for packaging and its preparation, can solve the problems of reduced excellent performance, poor flame retardant performance of ABS resin, etc. Effect

Inactive Publication Date: 2019-09-10
南京德荣包装制品有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flame retardancy of ABS resin is poor. How to find an additive that can improve the flame retardancy of ABS resin without reducing its excellent performance has become a research hotspot.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: a kind of ABS material for packaging, comprising the following components according to weight ratio: acrylonitrile-butadiene-styrene copolymer: 45 parts, vinyl acetate: 20 parts, ethylene: 10 parts, decabromodi Phenylethane: 3 parts, glass fiber: 4 parts, magnesium hydroxide: 7 parts, tackifying resin: 12 parts, mullite powder: 6 parts, white carbon black: 5 parts, mixed solution: 3 parts.

[0021] Glass fiber wherein is chopped glass fiber, can improve the high temperature resistance performance of ABS resin material of the present invention, the length of chopped glass fiber can be 0.3-0.4cm, mixed solution comprises ethanol, distilled water, acetic acid and polyether glycol, And the content ratio of ethanol, distilled water, acetic acid, polyether glycol and hydrochloric acid is 4:3:2:3.

[0022] The tackifying resin includes the following components according to the ratio of parts by weight: alkylphenol resin: 23-29 parts, petroleum resin: 25-27 parts,...

Embodiment 2

[0031] Embodiment 2: a kind of packaging ABS material, differs from embodiment 1 in that, comprises the following components according to weight ratio: acrylonitrile-butadiene-styrene copolymer: 50 parts, vinyl acetate: 22 parts , ethylene: 11 parts, decabromodiphenylethane: 4 parts, glass fiber: 4-6 parts, magnesium hydroxide: 8 parts, tackifying resin: 15 parts, mullite powder: 8 parts, white carbon black: 6 parts Parts, mixed solution: 5.5 parts.

[0032] The tackifying resin selected in this embodiment includes the following components according to the ratio of parts by weight: alkylphenol resin: 26 parts, petroleum resin: 26 parts, solvent naphtha: 11.5 parts, antioxidant 180: 13 parts, flame retardant Polyether polyol: 7.5 parts.

Embodiment 3

[0033] Embodiment 3: a kind of ABS material for packaging, differs from embodiment 1 in that, comprises the following components according to weight ratio: acrylonitrile-butadiene-styrene copolymer: 55 parts, vinyl acetate: 24 parts , ethylene: 12 parts, decabromodiphenylethane: 5 parts, glass fiber: 6 parts, magnesium hydroxide: 9 parts, tackifying resin: 18 parts, mullite powder: 10 parts, white carbon black: 7 parts, Mixed solution: 8 parts.

[0034] The tackifying resin selected in this embodiment includes the following components according to the ratio of parts by weight: alkylphenol resin: 29 parts, petroleum resin: 27 parts, solvent naphtha: 13 parts, antioxidant 180: 14 parts, flame retardant Polyether polyol: 9 parts.

[0035] The experimental process and data are as follows:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ABS material for packaging and a preparation method thereof, and relates to the technical field of ABS materials. The material comprises the following components in parts byweight: 45-55 parts of an acrylonitrile-butadiene-styrene copolymer, 20-24 parts of vinyl acetate, 10-12 parts of ethylene, 3-5 parts of 1,2-bis(pentabromophenyl) ethane, 4-6 parts of glass fiber, 7-9 parts of magnesium hydroxide, 12-18 parts of tackifying resin, 6-10 parts of mullite powder, 5-7 parts of white carbon black, and 3-8 parts of a mixed solution. The ABS material of the scheme has excellent flame retardant properties and high-temperature resistance.

Description

technical field [0001] The invention relates to the technical field of ABS materials, in particular to an ABS material for packaging and a preparation method thereof. Background technique [0002] ABS is a terpolymer composed of acrylonitrile, butadiene and styrene. As a thermoplastic engineering plastic, it is widely used in the automotive industry, electronics, Electrical appliances, textiles, appliances and building materials and other fields. However, the flame retardancy of ABS resin is poor. How to find an additive that can improve the flame retardancy of ABS resin without reducing its excellent performance has become a research hotspot. Contents of the invention [0003] The technical problem to be solved by the invention is how to improve the flame retardant performance of the ABS resin. [0004] In order to solve the above technical problems, the present invention provides an ABS material for packaging, comprising the following components according to weight rat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L31/04C08L61/06C08L57/02C08L71/00C08K13/04C08K7/14C08K5/03C08K3/22C08K3/36
CPCC08K2003/2224C08L55/02C08L2201/02C08L2201/08C08L2205/035C08L31/04C08L61/06C08L57/02C08L71/00C08K13/04C08K7/14C08K5/03C08K3/22C08K3/36
Inventor 杨淙茗
Owner 南京德荣包装制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com