A kind of preparation technology of fecrcomnni high entropy alloy matrix composite material

A composite material and high-entropy alloy technology is applied in the field of preparation of high-entropy alloy-based composite materials to achieve the effects of high hardness, broad application prospects and simple structure.

Active Publication Date: 2021-05-04
HEFEI UNIV OF TECH
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, using high-entropy alloy powders as raw materials, high-entropy alloy matrix composites are rarely reported by spark plasma sintering.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation technology of fecrcomnni high entropy alloy matrix composite material
  • A kind of preparation technology of fecrcomnni high entropy alloy matrix composite material
  • A kind of preparation technology of fecrcomnni high entropy alloy matrix composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] In this embodiment, the process of preparing FeCrCoMnNi high-entropy alloy-based composite material by spark plasma sintering is as follows:

[0027] 1. Preparation of mixed powder

[0028] Weigh 3wt% nano-TiC powder and 97wt% FeCrCoMnNi high-entropy alloy powder, pour the two powders into a stainless steel ball mill tank, add cemented carbide balls, the ball-to-material ratio is 10:1, the ball mill tank is first evacuated and then filled with argon Air, ball milled for 20 hours until completely mixed uniformly, the reaction sintered mixed powder is obtained;

[0029] 2. Assembly

[0030] Prepare a graphite mold with an inner diameter of 20mm, two matching graphite indenters, two graphite gaskets, and graphite paper; cut the graphite paper into two circular graphite papers with a diameter of 20mm and a rectangle that just covers the inner wall of the graphite mold Graphite paper: Paste the rectangular graphite paper on the inner wall of the graphite mold, and assemble...

experiment example 2

[0035] In this embodiment, the process of preparing FeCrCoMnNi high-entropy alloy-based composite material by spark plasma sintering is as follows:

[0036] 1. Preparation of mixed powder

[0037] Weigh 5wt% nano-TiC powder and 95wt% FeCrCoMnNi high-entropy alloy powder, pour the two powders into a stainless steel ball mill tank, add cemented carbide balls, the ball-material ratio is 10:1, the ball mill tank is first vacuumed and then filled with argon Air, ball milled for 20 hours until completely mixed uniformly, the reaction sintered mixed powder is obtained;

[0038] 2. Assembly

[0039] Prepare a graphite mold with an inner diameter of 20mm, two matching graphite indenters, two graphite gaskets, and graphite paper; cut the graphite paper into two circular graphite papers with a diameter of 20mm and a rectangle that just covers the inner wall of the graphite mold Graphite paper: Paste the rectangular graphite paper on the inner wall of the graphite mold, and assemble in th...

Embodiment 3

[0044] In this embodiment, the process of preparing FeCrCoMnNi high-entropy alloy-based composite material by spark plasma sintering is as follows:

[0045] 1. Preparation of mixed powder

[0046] Weigh 7wt% nano-TiC powder and 93wt% FeCrCoMnNi high-entropy alloy powder, pour the two powders into a stainless steel ball mill tank, add cemented carbide balls, the ball-to-material ratio is 10:1, the ball mill tank is first evacuated and then filled with argon Air, ball milled for 20 hours until completely mixed uniformly, the reaction sintered mixed powder is obtained;

[0047] 2. Assembly

[0048] Prepare a graphite mold with an inner diameter of 20mm, two matching graphite indenters, two graphite gaskets, and graphite paper; cut the graphite paper into two circular graphite papers with a diameter of 20mm and a rectangle that just covers the inner wall of the graphite mold Graphite paper: Paste the rectangular graphite paper on the inner wall of the graphite mold, and assemble...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
hardnessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation process of a FeCrCoMnNi high-entropy alloy-based composite material, which is prepared by a discharge plasma sintering process of FeCrCoMnNi powder and nano-TiC powder. -9%. In the present invention, when the sintering temperature is 1000°C, the loading pressure is 50MPa, the holding time is 5min, and the addition amount of TiC is 7%, the performance of the FeCrCoMnNi high-entropy alloy matrix composite material obtained by spark plasma sintering is better, and the hardness, room temperature yield strength and 600°C high temperature yield strength are better. They are 1092.4HV, 979.7MPa, 563.6MPa respectively. TiC and the M formed by the reaction 23 C 6 The strengthening phase is evenly distributed in the FeCrCoMnNi high-entropy alloy matrix, which plays the role of dispersion strengthening.

Description

technical field [0001] The invention relates to a preparation process of a FeCrCoMnNi high-entropy alloy-based composite material, and belongs to the field of preparation of high-entropy alloy-based composite materials. Background technique [0002] The design of multi-principal high-entropy alloys breaks through the design limitations of traditional metal materials, and high-entropy alloy materials with excellent properties such as high hardness, high strength, and corrosion resistance can be obtained through reasonable composition design. Among all the currently studied high-entropy alloy systems, the FeCrCoMnNi high-entropy alloy with a stable single-phase face-centered cubic structure (FCC) is the most popular among researchers. The FeCrCoMnNi high-entropy alloy exhibits high plasticity at room temperature and low temperature, and its mechanical properties change slightly with temperature at high temperature, and it has high temperature stability. However, the hardness ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C30/00C22C32/00C22C1/05C22C1/10
CPCC22C1/05C22C30/00C22C32/0052
Inventor 钟志宏翟博汤蔚霞陈畅吴玉程
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com