Ceramic glazed tile glaze prepared from coal gangue, and preparation method and use method of ceramic glazed tile glaze

A technology for glazed tiles and coal gangue is applied in the field of porcelain glazed tile glaze and its preparation, which can solve the problems of less substitution and affecting the performance of ceramic embryos.

Active Publication Date: 2019-11-15
DONGGUAN CITY WONDERFUL CERAMICS IND PARK +1
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there have been studies on the use of coal gangue to prepare ceramic tiles, but they are mainly used in the formula of ceramic blanks, and the substitutio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of preparation method of porcelain glazed tile glaze of the present embodiment, comprises the following steps:

[0043] Step a, glaze ingredients:

[0044] In parts by weight, take 2 parts of zinc oxide, 6 parts of barium carbonate, 6 parts of zirconium silicate, 32 parts of potassium feldspar, 4 parts of desiliconized aluminum powder, 8 parts of burnt talc, 4 parts of calcite, 8 parts of kaolin, 8 parts of dolomite stone, 4 parts of quartz, and 6 parts of coal gangue; of which:

[0045] Coal gangue waste slag mainly includes the following chemical components in mass percentage:

[0046] 46.85% SiO2 , 50.35% Al 2 o 3 , 0.05% Fe 2 o 3 , 0.52% CaO, 0.04% MgO, 0.20% K 2 O, 0.06% Na 2 O and 0.6% I.L;

[0047] The performance parameters of the coal gangue waste slag are as follows: the fineness is 60 mesh, the sieve balance is 10-20%, the water mass content is 1-2%; the physical properties are small particles, no plasticity, and complete calcination.

[0048]...

Embodiment 2

[0068] A kind of preparation method of porcelain glazed tile glaze of the present embodiment, comprises the following steps:

[0069] Step a, glaze ingredients:

[0070] In parts by weight, get 4 parts of zinc oxide, 8 parts of barium carbonate, 10 parts of zirconium silicate, 38 parts of potassium feldspar, 8 parts of desilication aluminum powder, 12 parts of calcite, 6 parts of calcite, 10 parts of kaolin, 10 parts of dolomite stone, 6 parts of quartz, and 10 parts of coal gangue; of which:

[0071] Coal gangue waste slag mainly includes the following chemical components in mass percentage:

[0072] 47.82% SiO 2 , 51.36% Al 2 o 3 , 0.15% Fe 2 o 3 , 1.12% CaO, 0.12% MgO, 0.40% K 2 O, 0.15% Na 2 O and 1.4% I.L;

[0073] The performance parameters of the coal gangue waste slag are as follows: the fineness is 60 mesh, the sieve balance is 10-20%, the water mass content is 1-2%; the physical properties are small particles, no plasticity, and complete calcination.

[007...

Embodiment 3

[0094] A kind of preparation method of porcelain glazed tile glaze of the present embodiment, comprises the following steps:

[0095] Step a, glaze ingredients:

[0096] In parts by weight, take 3 parts of zinc oxide, 7 parts of barium carbonate, 8 parts of zirconium silicate, 35 parts of potassium feldspar, 6 parts of desiliconized aluminum powder, 10 parts of calcite, 5 parts of calcite, 9 parts of kaolin, and 9 parts of dolomite stone, 5 parts of quartz, and 8 parts of coal gangue; of which:

[0097] Coal gangue waste slag mainly includes the following chemical components in mass percentage:

[0098] 47.35% SiO 2 , 50.85% Al 2 o 3 , 0.11% Fe 2 o 3 , 0.82% CaO, 0.08% MgO, 0.30% K 2 O, 0.11% Na 2 O and 1.0% I.L;

[0099] The performance parameters of the coal gangue waste slag are as follows: the fineness is 60 mesh, the sieve balance is 10-20%, the water mass content is 1-2%; the physical properties are small particles, no plasticity, and complete calcination.

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of ceramic glazed tiles, in particular to a ceramic glazed tile glaze prepared from coal gangue, and a preparation method and use method of the ceramic glazed tile glaze. The ceramic glazed tile glaze is prepared from 1-5 parts of zinc oxide, 4-10 parts of barium carbonate, 4-12 parts of zirconium silicate, 30-40 parts of potassium feldspar, 2-10 partsof desiliconized aluminum powder, 6-14 parts of calcined talc, 2-8 parts of calcite, 6-12 parts of kaolin, 6-12 parts of dolomite, 3-8 parts of quartz and 5-12 parts of coal gangue waste residues, wherein the fineness of the coal gangue waste residues is that screening residues of 60 meshes is 10-20%, and the mass content of water is 1-2%. According to the glaze, the cheap coal gangue waste residues are adopted to replace high-cost calcined kaolin, so that cost of the glaze is greatly reduced, and raw material cost per ton can be reduced by 60% or above. In addition, the texture and luster ofthe glaze surface are finally ensured to meet use requirements by controlling the glaze slurry performance, the glaze formula and the glazing conditions.

Description

technical field [0001] The invention relates to the technical field of porcelain glazed tiles, in particular to a porcelain glazed tile glaze prepared from coal gangue and a preparation method and application method thereof. Background technique [0002] In recent years, the ceramic industry has developed rapidly, and the demand for raw materials is also increasing. As we all know, mineral resources are non-renewable resources. Most ceramic companies are constantly improving the whiteness of ceramic bodies and improving the market competitiveness of their products. However, high-quality raw materials are decreasing day by day, and the rise in raw material prices directly leads to high production costs. Amplitude rises. Therefore, developing new raw materials, reducing production costs and improving product quality is a new research direction in the current ceramic industry. [0003] With the development of industry, the demand for electricity in the domestic market is incr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/89
CPCC03C8/00C04B41/89C04B41/52C04B41/5022C04B41/4539C04B41/4572
Inventor 杜希希周青龙友福王爱芳
Owner DONGGUAN CITY WONDERFUL CERAMICS IND PARK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap