A kind of genuine stone paint emulsion and preparation method thereof
A technology of real stone paint and emulsion, applied in the field of real stone paint emulsion and its preparation, can solve the problems of unsuitable for general application, high price, low performance and characteristics of low-grade real stone paint, and avoid excessive local compounding additives, high glass The effect of melting temperature and high solid content
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] A kind of real stone paint emulsion, its raw material ratio is shown in Table 1, Table 2, Table 3;
[0045] (1) In the mixing kettle, water, allyloxy hydroxypropyl sulfonate sodium reactive emulsifier, and sodium bicarbonate are mixed evenly to obtain the solution at the bottom of the kettle, which is set aside;
[0046] (2) In another mixing tank, mix water, compound emulsifier, n-butyl acrylate, styrene, acrylamide, and acrylic acid evenly. At this time, the weight ratio of n-butyl acrylate and styrene is 1:1.33 , to obtain a mixed monomer solution for subsequent use;
[0047] (3) Add still bottom solution in reactor, and under the condition that temperature is 83 ℃, add initial initiator in the still bottom solution in reactor, initial initiator selects mass fraction for use and is the ammonium persulfate solution of 18.33% , and the initial initiator was prepared 20 minutes before adding to the reactor, the temperature was controlled at 86°C, and then the mixed mon...
Embodiment 2
[0053] A kind of real stone paint emulsion, its raw material ratio is shown in Table 1, Table 2, Table 3;
[0054] (1) In the mixing kettle, water, allyloxy hydroxypropyl sulfonate sodium reactive emulsifier, and sodium bicarbonate are mixed evenly to obtain the solution at the bottom of the kettle, which is set aside;
[0055] (2) In another mixing tank, mix water, compound emulsifier, n-butyl acrylate, styrene, acrylamide, and acrylic acid evenly. At this time, the weight ratio of n-butyl acrylate and styrene is 1:1.33 , to obtain a mixed monomer solution for subsequent use;
[0056] (3) Add still bottom solution in reactor, and under the condition that temperature is 83 ℃, add initial initiator in the still bottom solution in reactor, initial initiator selects mass fraction for use and is the ammonium persulfate solution of 18.33% , and the initial initiator was prepared 10 minutes before adding to the reactor, the temperature was controlled at 86°C, and then the mixed mon...
Embodiment 3
[0062] A kind of real stone paint emulsion, its raw material ratio is shown in Table 1, Table 2, Table 3;
[0063] (1) In the mixing kettle, water, allyloxy hydroxypropyl sulfonate sodium reactive emulsifier, and sodium bicarbonate are mixed evenly to obtain the solution at the bottom of the kettle, which is set aside;
[0064] (2) In another mixing tank, mix water, compound emulsifier, n-butyl acrylate, styrene, acrylamide, and acrylic acid evenly. At this time, the weight ratio of n-butyl acrylate and styrene is 1:1.33 , to obtain a mixed monomer solution for subsequent use;
[0065] (3) Add still bottom solution in reactor, and under the condition that temperature is 83 ℃, add initial initiator in the still bottom solution in reactor, initial initiator selects mass fraction for use and is the ammonium persulfate solution of 18.33% , and the initial initiator was prepared 10 minutes before adding to the reactor, the temperature was controlled at 86°C, and then the mixed mon...
PUM
| Property | Measurement | Unit |
|---|---|---|
| minimum film forming temperature | aaaaa | aaaaa |