Preparation method of aromatic anion nylon filaments

An anion, anion additive technology, applied in rayon manufacturing, filament/thread forming, single-component polyamide rayon, etc., can solve the problems of no negative ion function, no aromatic function, single product function, etc. To achieve the effect of eliminating indoor odor, increasing added value, and reasonable preparation process

Inactive Publication Date: 2019-12-13
JIANGSU YUEYUAN FIBER TECH
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] A preparation method of nylon yarn is disclosed in the Chinese patent database, the patent application number: CN201810067425.2, application date: 2018-1-23, publication number: CN108193305A, publication date: 2018-06-22; the nylon yarn It is prepared by mixing organic copper complexes with germanium powder slurry and modified anion far-infrared powder color masterbatch and nylon 6 (PA6) slices, and then melt spinning, cooling, and winding. It has far-infrared, anion functional, and no dyeing process is required, but the disadvantage of the product is that the compatibility between germanium powder slurry and PA6 material is poor, making it difficult to manufacture, and the product has a single function and does not have an aromatic function
In addition, a production method of aromatic nylon fibers is also disclosed in the Chinese patent database. The application number of this patent is: CN 201110450221.5, the application date: 2011-12-29, the publication number: CN103184573A, the publication date: 2013-07-3 The nylon fiber preparation method is as follows: mix the essence clathrate and nylon chips, and prepare masterbatches by granulating through a granulator, then mix the masterbatches with nylon chips, and obtain aroma function through screw melt spinning. Nylon fiber: the production process of this invention is simple, the performance of the produced nylon fiber is good, it is easy to post-process, it is washable, and the fragrance releases for a long time, but the advantage is that the product does not have a single function and does not have the function of negative ions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of aromatic anion nylon filaments

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing aromatic anion nylon filaments, which uses aromatic anion nylon masterbatches and nylon 6 slices as raw materials, and undergoes drying, melt spinning, filtering, metering spinning, ring air cooling, oiling, winding and other processes, Obtain aromatic anion nylon filament; Concretely comprise the following steps:

[0021] 1) Dry nylon 6 slices: put raw nylon 6 slices into a vacuum drum dryer, feed steam or heat transfer oil with a pressure of 0.3MPa into the drum jacket, keep the temperature at 130°C, rotate the drum and start The vacuum pump is used to evacuate, the vacuum degree is maintained at 0.06MPa, the drying time is 5 hours, and the moisture content of the dried nylon 6 slices is controlled below 100ppm.

[0022] 2) Dry the aromatic anion nylon masterbatch: put the prepared aromatic anion nylon masterbatch into the sealed silo, let dry hot air into the bottom of the sealed silo, keep the temperature at 120°C, and dry for 5 hours. The mo...

Embodiment 2

[0027] A kind of preparation method of aromatic anion nylon filament is characterized in that comprising the following steps:

[0028] 1) Dry the nylon 6 slices: Put the raw nylon 6 slices into the vacuum drum dryer, feed steam or heat transfer oil with a pressure of 0.4MPa into the drum jacket, keep the temperature at 140°C, rotate the drum and start The vacuum pump is used to evacuate, the vacuum degree is maintained at 0.07MPa, the drying time is 6 hours, and the moisture content of the dried nylon 6 slices is controlled below 100ppm.

[0029] 2) Dry the aromatic anion nylon masterbatch: put the prepared aromatic anion nylon masterbatch into the sealed silo, let dry hot air into the bottom of the sealed silo, keep the temperature at 120°C, and dry for 6 hours. The moisture content of aromatic negative ion nylon masterbatch is controlled below 60ppm. The aromatic negative ion nylon masterbatch contains 5% by weight aromatic negative ion additive and 95% by weight nylon 6 ch...

Embodiment 3

[0034] A kind of preparation method of aromatic anion nylon filament is characterized in that comprising the following steps:

[0035] 1) Dry the nylon 6 slices: Put the raw nylon 6 slices into the vacuum drum dryer, feed steam or heat transfer oil with a pressure of 0.5MPa into the drum jacket, keep the temperature at 150°C, rotate the drum and start The vacuum pump is used to evacuate, the vacuum degree is maintained at 0.08MPa, the drying time is 7 hours, and the moisture content of the dried nylon 6 slices is controlled below 100ppm.

[0036] 2) Dry the aromatic anion nylon masterbatch: put the prepared aromatic anion nylon masterbatch into the sealed silo, let dry hot air into the bottom of the sealed silo, keep the temperature at 120°C, and dry for 7 hours. The moisture content of aromatic negative ion nylon masterbatch is controlled below 60ppm. The aromatic negative ion nylon masterbatch contains 5% by weight aromatic negative ion additive and 95% by weight nylon 6 ch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of aromatic anion nylon filaments in the field of chemical fiber production. The method comprises the following steps of drying and mixing aromatic anion nylon master batch and nylon 6 slice raw materials to obtain a mixture; then, extruding and melting the mixture through a screw to obtain a melt, and then preparing the nylon filaments with an aromaticanion function through the procedures of filtering, metering spinning, circular blowing for cooling and shaping, oiling and winding. According to the nylon filaments, the aromatic anion nylon masterbatch and nylon 6 slices are adopted for melt spinning, the preparation method is reasonable, the operability is high, and industrial implementation is easy. The nylon filaments can continuously release anions and a fragrant and fresh smell and has not only the functions of purifying air and removing indoor peculiar smell but also a good healthcare effect. The aromatic anion nylon filaments obtained by means of the method have the advantages of high spinnability, lasting functions and long service life, and can be widely applied to the fields of clothing, home textiles, automobile interior decoration and the like.

Description

technical field [0001] The invention relates to a functional nylon fiber, in particular to a method for preparing aromatic anion nylon filaments, and belongs to the field of chemical fiber technology manufacturing. Background technique [0002] With the improvement of people's living standards, functional textiles have become a necessity in daily life, and their application fields are becoming more and more extensive. [0003] A preparation method of nylon yarn is disclosed in the Chinese patent database, the patent application number: CN201810067425.2, application date: 2018-1-23, publication number: CN108193305A, publication date: 2018-06-22; the nylon yarn It is prepared by mixing organic copper complexes with germanium powder slurry and modified anion far-infrared powder color masterbatch and nylon 6 (PA6) slices, and then melt spinning, cooling, and winding. It has far-infrared, anion Function, and no dyeing process, but the disadvantage of the product is that the comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/08D01D5/092D01F1/10D01F6/90
CPCD01D5/08D01D5/092D01F1/10D01F6/90
Inventor 金光宝
Owner JIANGSU YUEYUAN FIBER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com