PVD vacuum coating process and coating workpiece

A vacuum coating and process technology, applied in the direction of vacuum evaporation coating, metal material coating process, sputtering coating, etc., can solve the problems of unqualified film layer of the workpiece, uneven coating, hurting people, etc., and achieve the improvement of the working environment , reduce the risk of bursting, and improve work efficiency

Active Publication Date: 2019-12-27
海盐鑫中岳电子科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The following deficiencies exist in the existing PVD vacuum coating process: during the workpiece coating process, the workpiece is hung on the workpiece hanger for spray coating. Coating nozzle, its coating film is not uniform, so that the partial film layer of the workpiece is unqualified; the vacuum pump used for vacuuming will vibrate during operation, and the noise generated greatly affects the working environment of the factory personnel, and the vacuum pump connected Due to the long-term extrusion of the atmospheric pressure, the internal stress of the vacuum tank is difficult to eliminate, which will easily lead to bursting; at present, the knives are manually put into the cleaning pool of the ultrasonic cleaning machine. and there is a risk of injury

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVD vacuum coating process and coating workpiece
  • PVD vacuum coating process and coating workpiece
  • PVD vacuum coating process and coating workpiece

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention;

[0036] The present embodiment provides a kind of PVD vacuum coating process, comprises the following steps:

[0037] Step 1: Surface treatment of the base material; wipe and clean the surface of the base material, remove oil and dust; ensure that the base material is clean and dry;

[0038] Step 2: base coating and drying of the base material; coating coating oil on the surface of the base material, and then drying, the drying temperature is 60-70 degrees Cels...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a PVD vacuum coating process. The PVD vacuum coating process comprises the following steps that 1, the surface of a base material is treated, specifically, the surface of the base material is wiped and washed, and degreasing and dedusting treatments are conducted; and the cleanness and dryness of the base material are ensured; 2, prime coating and drying of the base material are conducted, specifically, the surface of the base material is coated with coating oil, then drying is conducted, the drying temperature is 60-70 DEG C, and the drying time is 2 hours; 3, coatingis conducted, specifically, the base material in the step 2 is placed in a vacuum coating furnace, a vacuumizing device vacuumizes the vacuum coating furnace, and after the vacuum degree reaches the requirements, the vacuum coating furnace starts coating; 4, cleaning is conducted, specifically, the coated workpiece is put into an ultrasonic cleaning device for cleaning; and 5, drying is conducted,specifically, the cleaned workpiece is dried, and packaging is conducted.

Description

technical field [0001] The invention belongs to the technical field of PVD vacuum coating, and in particular relates to a PVD vacuum coating process and a coating workpiece. Background technique [0002] Empty coating is an important aspect in the field of vacuum applications. It is based on vacuum technology, uses physical or chemical methods, and absorbs a series of new technologies such as electron beams, molecular beams, ion beams, plasma beams, radio frequency and magnetron. Scientific research and practical production provide a new process for thin film preparation. Simply put, the method of evaporating or sputtering metals, alloys or compounds in a vacuum to solidify and deposit them on the coated object is called vacuum coating. [0003] The following deficiencies exist in the existing PVD vacuum coating process: during the workpiece coating process, the workpiece is hung on the workpiece hanger for spray coating. Coating nozzle, its coating is not uniform, so that...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/50C23C14/56C23C14/24
CPCC23C14/24C23C14/50C23C14/56
Inventor 吴晓明
Owner 海盐鑫中岳电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products