Wire drawing process of automobile mark

A technology for automobile signage and wire drawing, which is applied in the direction of manufacturing tools, metal processing equipment, detergent compositions, etc., can solve problems such as affecting mechanical efficiency, production process and product performance, no effect, particularly good non-foaming cleaning agent, difficult to remove, etc. , to achieve the effect of high dispersibility, high dispersion retention and easy diffusion

Active Publication Date: 2020-02-07
NINGBO SWELL IND CO LTD
View PDF20 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the prior art, the car signs should be treated with PVD due to processing needs. Before the PVD treatment, the car signs need to be cleaned with high precision. However, most of the existing cleaning agents with better cleaning effects have more foam and are difficult to remove. The foam of the cleaning agent will great

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wire drawing process of automobile mark

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A wire drawing process for an automobile label, comprising the steps of:

[0047] S1, drawing process;

[0048] a. Use a laser laser machine for a wire drawing; the surface is for a wire drawing with polishing properties, and the vacuum degree is 2.5 -1 Pa, frequency 30KHz, speed 1500mm / s, temperature 50℃, time 30min;

[0049] b. Use a laser laser machine for secondary drawing; the surface is drawn with lines, and the vacuum degree is 2.5 -1Pa, frequency 30KHz, speed 1500mm / s, temperature 50℃, time 30min;

[0050] c. Ultrasonic treatment; time 3min;

[0051] d. Surface wipe;

[0052] S2, PVD surface treatment process;

[0053] Step 1, PVD pre-treatment; clean the car signs with a cleaning agent for 15 minutes;

[0054] Step 2, baking; baking in a vacuum furnace at a temperature of 80°C for 10 minutes;

[0055] Step 3, hang up;

[0056] Step 4, coating;

[0057] Step 5, hang down.

[0058] The preparation steps of the cleaning agent in step 1 are: take the requ...

Embodiment 2

[0061] A wire drawing process for an automobile label, comprising the steps of:

[0062] S1, drawing process;

[0063] a. Use a laser laser machine for a wire drawing; the surface is for a wire drawing with polishing properties, and the vacuum degree is 2.5 -1 Pa, frequency 40KHz, speed 1600mm / s, temperature 60℃, time 35min;

[0064] b. Use a laser laser machine for secondary drawing; the surface is drawn with lines, and the vacuum degree is 2.5 -1 Pa, frequency 40KHz, speed 1600mm / s, temperature 60℃, time 35min;

[0065] c. Ultrasonic treatment; time 5min;

[0066] d. Surface wipe;

[0067] S2, PVD surface treatment process;

[0068] Step 1, PVD pre-treatment; clean the car signs with a cleaning agent for 25 minutes;

[0069] Step 2, baking; baking in a vacuum furnace at a temperature of 80°C for 15 minutes;

[0070] Step 3, hang up;

[0071] Step 4, coating;

[0072] Step 5, hang down.

[0073] The preparation steps of the cleaning agent in step 1 are: take the req...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of metal processing processes, and discloses a wire drawing process of an automobile mark. The wire drawing process comprises the following steps of S1, the wire drawing procedure and S2 the PVD surface treatment procedure. S2 further comprises the following steps of PVD pretreatment, wherein the automobile mark is cleaned through a cleaning agent, andtime ranges from 15 min to 25 min; secondly, baking, wherein the automobile mark is baked for 10-15 min at the vacuum furnace temperature ranging from 80 DEG C to 90 DEG C; thirdly, hanging up; fourthly, coating; and fifthly, hanging down. The cleaning agent in the first step comprises, by weight, 70-80 parts of polyethylene glycol octylphenol ether and a modifier. The modifier comprises 10-15 parts of methyl triethoxysilane. The wire drawing process has the following advantages and effects that oil dirt can be separated from the metal surface by means of polyethylene glycol octylphenol ether;and methyl triethoxysilane is grafted to polyethylene glycol octylphenol ether, the molecular weight of hydrophilic groups is increased, modified polyethylene glycol octylphenol ether can enter a liquid film more easily, and bubbles can be diffused more easily so as to be permeated and broken.

Description

technical field [0001] The invention relates to the technical field of metal processing technology, in particular to a wire drawing technology for automobile signs. Background technique [0002] The wire drawing process is a metal processing process. In metal pressure processing, the metal is forcibly passed through the mold under the action of external force, the metal cross-sectional area is compressed, and the technical processing method to obtain the required cross-sectional shape and size is called the metal wire drawing process. [0003] PVD, that is, physical vapor deposition, refers to the use of low-voltage, high-current arc discharge technology under vacuum conditions, using gas discharge to evaporate the target material and ionize both the evaporated material and the gas, and use the acceleration of the electric field to make The evaporated substance and its reaction products are deposited on the workpiece. Its function is to spray some particles with special pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K26/352B23K26/60C23G1/06C11D1/72C11D3/20C11D3/16C11D3/34C11D3/28C11D3/30C11D3/33C11D3/60
CPCB23K26/352B23K26/60C11D1/72C11D3/162C11D3/2068C11D3/28C11D3/30C11D3/33C11D3/3409C23G1/061
Inventor 许自金徐海燕宓烨辉
Owner NINGBO SWELL IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap