Processing method of high-toughness PVC pipe

A technology for PVC pipes and processing methods, applied in the field of PVC pipes, can solve the problems of poor pressure resistance of PVC pipes, hidden dangers in subsequent use, insufficient strength, etc., achieve improved weather resistance, increase high strength and high toughness, hydraulic strength and The Effect of Improving the Aging Resistance of Pipes

Inactive Publication Date: 2020-02-21
DENG QUAN PLASTIC TECH HUNAN CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PVC pipes have poor pressure resistance and insufficient strength.
These shortcomings not only limit its use, but also bring certain hidden dangers to subsequent use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A processing method for a high-toughness PVC pipe, which is made of the following raw materials according to the weight components:

[0026] 50 parts of PVC resin, 30 parts of dibutyl phthalate, 10 parts of paraffin wax, 5 parts of calcium carbonate, 5 parts of stabilizer, 2 parts of lubricant, 2 parts of auxiliary agent and 2 parts of quartz sand.

[0027] Including the following steps:

[0028] (1) Preparation of raw materials: take PVC resin, dibutyl phthalate, paraffin, calcium carbonate, stabilizer, lubricant, additives and quartz sand for standby;

[0029] (2) Preparation of calcium carbonate with different particle sizes: put the calcium carbonate in step (1) into a crusher for crushing, and crush until the particle size is less than or equal to 4mm, so as to obtain miniature calcium carbonate strips with different particle sizes, that is, different lengths;

[0030] (3) Grinding: Put the micro calcium carbonate strips obtained in step (2) into a grinder, and gr...

Embodiment 2

[0038] A processing method for a high-toughness PVC pipe, which is made of the following raw materials according to the weight components:

[0039] 65 parts of PVC resin, 35 parts of dibutyl phthalate, 13 parts of paraffin wax, 8 parts of calcium carbonate, 8 parts of stabilizer, 3 parts of lubricant, 3 parts of auxiliary agent and 3 parts of quartz sand.

[0040] Including the following steps:

[0041] (1) Preparation of raw materials: take PVC resin, dibutyl phthalate, paraffin, calcium carbonate, stabilizer, lubricant, additives and quartz sand for standby;

[0042] (2) Preparation of calcium carbonate with different particle sizes: put the calcium carbonate in step (1) into a crusher for crushing, and crush until the particle size is less than or equal to 4mm, so as to obtain miniature calcium carbonate strips with different particle sizes, that is, different lengths;

[0043] (3) Grinding: Put the micro calcium carbonate strips obtained in step (2) into a grinder, and gr...

Embodiment 3

[0051] A processing method for a high-toughness PVC pipe, which is made of the following raw materials according to the weight components:

[0052] 80 parts of PVC resin, 40 parts of dibutyl phthalate, 15 parts of paraffin wax, 10 parts of calcium carbonate, 10 parts of stabilizer, 5 parts of lubricant, 5 parts of auxiliary agent and 5 parts of quartz sand.

[0053] Including the following steps:

[0054] (1) Preparation of raw materials: take PVC resin, dibutyl phthalate, paraffin, calcium carbonate, stabilizer, lubricant, additives and quartz sand for standby;

[0055] (2) Preparation of calcium carbonate with different particle sizes: put the calcium carbonate in step (1) into a crusher for crushing, and crush until the particle size is less than or equal to 4mm, so as to obtain miniature calcium carbonate strips with different particle sizes, that is, different lengths;

[0056] (3) Grinding: Put the micro calcium carbonate strips obtained in step (2) into a grinder, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a processing method of a high-toughness PVC pipe, and relates to the field of PVC pipes, wherein the high-toughness PVC pipe comprises the raw materials: PVC resin, dibutyl phthalate, paraffin, calcium carbonate, a stabilizer, a lubricant, an auxiliary agent and quartz sand. Through design of the processing method of the high-toughness PVC pipe, calcium carbonate is added into PVC; calcium carbonate is ground into micro calcium carbonate powder with different particle sizes, namely different lengths, through a stirring mechanism and a grinding mechanism; then the micro calcium carbonate powder is uniformly added into the raw materials and mixed and stirred with the raw materials; the high strength and high toughness of the PVC pipe can be improved through different regular arrangement of the calcium carbonate in the raw materials; compared with a pipe produced according to a common formula, the weather resistance of the pipe is remarkably improved, the impact strength of the pipe is improved, and the hydraulic strength and the aging resistance of the pipe are improved.

Description

technical field [0001] The invention relates to the field of PVC pipes, in particular to a processing method for high-toughness PVC pipes. Background technique [0002] The main component of PVC is polyvinyl chloride, and other ingredients are added to enhance its heat resistance, toughness, and ductility. The top layer of this surface film is lacquer, the main component in the middle is polyvinyl chloride, and the bottom layer is back-coated adhesive. [0003] PVC pipe is a type of pipe mainly composed of polyvinyl chloride. At present, PVC pipes are widely used in power cable laying and other fields. However, PVC pipes have poor pressure resistance and insufficient strength. These shortcomings not only limit its use, but also bring certain hidden dangers to subsequent use. Therefore, it is the problem to be solved by the present invention to provide a processing method for high-toughness PVC pipes. Contents of the invention [0004] The object of the present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/06C08K13/02C08K5/12C08K3/26C08K3/36
CPCC08K2003/265C08L27/06C08L2201/08C08L2203/18C08L2205/03C08L2205/035C08L91/06C08K13/02C08K5/12C08K3/26C08K3/36
Inventor 邓权
Owner DENG QUAN PLASTIC TECH HUNAN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products