A kind of high hydrophobic angle TPU film and preparation method thereof

A technology of film and polyvinylidene fluoride, which is applied in the field of TPU film and its preparation, TPU film with high hydrophobic angle and its preparation, can solve the problems of poor hydrophobic performance and small hydrophobic angle, and achieve easy roll-off and improved hydrophobic angle , Excellent effect of hydrophobic performance

Active Publication Date: 2021-09-24
DONGGUAN XIONGLIN NEW MATERIAL TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In view of the deficiencies in the prior art, the purpose of the present invention is to provide a TPU film and its preparation method, especially to provide a high hydrophobic angle TPU film and its preparation method, to solve the problem that the existing TPU film has a small hydrophobic angle and poor hydrophobic performance. bad question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high hydrophobic angle TPU film and preparation method thereof
  • A kind of high hydrophobic angle TPU film and preparation method thereof
  • A kind of high hydrophobic angle TPU film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The preparation raw material of the TPU film that the present embodiment provides comprises the following components by weight:

[0047]

[0048] Preparation:

[0049] (1) Add toluene diisocyanate and polyethylene glycol adipate diol into the container, and under the condition of stirring at a speed of 160r / min, vacuum dehydrate at 65°C for 2 hours;

[0050] (2) Add 1,2-propanediol and dibutyltin dioctoate to step (1) and mix and react at 65°C for 18 hours;

[0051] (3) Add hexafluorobutyl methacrylate, octadecyl acrylate and polyvinylidene fluoride to the mixture after the reaction in step (2), stir and mix at 68°C for 18 hours, and then add to the twin-screw extruder The TPU film was obtained by extrusion molding, wherein the temperature of the feeding section of the twin-screw extruder was 115°C, the temperature of the mixing section was 150°C, the temperature of the extrusion section was 170°C, and the temperature of the head was 155°C.

Embodiment 2

[0053] The preparation raw material of the TPU film that the present embodiment provides comprises the following components by weight:

[0054]

[0055] Preparation:

[0056] (1) Add toluene diisocyanate and polyethylene adipate diethylene glycol diol into the container, and under the condition of stirring at a speed of 160r / min, vacuum dehydrate at 65°C for 2 hours;

[0057] (2) Add 1,2-propanediol and stannous octoate to step (1) and mix and react at 65°C for 18 hours;

[0058] (3) Add hexafluorobutyl methacrylate, octadecyl acrylate and polyvinylidene fluoride to the mixture after the reaction in step (2), stir and mix at 68°C for 18 hours, and then add to the twin-screw extruder The TPU film was obtained by extrusion molding, wherein the temperature of the feeding section of the twin-screw extruder was 115°C, the temperature of the mixing section was 150°C, the temperature of the extrusion section was 170°C, and the temperature of the head was 155°C.

Embodiment 3

[0060] The preparation raw material of the TPU film that the present embodiment provides comprises the following components by weight:

[0061]

[0062] Preparation:

[0063] (1) Add toluene diisocyanate and polyethylene adipate propylene glycol ester diol into the container, and under the condition of stirring at a speed of 160r / min, vacuum dehydrate at 65°C for 2 hours;

[0064] (2) Add ethylene glycol and dibutyltin diacetate to step (1) and mix and react at 65°C for 18 hours;

[0065] (3) Add hexafluorobutyl methacrylate, octadecyl acrylate and polyvinylidene fluoride to the mixture after the reaction in step (2), stir and mix at 68°C for 18 hours, and then add to the twin-screw extruder The TPU film was obtained by extrusion molding, wherein the temperature of the feeding section of the twin-screw extruder was 115°C, the temperature of the mixing section was 150°C, the temperature of the extrusion section was 170°C, and the temperature of the head was 155°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a TPU film with a high hydrophobic angle and a preparation method thereof. The preparation raw materials of the TPU film include the following components in parts by weight: 30-50 parts of toluene diisocyanate, 20-40 parts of polyester polyol, formaldehyde 4-6 parts of hexafluorobutyl acrylate, 1-2 parts of octadecyl acrylate, 5-10 parts of polyvinylidene fluoride, 3-8 parts of chain extender, and 1-3 parts of catalyst; TPU film provided by the invention , through the use of hexafluorobutyl methacrylate and octadecyl acrylate, the fluorine-containing groups are regularly arranged on the polymerization surface, and a stable film is formed after reaction, and the formed coating has low surface free energy; further mixing Polyvinylidene fluoride with good insulation makes it easier for water droplets to roll off the surface of the film. The combination with fluorine-containing groups improves the hydrophobic angle of the film. The hydrophobic angle can reach 121°-124°, and the hydrophobicity is excellent. Application bright future.

Description

technical field [0001] The invention belongs to the field of polymer materials, and relates to a TPU film and a preparation method thereof, in particular to a high hydrophobic angle TPU film and a preparation method thereof. Background technique [0002] TPU (Thermoplastic polyurethanes), thermoplastic TPU elastomer, due to its good elasticity, good physical properties, and various mechanical strengths, it is widely used in processing methods such as injection, extrusion, calendering, and dissolved into solution resins. It is a plastic processing It is a plastic material often used by the industry, and its products cover a range of industrial applications and civilian necessities. [0003] TPU film is a film made by special processes such as calendering, casting, film blowing and coating on the basis of TPU pellets. In recent years, due to the continuous development of new products, new opportunities have been created for the plastic processing industry to create low-cost, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/06C08L33/16C08L27/16C08J5/18C08G18/10C08G18/66C08G18/32
CPCC08G18/10C08G18/664C08J5/18C08J2375/06C08J2427/16C08J2433/16C08G18/3206
Inventor 王一良何建雄杨博
Owner DONGGUAN XIONGLIN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com