High-strength impact-resistant composite material for automotive interior decoration member, and preparation method thereof
A technology for automotive interior parts and composite materials, which is applied in the field of high-strength impact-resistant composite materials for automotive interior parts and its preparation, and can solve the problems of poor rigidity, low tensile strength, and failure to meet the standards for automotive materials, etc. problems, to achieve the effect of improving mechanical and physical properties, increasing tensile strength, and improving low-temperature toughness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0036] A high-strength impact-resistant composite material for automotive interior parts, prepared by the following method:
[0037] Weigh 80 parts of nylon 66, 140 parts of reinforced nylon sample, 130 parts of rubber copolymer sample, 5 parts of maleic anhydride grafted ethylene-acrylic acid copolymer, 5 parts of ethylene-hexene copolymer, hydrogenated ethylene - 5 parts of butadiene-styrene copolymer, 5 parts of carbon black, 0.8 part of tetramethylthiuram disulfide and 2 parts of glass fiber, 2 parts of calcium carbonate, 1 part of quartz powder, add to a high-speed mixer and mix evenly , the rotation speed of the mixer is 5000r / min, and the heating temperature is 120°C; the above mixture is extruded and granulated by a co-rotating, parallel twin-screw extruder; the screw speed is 80r / min, and the extrusion temperature is 220°C to obtain Example 1 High-strength impact-resistant composite materials.
Embodiment 2
[0039] A high-strength impact-resistant composite material for automotive interior parts, prepared by the following method:
[0040] Weigh 50 parts of nylon 66 according to the following parts by weight, 22 parts of reinforced nylon samples, 15 parts of rubber copolymer samples, 5 parts of maleic anhydride grafted ethylene-acrylic acid copolymers, 5 parts of ethylene-butylene copolymers, carbon black 1 part, 0.3 parts of tetramethylthiuram disulfide and 1 part of talc powder, put into a high-speed mixer and mix evenly, the speed of the mixer is 4500r / min, and the heating temperature is 100°C; The screw extruder extruded and granulated; the screw speed was 80r / min, and the extrusion temperature was 210°C to obtain the high-strength impact-resistant composite material of Example 2.
Embodiment 3
[0042] A high-strength impact-resistant composite material for automotive interior parts, prepared by the following method:
[0043] Weigh 60 parts of nylon 66 according to the following parts by weight, 3 25 parts of reinforced nylon samples, 3 20 parts of rubber copolymer samples, 1 part of maleic anhydride grafted ethylene-acrylic acid copolymer, 5 parts of ethylene-propylene-octene terpolymer 1 part, 1 part of carbon black, 0.3 part of tetramethylthiuram disulfide and 1 part of mica powder, add them into a high-speed mixer and mix evenly, the speed of the mixer is 4500r / min, and the heating temperature is 110°C; Parallel twin-screw extruder extruded and granulated; the screw speed was 80r / min, and the extrusion temperature was 210°C to obtain the high-strength impact-resistant composite material of Example 3.
PUM
Property | Measurement | Unit |
---|---|---|
melting point | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com