A kind of composite yarn, cloth and manufacturing method thereof
A technology of yarn and spun yarn, which is applied in the manufacture of rayon, artificial filament and yarn made of viscose, etc. It can solve the problems of affecting the experience and poor comfort of composite yarns, so as to improve immunity, The effect of unique style and improved comfort of use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0039] Step 1, the preparation of the polyester inner core adopts one of the following two methods: 1) take 0.5-10% of Bianstone by mass percentage, 0.5-10% of zinc oxide and polyester used as the balance, 2) Take 0.5-10% of Bianstone, 0.5-10% of zinc oxide and purified terephthalic acid (PTA) or terephthalic acid as the remainder by mass percentage Methyl ester (DMT) and ethylene glycol (MEG) are produced by esterification or transesterification and polycondensation to obtain polyethylene terephthalate (PET), which is made by spinning into tow and post-processing;
[0040] Step 2. Preparation of cellulose staple fiber yarn: take 0.2-6% by mass of far-infrared ceramic powder, metal oxide powder, carbon fiber or jade, and viscose fiber, bamboo fiber, modal fiber or One or more of the lyocell fibers are obtained after mixing, blowing, top, drawing, roving, spun yarn and winding in sequence;
[0041] Step 3, winding the cellulose staple yarn on the polyester inner core to obtain...
Embodiment 1
[0044] like figure 1 As shown, a composite yarn includes a polyester inner core 1 and a cellulose staple yarn 2 wound on the polyester inner core 1 . The polyester inner core 1 contains 0.5% by mass of Bianstone and 0.5% of zinc oxide; the cellulose staple fiber yarn 2 contains 0.2% by mass of far-infrared components. It should be noted that the polyester inner core is polyester filament. And the cellulose staple fiber yarn is viscose fiber. The far-infrared component is far-infrared ceramic powder.
[0045] A cloth made of composite yarns.
[0046] A manufacturing method of composite yarn, comprising the steps:
[0047] Step 1. Preparation of polyester inner core: take 0.5% of Bianstone, 0.5% of zinc oxide and polyester used as the balance by mass percentage, and cut them after spinning into tow;
[0048] Step 2. Preparation of cellulose staple fiber yarn: take far-infrared ceramic powder with a mass percentage of 0.2% and viscose fiber as the balance, and perform mixing...
Embodiment 2
[0052] like figure 1 As shown, a composite yarn includes a polyester inner core 1 and a cellulose staple yarn 2 wound on the polyester inner core 1 . The polyester inner core 1 contains 5% by mass of Bianstone and 5% of zinc oxide; the cellulose staple yarn 2 contains 3% by mass of far-infrared components. It should be noted that the polyester inner core is polyester filament. And the cellulose staple fiber yarn is viscose fiber. The far-infrared component is far-infrared ceramic powder.
[0053] A cloth made of composite yarns.
[0054] A manufacturing method of composite yarn, comprising the steps:
[0055] Step 1. Preparation of polyester inner core: take 5% of Bianstone by mass, 5% of zinc oxide and polyester used as the balance, and cut them after spinning into tow;
[0056] Step 2. Preparation of cellulose staple fiber yarn: take the far-infrared ceramic powder with a mass percentage of 3% and viscose fiber as the balance, and perform mixing, cleaning, top, drawing,...