Gemini concrete air entraining agent and preparation method thereof

A concrete and twin-type technology, which is applied in the direction of sulfonate preparation, carboxylate preparation, chemical instruments and methods, etc., can solve problems such as harsh reaction conditions and complex structures, and achieve reduced freezing damage, good composite performance, and buffer expansion stress Effect

Active Publication Date: 2020-05-19
山东建科建筑材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems of the existing concrete air-entraining agent, complex structure and harsh reaction conditions, the invention discloses a twin-type concrete air-entraining agent and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gemini concrete air entraining agent and preparation method thereof
  • Gemini concrete air entraining agent and preparation method thereof
  • Gemini concrete air entraining agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1: a kind of preparation method of twin type concrete air-entraining agent, it comprises the steps:

[0034] Step (1): Add 1.0mol (262g) C1 and 1.0mol (98g) maleic anhydride at 40°C, add 5.24g anhydrous sodium acetate, and stir for 3 hours to obtain maleic anhydride fatty alcohol polyoxyethylene ethers monoester.

[0035] Step (2): Heat up to 130°C, add 0.50mol (31g) D1, continue to heat up to 150°C, keep the vacuum less than 0.2 MPa, and stir for 6 hours.

[0036] Step (3): Lower the temperature, control the temperature at 100°C, add 1.0mol (104g) sodium bisulfite, 8.82g octadecyltrimethylammonium bromide and water, and stir for 2 hours. The obtained product was dissolved in water and adjusted to a solution with a solid content of 50%. It is the twin-type concrete air-entraining agent of the present invention.

[0037] The air-entraining agent was diluted to 5%, and the surface tension of the solution was measured to be 31.2 mN / m.

Embodiment 2

[0038] Embodiment 2: a kind of preparation method of twin-type concrete air-entraining agent, it comprises the steps:

[0039] Step (1): Add 1.15mol (365.7g) of C2 and 1.0mol (98g) of maleic anhydride at 90°C, add 10.97g of p-toluenesulfonic acid, and stir for 2 hours to obtain maleic anhydride fatty alcohol polyoxygen Vinyl ether monoester.

[0040] Step (2): Heat up to 120°C, add 0.55mol (49.5g) D2, continue to heat up to 150°C, keep vacuum less than 0.2 MPa, and stir for 6 hours.

[0041] Step (3): Lower the temperature, control the temperature at 90°C, add 1.1mol (114.4g) of sodium bisulfite, 9.8g of cetyltrimethylammonium bromide and water, and stir for 1.5 hours to react. The obtained product was dissolved in water and adjusted to a solution with a solid content of 40%. It is the twin-type concrete air-entraining agent of the present invention.

[0042] The air-entraining agent was diluted to 5%, and the surface tension of the solution was measured to be 30.5 mN / m.

Embodiment 3

[0043] Embodiment 3: a kind of preparation method of twin-type concrete air-entraining agent, it comprises the steps:

[0044] Step (1): Add 1.2mol (607.2g) of C3 and 1.0mol (98g) of maleic anhydride at 80°C, add 24.29g of concentrated sulfuric acid, and stir for 1 hour to obtain maleic anhydride fatty alcohol polyoxyethylene ethers ester.

[0045] Step (2): Heat up to 125°C, add 0.60mol (66g) of D3, continue to heat up to 140°C, keep the vacuum less than 0.2 MPa, and stir for 4 hours.

[0046]Step (3): Lower the temperature, control the temperature at 85°C, add 1.2mol (124.8g) sodium bisulfite, 11.76g tetradecyltrimethylammonium bromide and water, and stir for 1 hour. The obtained product was dissolved in water and adjusted to a solution with a solid content of 30%. It is the twin-type concrete air-entraining agent of the present invention.

[0047] The air-entraining agent was diluted to 5%, and the measured surface tension of the solution was 30.8 mN / m.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
surface tensionaaaaaaaaaa
surface tensionaaaaaaaaaa
Login to view more

Abstract

According to the gemini concrete air entraining agent and the preparation method thereof, the chemical structure of the gemini concrete air entraining agent belongs to a gemini surfactant, and the gemini concrete air entraining agent has higher surface activity. When the gemini concrete air entraining agent is added into concrete, uniform and fine bubbles can be generated. When the air content ofthe concrete is 4.5-5.0%, the air content in one hour is basically unchanged, and the average chord length of bubbles of the hardened concrete is 120-150 microns. The uniform and fine bubbles have a certain heat preservation effect, and more importantly, expansion stress generated after frozen water is frozen can be buffered, so that freezing damage to concrete is reduced.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a concrete air-entraining agent capable of significantly improving the durability of concrete and a preparation method thereof. Background technique [0002] Concrete air-entraining agent is widely used in concrete as an important independent species of concrete admixture. It can significantly improve the workability and homogeneity of freshly mixed concrete, and can improve the comprehensive durability of concrete. [0003] Currently commonly used concrete air-entraining agents include: rosin resins, alkyl and alkyl aromatic hydrocarbon sulfonic acids, fatty alcohol sulfonates, saponins, protein salts, petroleum sulfonic acid hydrochloric acid, etc. From the perspective of chemical structure, the above-mentioned air-entraining agents are all traditional single-chain surfactants, that is, amphiphilic molecules with a hydrophilic group at one end and a hydr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07C309/17C07C303/32B01F17/10B01F17/16C04B24/16C04B103/30C09K23/10C09K23/16
CPCC07C309/17C07C303/32C07C67/08C07C291/04C04B24/16C04B2103/304C07C69/60Y02W30/91
Inventor 王立亚蔡贵生鲁统卫孙璐王开宇徐磊郭向阳宋西成赵法国
Owner 山东建科建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap