A raw material homogenization process for dead-burned magnesia shaft kiln

A dead-burned magnesia and shaft kiln technology, applied in the field of refractory materials, can solve problems such as waste of magnesium resources, achieve the effects of improving density, solving uneven sintering, and saving magnesite resources

Active Publication Date: 2022-04-01
海城市军刚中档镁砂有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the defects of the prior art and solve the problem of waste of low-grade magnesite magnesium resources such as high-calcium magnesite powder ore, crushed ore, high-silicon magnesite powder ore, and crushed ore, the invention provides a dead-burned magnesite Shaft kiln raw material homogenization process, using high-calcium magnesite powder ore, crushed ore and high-silicon magnesite powder ore, crushed ore as raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Put 26 parts of natural high-calcium magnesite powder ore and crushed ore with a particle size of 0~30mm, 74 parts of natural high-silicon magnesite powder ore and crushed ore with a particle size of 0~30mm, and 15 parts of coke or Ningxia white coal in the crusher Separately crush to 200~325 meshes to get natural high-calcium magnesite powder, natural high-silicon magnesite powder, coke or Ningxia white coal powder; put all the natural high-calcium magnesite powder and natural high-silicon magnesite powder into the mix In the homogenization tank, mix at room temperature for 5 minutes and rotate at a speed of 40r / min to obtain a primary homogenized material; put the primary homogenized material into a briquetting machine and press it into a magnesia ball with a diameter of 40mm at 3Mpa; mix the magnesia ball with all Put the fuel in the formula quantity into the mixing and homogenizing tank together, mix at room temperature for 5 minutes, and rotate at a speed of 40r / min...

Embodiment 2

[0023] Put 35 parts of natural high-calcium magnesite powder ore and crushed ore with a particle size of 0~30mm, 65 parts of natural high-silicon magnesite powder ore and crushed ore with a particle size of 0~30mm and 20 parts of coke or Ningxia white coal in the crusher Separately crush to 200~325 meshes to get natural high-calcium magnesite powder, natural high-silicon magnesite powder, coke or Ningxia white coal powder; put all the natural high-calcium magnesite powder and natural high-silicon magnesite powder into the mix In the homogenizing tank, mix at room temperature for 8 minutes and rotate at 40r / min to obtain a primary homogenized material; put the primary homogenized material into a briquetting machine and press it into a magnesia ball with a diameter of 50mm at 5Mpa; mix the magnesia ball with all Put the fuel in the formula quantity into the mixing and homogenizing tank together, mix at room temperature for 8 minutes, and rotate at a speed of 40r / min to obtain the...

Embodiment 3

[0026] Put 42 parts of natural high-calcium magnesite powder ore and crushed ore with a particle size of 0~30mm, 58 parts of natural high-silicon magnesite powder ore and crushed ore with a particle size of 0~30mm, and 25 parts of coke or Ningxia white coal in the crusher Separately crush to 200~325 meshes to get natural high-calcium magnesite powder, natural high-silicon magnesite powder, coke or Ningxia white coal powder; put all the natural high-calcium magnesite powder and natural high-silicon magnesite powder into the mix In the homogenizing tank, mix at room temperature for 10 minutes and rotate at 40r / min to obtain a primary homogenized material; put the primary homogenized material into a briquetting machine and press it into a magnesia ball with a diameter of 60mm at 8Mpa; mix the magnesia ball with all Put the fuel in the formula quantity into the mixing and homogenizing tank together, mix at room temperature for 10 minutes, and rotate at a speed of 40r / min to obtain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The patent of the present invention relates to a material homogenization process for dead-burned magnesia shaft kiln, including fine grinding, primary mixing and homogenization, ball pressing, secondary mixing and homogenization, and sintering. The raw materials are and fuel. First, the natural high-calcium magnesite powder ore and crushed ore and the natural high-silicon magnesite powder ore and crushed ore are finely ground and mixed and homogenized; then the primary mixed and homogenized material is briquetted; then the briquette is mixed with fuel Carry out secondary mixing and homogenization together, and finally sinter the secondary mixing and homogenizing material at 1500-1800°C to obtain dead-burned magnesia. The method of the invention has the advantages of simple process flow, high product density and the like, and can improve the high temperature resistance and corrosion resistance of the refractory material due to the existence of the forsterite phase with a high melting point.

Description

technical field [0001] The invention relates to the technical field of refractory materials, in particular to a raw material homogenization process for a dead-burned magnesia shaft kiln. Background technique [0002] Dead-burned magnesia is the main raw material for the production of magnesia refractory products. Its sintering performance, especially the bulk density, has an important impact on the slag intrusion resistance and high-temperature mechanical properties of refractory products, and directly affects the service life of refractory materials. [0003] At present, natural magnesite is usually used to produce dead-burned magnesia. The raw materials of dead-burned magnesite are all ore lumps with a particle size of 30-120 mm. After being put into a high-temperature shaft kiln, coal or coke is used as fuel, and the temperature is controlled at 1500-1600 ° C. Obtain dead burnt magnesia. However, due to the inhomogeneity of raw materials and uneven distribution, the prep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B2/12
CPCC04B2/12
Inventor 刘士军彭子钧王明夺罗旭东周晓蕾
Owner 海城市军刚中档镁砂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com