High-performance soldering and brazing adhesive composition and preparation method thereof

An adhesive, high-performance technology, used in welding equipment, welding media, manufacturing tools, etc., to reduce carbon residues, improve brazing performance, and increase oxygen concentration

Active Publication Date: 2020-07-10
烟台精创力合科技有限公司
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the solution of adding free water can only be applied to brazing scenarios where there is no brazing flux and the contact metal has strong corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance soldering and brazing adhesive composition and preparation method thereof
  • High-performance soldering and brazing adhesive composition and preparation method thereof
  • High-performance soldering and brazing adhesive composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0043] Add 0.1 part of magnesium hydroxide, 0.1 part of nitrocellulose, and 0.1 part of potassium nitrate to the above resin solution A, and stir again. Then emulsify with the resin melt B according to the above steps, and then grind the emulsified liquid three times on a three-roller machine to obtain a solid particle diameter of 10 microns in the ground liquid to obtain the final product.

[0044] Put this product into a heating container and heat it to 100 degrees Celsius to soften. Take 1 part and 1 part of FB308S brazing flux powder and mix it in a stirring device, then add 2 parts of BAg30CuZnSn solder alloy powder, and stir to form an elastic body. Solder. The state of the elastomeric solder can achieve a certain degree of elasticity, viscosity and viscosity stability, and exhibits very excellent physical properties when making sticky tape and granular solder.

[0045] The control group was treated in the same way. Then execute Test A and Test C on them respectively. ...

Embodiment example 2

[0049] Add 0.1 part of magnesium hydroxide, 0.1 part of aluminum hydroxide, and 0.1 part of nitrocellulose to the above-mentioned resin melt solution A, and fully stir again. Then emulsify with the resin melt B according to the above steps, and then grind the emulsified liquid three times on a three-roller machine to obtain a solid particle diameter of 10 microns in the ground liquid to obtain the final product.

[0050] Put this product into a heating container and heat it to 100 degrees Celsius to soften. Take 1 part and 1 part of FB308S brazing flux powder and mix it in a stirring device, then add 2 parts of BAg30CuZnSn solder alloy powder, and stir to form an elastic body. Solder. The state of the elastomeric solder can achieve a certain degree of elasticity, viscosity and viscosity stability, and exhibits very excellent physical properties when making sticky tape and granular solder.

[0051] The control group was treated in the same way. Then execute Test A and Test C ...

Embodiment example 3

[0054] Add 0.1 part of nickel hydroxide, 0.1 part of nitrocellulose, and 0.1 part of ferric nitrate to the above-mentioned resin melt A, and fully stir again. Then emulsify with the resin melt B according to the above steps, and then grind the emulsified liquid three times on a three-roller machine to obtain a solid particle diameter of 0.5 microns in the ground liquid to obtain the final product.

[0055] Put this product into a heating container and heat it to 100 degrees Celsius to soften it. Take 1 part and 3 parts of BNi-2 solder alloy powder and stir to make a solder paste. The state of the elastomeric solder can achieve a certain degree of elasticity, viscosity and viscosity stability, and exhibits very excellent physical properties when making sticky tape and granular solder.

[0056] The control group was treated in the same way. Then execute Test B and Test D on it respectively. In control group 1, the nitrocellulose and ferric nitrate added in the above materials ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-performance soldering and brazing adhesive composition and a preparation method of the high-performance soldering and brazing adhesive composition. An adhesive contains asubstance releasing oxygen by heating, a substance releasing water by heating and an organic substance with viscous performance. All performance of the soldering and brazing adhesive can be better optimized to meet the process requirements, meanwhile soldering and brazing defects are reduced, and better soldering and brazing quality is obtained.

Description

technical field [0001] The invention relates to the technical field of brazing, in particular to a high-performance brazing adhesive composition and a preparation method thereof. Background technique [0002] During the welding process of brazing, as the temperature rises, the brazing aid gradually melts and begins to work. As the temperature continues to rise, the solder alloy also melts and flows to the brazed joint under the action of the flux. In addition to brazing fluxes and brazing alloys, the role of brazing adhesives is to link brazing fluxes, brazing filler metals, base metals and other materials involved in brazing in different ways at room temperature, so as to Meet various technological requirements. [0003] The environment in which the soldering adhesive works is normal temperature. When brazing is performed, the assembled workpiece is heated to brazing temperature, usually above 450 degrees Celsius. During the process of temperature rise, the soldering ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/36B23K35/14
CPCB23K35/025B23K35/3601B23K35/3602B23K35/3612
Inventor 孙韶
Owner 烟台精创力合科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com