Environment-friendly high-strength ultraviolet-cured acrylate pressure-sensitive adhesive and preparation method thereof

An acrylate and urethane acrylate technology, applied in the field of acrylate pressure-sensitive adhesive and its preparation, can solve the problems of solvent pollution, low pressure-sensitive adhesive strength, etc. Effect

Active Publication Date: 2020-07-24
王凤艳
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of using a large amount of solvent to pollute the environment and the low strength of the prepared pressure-sensitive adhesive in the pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Specific embodiment 1: This embodiment is an environmentally friendly high-strength UV-curable acrylate pressure-sensitive adhesive based on the weight of 30 parts to 70 parts of nano-modified polyurethane acrylate oligomer, 30 parts to 70 parts of active It is prepared from diluent, 1 part to 3 parts adhesion promoter and 0.2 part to 5 parts photoinitiator.

Example Embodiment

[0016] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the nano-modified polyurethane acrylate oligomer is prepared according to the following steps:

[0017] Add 0.1 mol of the glycol dehydrated under vacuum to a four-necked flask equipped with a stirrer, thermometer and dropping funnel. After heating to 60℃~80℃, add 0.05%~0.3% of the total weight of the glycol under stirring conditions. Then add 0.12mol~0.2mol diisocyanate monomer dropwise, then react at 60℃~80℃ for 3h~6h, then add 1%~10% of the total mass of diol with inorganic nanometer containing hydroxyl The ethyl acetate solution of the particles is reacted at 60℃~80℃ for 0.5h~2h, then 0.1mol~0.2mol of hydroxyl-containing acrylate monomer is added, and then reacted at 60℃~80℃ for 1h~1.5h Then, the ethyl acetate in the system is distilled off under reduced pressure at 40°C-50°C to obtain nano-modified polyurethane acrylate oligomer. The other steps are the same as the first embodiment.

Example Embodiment

[0018] Specific embodiment three: this embodiment is different from specific embodiment one or two in that: the diol is polypropylene glycol PPG-600, polypropylene glycol PPG-1000, polypropylene glycol PPG-1500, polypropylene glycol PPG- 2000. One or a mixture of polypropylene glycol PPG-3000 and polypropylene glycol PPG-4000; the organotin catalyst is dibutyltin dilaurate, stannous octoate, and bis(dodecylthio) Dibutyltin or dibutyltin diacetate; the diisocyanate monomers are toluene diisocyanate, 1,6-hexamethylene diisocyanate, isophorone diisocyanate, 4,4-diisocyanate dicyclohexylmethane and diphenylmethane di One or a mixture of isocyanates. The other steps are the same as the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly high-strength ultraviolet-cured acrylate pressure-sensitive adhesive and a preparation method thereof, relates to an acrylate pressure-sensitive adhesive and a preparation method thereof, and aims to solve the problems that a large amount of solvent is used in the preparation process of the existing solvent type pressure-sensitive adhesive to pollutethe environment and the prepared pressure-sensitive adhesive is low in strength. The pressure-sensitive adhesive is prepared from a nano-modified urethane acrylate oligomer, an active diluent, an adhesion promoter and a photoinitiator. The preparation method comprises the following steps: 1, weighing; and 2, sequentially mixing the reactive diluent, the nano-modified urethane acrylate oligomer, the photoinitiator and the adhesion promoter. When the nano-modified urethane acrylate oligomer is synthesized, hydroxyl-containing nanoparticles are introduced to participate in the reaction, and theadhesion promoter is introduced so that the peel strength is obviously improved. The environment-friendly high-strength ultraviolet-cured acrylate pressure-sensitive adhesive can be obtained.

Description

technical field [0001] The invention relates to an acrylate pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] Pressure-sensitive adhesive is a kind of pressure-sensitive adhesive, which can stick to other surfaces by applying appropriate pressure during use. Due to its special bonding characteristics, pressure-sensitive adhesive products are currently widely used in various industries such as printing and packaging. Industry. With the continuous improvement of people's environmental awareness and technical requirements, the research and development of environmentally friendly and high-performance pressure-sensitive adhesives has become a research hotspot. UV-curable pressure-sensitive adhesive is a new type of energy-saving and environment-friendly pressure-sensitive adhesive, which has the characteristics of fast curing speed, low energy consumption, no pollution, good water resistance and heat resistance. UV-curable pressure-sens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/14C09J11/04
CPCC09J175/14C09J11/04C08K2201/011C08K2003/2227C08K3/36C08K3/22
Inventor 王凤艳
Owner 王凤艳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap