Processing method of weather-proof improved artificial turf backing fabric

A technology of artificial turf and processing method, applied in the direction of fiber type, light-fast fiber, textile and papermaking, etc., can solve the problems of easy damage and short service life of turf, achieve good thermal stability, improve weather resistance, and improve water resistance. Effect

Active Publication Date: 2020-07-31
扬州海众织物有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing lawn base cloth is woven from pp material after wire drawing, but the lawn base cloth is exposed to the open air, exposed to wind and sun, rain, cement and sand, and is easily damaged, resulting in a short service life of the lawn

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing method of weather-proof improved artificial turf backing fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of processing method of weather-resistant improved artificial turf base cloth of this embodiment, flow process is as follows figure 1 shown, including the following steps:

[0026] Step 1, preparation of upper layer weft: mix PP fiber and silicone resin in a weight ratio of 1:3, and then add bisphenol-A-glycidyl dimethacrylate with 20% of the total amount of silicone resin, and continue to use 200r The rotation speed of / min is stirred for 30min, and the stirring is completed, and then extruded in a twin-screw extruder, and the extruded upper layer weft base material is drawn to obtain the upper layer weft;

[0027] Step 2, preparation of the lower layer of weft: the PP fiber is first treated in a plasma box, then mixed with a waterproofing agent at a weight ratio of 1:3, and then lignocellulose is added, and then steam explosion treatment is performed in a steam explosion machine, and the pressure is released The pressure is 2MPa; the treated lower weft thread ...

Embodiment 2

[0036] A processing method of a weather-resistant improved artificial turf base cloth of the present embodiment comprises the following steps:

[0037] Step 1, preparation of upper layer weft: mix PP fiber and silicone resin in a weight ratio of 1:3, then add bisphenol-A-glycidyl dimethacrylate with 30% of the total amount of silicone resin, and continue to 300r The rotation speed of / min is stirred for 40min, and the stirring is completed, and then extruded in a twin-screw extruder, and the extruded upper layer weft base material is drawn to obtain the upper layer weft;

[0038] Step 2, preparation of the lower layer of weft: the PP fiber is first treated in a plasma box, then mixed with a waterproofing agent at a weight ratio of 1:3, and then lignocellulose is added, and then steam explosion treatment is performed in a steam explosion machine, and the pressure is released The pressure is 5MPa, and the treated lower weft thread substrate is drawn to obtain the lower weft thre...

Embodiment 3

[0047] A processing method of a weather-resistant improved artificial turf base cloth of the present embodiment comprises the following steps:

[0048] Step 1, preparation of upper layer weft: mix PP fiber and silicone resin in a weight ratio of 1:3, then add bisphenol-A-glycidyl dimethacrylate with 25% of the total amount of silicone resin, and continue to use 250r The rotation speed of / min is stirred for 35min, and the stirring is completed, and then extruded in a twin-screw extruder, and the extruded upper layer weft base material is drawn to obtain the upper layer weft;

[0049] Step 2, preparation of the lower layer of weft: the PP fiber is first treated in a plasma box, then mixed with a waterproofing agent at a weight ratio of 1:3, and then lignocellulose is added, and then steam explosion treatment is performed in a steam explosion machine, and the pressure is released The pressure is 3.5MPa, and the treated lower weft thread substrate is drawn to obtain the lower wef...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing method of weather-resistant improved artificial turf backing fabric. The method comprises four parts, namely, upper-layer weft preparation, lower-layer weft preparation, backing fabric weaving and backing fabric modification treatment. The finished turf backing fabric is formed by interweaving and fixing the upper-layer wefts and the lower-layer wefts through alayer of warps, the upper-layer wefts have good sun-shading and weather-proof performance, and the lower-layer wefts have high waterproof performance, so that the prepared turf backing fabric is highin comprehensive performance, the weather resistance is obviously improved, and the service life of the turf backing fabric can be prolonged to a great extent.

Description

technical field [0001] The invention relates to the technical field of turf base fabric production, in particular to a processing method of a weather-resistant improved artificial turf base fabric. Background technique [0002] China is a big country with plastic pollution and is facing serious plastic pollution problems. Therefore, our country attaches great importance to the recycling and reuse of plastic materials. The plastic weaving industry is currently a very important plastic reprocessing industry in my country. Through plastic weaving, the recycled polymer plastics The material is processed into carpets, lawns, mats, clothing, etc., and the plastic can be reused. [0003] The existing lawn base cloth is woven from PP material after wire drawing, but the lawn base cloth is exposed to the open air, exposed to wind, sun, rain, cement and sand, and is easily damaged, resulting in a short service life of the lawn. Contents of the invention [0004] Purpose of the inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E01C13/08D03D11/00D03D15/00D06B3/10D06M10/10D06M11/79D06M13/224D06M13/41D06M15/256D06M15/263D06M15/564D06M15/643D06M23/00D03D15/292D03D15/50D03D15/527
CPCE01C13/08D03D11/00D03D15/00D06B3/10D06M15/256D06M15/263D06M11/79D06M13/41D06M13/224D06M15/564D06M23/00D06M15/643D06M13/2243D06M10/10D10B2321/022D06M2101/20D06M2200/12D06M2200/25
Inventor 朱习兰钱长海茅建新魏春李超陈户霞陈杏华吴立红刘陈王广荣王明军