Gypsum-based self-leveling mortar and preparation method thereof

A self-leveling mortar and gypsum-based technology, applied in the field of building materials, can solve the problem of increasing industrial solid waste

Inactive Publication Date: 2020-08-07
张延年
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, industrial solid waste has also increased significantly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) Add 47.6% of phosphorus building gypsum, 10% of aluminate cement, 15% of fly ash, 25% of iron tailings, 0.04% of commercially available polyacrylate superabsorbent resin, 0.29% of F15G water reducer, 2% three-dimensional redispersible latex powder, and 0.06% hydroxypropyl methylcellulose ether are mixed in proportion to obtain a powder mixture;

[0040] (2) Measure the incoming water in proportion and pour it into the mixer, pour (1) the mixed powder mixture into the mixer at a constant speed, mix at a low speed, and the mixing time is 20 minutes;

[0041] (3) After stopping the stirring in (2), use a scraper and scrape off the uneven mixture on the wall of the pot, then add 0.01% P841 defoamer, stir at a high speed, stop, and then stir at a high speed to obtain a gypsum base self-leveling mortar;

[0042] (4) After the gypsum-based self-leveling mortar is flattened and dried, paint 100g / m on the surface 2 hardener.

[0043] The phosphorus building gypsum is β-he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a gypsum-based self-leveling mortar and a preparation method thereof, and belongs to the technical field of building materials, wherein the gypsum-based self-leveling mortar comprises the following components: 40%-50% of phosphorus building gypsum, 5%-15% of aluminate cement, 10%-20% of fly ash, 15%-30% of iron tailing sand, 0.03%-0.05% of a super absorbent resin, 0.2%-0.5%of a water reducing agent, 0.2%-0.5% of redispersible latex powder, 0.05%-0.15% of cellulose ether, and 0.005% to 0.01% of a defoaming agent. The iron tailing sand is used for replacing non-renewableriver sand, coal ash is used for replacing part of cement, and the problems that solid waste is accumulated, utilization of the solid waste is improved, and the environment is affected can be effectively solved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a gypsum-based self-leveling mortar prepared by using phosphorus building gypsum, iron tailings sand and fly ash and a preparation method thereof. Background technique [0002] With the rise of the construction industry in the world, a lot of research on building materials has been produced. At the same time, industrial solid waste has also increased significantly. With the increasing accumulation of industrial solid waste and the use of less and less non-renewable resources in construction, the demand for industrial solid waste to be used in building materials is also increasing. [0003] The main sources of industrial solid waste in daily production and life are: coal gangue produced by the coal industry; blast furnace slag, steel slag and red mud produced by the metallurgical industry; fly ash and slag produced by fuel power plants and urban central hea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14
CPCC04B28/147C04B7/32C04B18/08C04B18/12C04B24/2641C04B2103/302C04B2103/0057C04B24/383C04B2103/50
Inventor 张延年崔长青顾晓薇海洪王亭张于于康楠王铁源闫明程于洋李志军陈志燕杜松岩董宁李琦琦陈昊刘柏男张文洁
Owner 张延年
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products