HTEE series high-temperature infrared radiation coating and use method thereof

A technology of high-temperature infrared and radiation coatings, applied in combustion methods, fireproof coatings, coatings, etc., can solve the problems of low energy utilization rate of steam injection boilers, early development of heavy oil in oil fields, and affecting boiler operating efficiency, etc., to reduce heat preservation Effects of layer peeling, heat reduction, and life extension

Active Publication Date: 2020-08-18
新疆锑都节能科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In our country, the development period of heavy oil in oil fields is early, and most domestic steam injection boilers have been in operation for more than 20 years. The insulation layer of steam injection boilers that have been in operation for a long time will fall off, and the tile mouth will be aging and damaged, which will affect the operating efficiency of the boiler.
[0003] The inner wall of the traditional steam injection boiler is made of refractory materials and ceramic fiber materials, while the interior of the steam injection boiler mainly operates through internal radiation heat, the heat radiation rate in the furnace is insufficient, and the energy utilization rate of the steam injection boiler is low; at the same time, the insulation layer on the inner wall of the steam injection boiler falls off The loss of asbestos in insulation may cause diseases such as asbestosis, and long-term use will pose health risks to operators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • HTEE series high-temperature infrared radiation coating and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0047] A kind of HTEE series high-temperature infrared radiation coating, comprises following preparation steps:

[0048] (1) Mix the components according to the following mass percentage: ZrO 20%, activated alumina micropowder 5%, TiO 2 15%, Al(OH) 3 5%, CoO 20% into the stirring device;

[0049] (2) Add the following components by mass percentage: 15% of zirconia liquid slurry, 15% of solvent, and 5% of water are mixed and stirred, and soaked;

[0050] (3) After the soaking time is up, put the material into the mixer to stir, adjust the mixer to 45°C, react for 60 minutes and cool to 25°C;

[0051] (4) The flow line of the sampling liquid in the mixer is uninterrupted when it reaches more than 150mm, stop stirring, and put the material into a 185-400 mesh screen for filtration;

[0052] (5) Measuring after filtering and packing into barrels.

[0053] In the described step (1), ZrO is a nano zirconia powder, and the nano zirconia comprises the following preparation step...

Embodiment example 2

[0063] A kind of HTEE series high-temperature infrared radiation coating, comprises following preparation steps:

[0064] (1) Mix the components according to the following mass percentage: ZrO 17%, activated alumina micropowder 4.5%, TiO 2 17%, Al(OH) 3 4%, CoO 22% into the stirring device;

[0065] (2) Add the following components by mass percentage: 16% of zirconia liquid slurry, 16.5% of solvent, and 3% of water are mixed and stirred, soaked;

[0066] (3) After the soaking time is up, put the material into the mixer to stir, adjust the mixer to 48°C, react for 70 minutes and cool to 25°C;

[0067] (4) The flow line of the sampling liquid in the mixer is uninterrupted when it reaches more than 150mm, stop stirring, and put the material into a 185-400 mesh screen for filtration;

[0068] (5) Measuring after filtering and packing into barrels.

[0069] In the described step (1), ZrO is a nano zirconia powder, and the nano zirconia comprises the following preparation steps:...

Embodiment example 3

[0079] A kind of HTEE series high-temperature infrared radiation coating, comprises following preparation steps:

[0080] (1) Mix the components according to the following mass percentage: ZrO 25%, activated alumina micropowder 4.5%, TiO 2 12%, Al(OH) 3 4%, CoO 16% into the stirring device;

[0081] (2) Add the following components by mass percentage: 13% of zirconia liquid slurry, 18.5% of solvent, and 7% of water are mixed and stirred, soaked;

[0082] (3) After the soaking time is up, put the material into the mixer to stir, adjust the mixer to 45°C, react for 60 minutes and cool to 25°C;

[0083] (4) The flow line of the sampling liquid in the mixer is uninterrupted when it reaches more than 150mm, stop stirring, and put the material into a 185-400 mesh screen for filtration;

[0084] (5) Measuring after filtering and packing into barrels.

[0085] In the described step (1), ZrO is a nano zirconia powder, and the nano zirconia comprises the following preparation steps:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an HTEE series high-temperature infrared radiation coating and a use method thereof. The HTEE series high-temperature infrared radiation coating comprises the following components: ZrO, activated alumina micro-powder, TiO2, Al(OH)3, CoO, zirconia liquid slurry, a solvent and water, and the obtained mixture is stirred, mixed and filtered to obtain the high-temperature infrared radiation coating for a gas injection boiler. A coating is formed by spraying the high-temperature infrared radiation coating on the surface of an inner lining of a lining hearth of the gas injection boiler; the radiance (epsilon) in the gas injection boiler is improved, thus a heated object in the boiler is uniformly heated, the heating time is effectively reduced; the heat conductivity coefficient of the coating is lower than that of a heat preservation layer; after heat insulation of the coating, the temperature outside the boiler is reduced, the outward dissipated heat of the boiler body is reduced, the replacement frequency of heat preservation asbestos is effectively reduced, the falling of the heat preservation layer is reduced, and the service life of the boiler lining is prolonged.

Description

technical field [0001] The invention relates to the technical field of high-temperature infrared radiation coatings, in particular to an HTEE series high-temperature infrared radiation coating and its application method. Background technique [0002] In my country, heavy oil in oil fields has been developed for a long time, and most domestic steam injection boilers have been in operation for more than 20 years. The insulation layer of steam injection boilers that have been operating all year round will fall off, and the tiles will be aging and damaged, which will affect the operating efficiency of the boiler. [0003] The inner wall of the traditional steam injection boiler is made of refractory materials and ceramic fiber materials, while the interior of the steam injection boiler mainly operates through internal radiation heat, the heat radiation rate in the furnace is insufficient, and the energy utilization rate of the steam injection boiler is low; at the same time, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D7/61C04B35/49C04B35/01C04B35/622F23M5/00
CPCC04B35/01C04B35/49C04B35/62222C04B2235/3217C04B2235/3218C04B2235/3275C04B2235/3427C04B2235/6562C04B2235/6567C04B2235/96C09D1/00C09D5/18C09D7/61F23M5/00F23M2900/05004
Inventor 曾金凤曾理想
Owner 新疆锑都节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com