Stainless steel heating plate and preparation method thereof

A technology of stainless steel and heating sheet, applied in the field of stainless steel heating sheet and its preparation, can solve the problems of strength and tensile capacity degradation, uneven heating, high power consumption, etc., to improve material uniformity, prolong service life, and delay occurrence degenerate effect

Pending Publication Date: 2020-10-02
HUANYA TIANJIN ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Among them, stainless steel sheets are used in many heating fields including floor heating (such as product heating, pipeline heat tracing, road snow melting, building ice melting, etc.). However, the existing stainless steel sheets have uneven heating, heating Slow and high power consumption, and after long-term use, its own strength and tensile capacity will also degrade. Therefore, the existing technology still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A stainless steel heating plate, including by weight percentage: carbon C: 0.01%, silicon Si: 1.00%, manganese Mn: 1.00%, phosphorus P: 0.05%, sulfur S: 0.005%; nickel Ni: 0.01%; chromium Cr : 19.5%, nitrogen N: 0.01%, aluminum Al: 4.80%, the balance is iron Fe and unavoidable impurities.

[0025] Pour the 20Cr-5Al steel and the metal solution of silicon Si, phosphorus P, manganese Mn, Al, chromium Cr in the above weight percentage into a vacuum induction furnace for refining, pour the metal solution into a steel ingot, and pass the steel ingot through continuous casting, or belt The thin strip billet is prepared by casting; the temperature of the thin strip billet is heated to above 1100°C, and the thin strip billet is rolled into a plate-shaped billet, and then the plate-shaped billet is rolled into a strip-shaped billet with a thickness of 1.5mm; the strip-shaped billet is The billet is put into a continuous annealing furnace, and an inert protective gas is introduce...

Embodiment 2

[0027] The invention provides a stainless steel heating plate, which comprises: carbon C: 0.01%, silicon Si: 1.00%, manganese Mn: 1.00%, phosphorus P: 0.05%, sulfur S: 0.005%; nickel Ni: 0.01% in weight percentage ; Chromium Cr: 20.0%, nitrogen N: 0.01%, aluminum Al: 5.0%, and the balance is iron Fe and unavoidable impurities.

[0028] Pour the 20Cr-5Al steel and the above-mentioned silicon Si, phosphorus P, manganese Mn, aluminum Al, chromium Cr metal solution into a vacuum induction furnace for refining, pour the metal solution into a steel ingot, and pass the steel ingot through continuous casting, or The strip casting is prepared into a thin strip billet; the temperature of the thin strip billet is heated to above 1100°C, and the thin strip billet is rolled into a plate-shaped billet, and then the plate-shaped billet is rolled into a strip-shaped billet with a thickness of 1.5mm; the strip Put the strip-shaped billet into the continuous annealing furnace, pass inert protec...

Embodiment 3

[0030] The invention provides a stainless steel heating plate, which comprises: carbon C: 0.01%, silicon Si: 1.00%, manganese Mn: 1.00%, phosphorus P: 0.05%, sulfur S: 0.005%; nickel Ni: 0.01% in weight percentage ; Chromium Cr: 20.5%, nitrogen N: 0.01%, aluminum Al: 5.20%, the balance is iron Fe and unavoidable impurities.

[0031] Pour the 20Cr-5Al steel and the above-mentioned silicon Si, phosphorus P, manganese Mn, aluminum Al, chromium Cr metal solution into a vacuum induction furnace for refining, pour the metal solution into a steel ingot, and pass the steel ingot through continuous casting, or The strip casting is prepared into a thin strip billet; the temperature of the thin strip billet is heated to above 1100°C, and the thin strip billet is rolled into a plate-shaped billet, and then the plate-shaped billet is rolled into a strip-shaped billet with a thickness of 1.5mm; the strip Put the strip-shaped billet into the continuous annealing furnace, pass inert protectiv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a stainless steel heating plate and a preparation method thereof. The stainless steel heating plate comprises, by weight: C of not more than 0.01%, Si of not more than 1.00%, Mnof not more than 1.00%, Mn of not more than 1.00%, P of not more than 0.05%, S of not more than 0.005%, Ni of not more than 0.01%, Cr of not more than 20.5%, N of not more than 0.01%, Al of 4.80%-5.20%, and the balance being Fe and inevitable sundries. According to the invention, through improvement of a formula and a technology and through limiting of weight percentages of Al and Cr in total rawmaterials, material uniformity, electric conductivity and ductility of a stainless steel sheet are improved effectively; through a finish rolling method, the heating plate can be processed to the thickness of 30 mu m, and processing accuracy is ensured, so that the problems that an existing stainless steel sheet is uneven in heating, slow in heating and high in power consumption are solved; and through limiting of material proportions, the service life of the stainless steel heating plat is greatly prolonged, and degradation courses of own strength and tension resistance are delayed

Description

technical field [0001] The invention relates to the technical field of stainless steel heating sheets, in particular to a stainless steel heating sheet and a preparation method thereof. Background technique [0002] Stainless steel is the abbreviation of stainless acid-resistant steel, and the steel grades that are resistant to weak corrosive media such as air, steam, water, or have stainless properties are called stainless steel; The steel type is called acid-resistant steel. [0003] Due to the difference in chemical composition of the two, their corrosion resistance is different. Ordinary stainless steel is generally not resistant to chemical medium corrosion, while acid-resistant steel is generally stainless. The term "stainless steel" does not simply refer to one kind of stainless steel, but refers to more than one hundred kinds of industrial stainless steels, and each developed stainless steel has good performance in its specific application field. The key to success...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/40C21D8/02C22C33/04
CPCC22C38/02C22C38/04C22C38/06C22C38/40C22C38/001C22C33/04C21D8/0205C21D8/0226C21D8/0236C21D8/0247
Inventor 闫陶军刘昊辰
Owner HUANYA TIANJIN ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com