A kind of nizncu nanocomposite dehydrogenation catalyst and preparation method thereof

A dehydrogenation catalyst and nano-composite technology, applied in the direction of catalyst activation/preparation, catalyst protection, chemical instruments and methods, etc., can solve the problems of no catalytic activity, limited contribution, etc., to improve electron distribution, enhance interaction force, The effect of enhancing catalytic stability

Active Publication Date: 2022-03-08
SOUTHEAST UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current patents such as Chinese patent CN111111718A mainly focus on binary LDH, and studies have shown that ternary LDH doped with other metal substances may provide higher catalytic activity, and LDH is often used as a catalyst carrier, which itself does not have catalytic activity. Greatly limit its contribution in the field of catalysis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nizncu nanocomposite dehydrogenation catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] At room temperature, 0.23g ZnCl 2 , 0.23gCuCl 2 ·6H 2 O, 0.80gNiCl 2 ·6H 2 O, 0.32g of urea and 80g of deionized water were added to the reaction kettle, stirred for 0.5h, heated to 110°C for hydrothermal reaction for 12h, cooled to room temperature, filtered, washed with 150g of deionized water for 3 times, and vacuum-dried at 60°C 6h, obtain NiZnCu layered hydroxide;

[0036] Weigh 1.00g of the above-prepared NiZnCu layered hydroxide, 31.08g of trishydroxymethylaminomethane, 1.00g of dopamine, 260g of deionized water, and 12g of concentrated hydrochloric acid with a concentration of 37% into the reaction kettle and mix evenly. React for 12 hours, filter after cooling down to room temperature, wash the filter cake with 200g of deionized water three times, and vacuum dry at 60°C for 12 hours to obtain NiZnCu layered hydroxide / polydopamine;

[0037] Add 0.14g of graphene oxide, 1.00g of NiZnCu layered hydroxide / polydopamine, and 80g of deionized water into the react...

Embodiment 2

[0041] At room temperature, 1.72g ZnCl 2 , 1.72g CuCl 2 ·6H 2 O, 8.60gNiCl 2 ·6H 2 O, 3.44g of urea and 860g of deionized water were added to the reaction kettle, stirred for 0.5h, heated to 120°C for hydrothermal reaction for 12h, cooled to room temperature and filtered, washed with 800g of deionized water for 4 times, vacuumed at 70°C Dry for 8h to obtain NiZnCu layered hydroxide;

[0042] Weigh 3.20g of the above-prepared NiZnCu layered hydroxide, 96.40g of tris, 4.00g of dopamine, 1200g of deionized water, and 60g of concentrated hydrochloric acid with a concentration of 37% into the reaction kettle and mix evenly. React for 14 hours, filter after cooling down to room temperature, wash the filter cake with 600g deionized water 4 times, and vacuum dry at 60°C for 12 hours to obtain NiZnCu layered hydroxide / polydopamine;

[0043] Add 0.25g of graphene oxide, 2.00g of NiZnCu layered hydroxide / polydopamine, and 200g of deionized water into the reaction kettle for mixing, ...

Embodiment 3

[0047] At room temperature, 0.65gZn(NO 3 ) 2 ·6H 2 O, 0.65gCu(NO 3 ) 2 ·3H 2 O, 3.00g Ni(NO 3 ) 2 ·6H 2 O, add 1.50g urea and 320g deionized water into the reaction kettle, stir for 1h, heat up to 130°C for hydrothermal reaction for 20h, cool down to room temperature, filter, wash the filter cake with 300g deionized water for 3 times, and vacuum dry at 60°C for 8h , to obtain NiZnCu layered hydroxide;

[0048] Weigh 2.00g of the above-prepared NiZnCu layered hydroxide, 81.20g of tris, 3.50g of dopamine, 800g of deionized water, and 35g of concentrated hydrochloric acid with a concentration of 37% into the reaction kettle and mix evenly. React for 16 hours, filter after cooling down to room temperature, wash the filter cake with 350g deionized water 4 times, and vacuum dry at 60°C for 10 hours to obtain NiZnCu layered hydroxide / polydopamine;

[0049] Add 0.25g of graphene oxide, 2.00g of NiZnCu layered hydroxide / polydopamine, and 170g of deionized water into the reacti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a NiZnCu nanocomposite dehydrogenation catalyst. The catalyst first synthesizes a NiZnCu layered hydroxide, and then adds dopamine to obtain NiZnCu through self-polymerization reaction of dopamine on the surface of the NiZnCu layered hydroxide under alkaline conditions. Layered hydroxide / polydopamine, then adding graphene oxide through hydrothermal reaction to obtain NiZnCu layered hydroxide / polydopamine / graphene oxide, and finally roasting at 400-600°C in a nitrogen atmosphere to obtain NiZnCu nanocomposite Dehydrogenation catalyst, the catalyst is a nanocomposite of NiZnCu nitrogen-carbon core-shell nanospheres and redox graphene. The core of NiZnCu nitrogen-carbon core-shell nanospheres is NiZnCu alloy nanospheres, and the core is 10-100nm in diameter. It is a nitrogen-carbon nanometer material with a shell thickness of 20-50nm. The catalyst can be applied to the catalytic dehydrogenation of pyridine to synthesize 2,2'-bipyridine, and can obtain a high yield of 2,2'-bipyridine with a relatively small amount of catalyst, and has good industrial application prospects.

Description

technical field [0001] The invention relates to a NiZnCu nanocomposite dehydrogenation catalyst and a preparation method thereof, belonging to the catalyst preparation technology in the technical field of catalysis. Background technique [0002] 2,2'-Bipyridine is an important intermediate in modern chemical production, and has been widely used in the fields of redox indicators, photosensitizers, supercritical carbon dioxide extraction, electroless copper plating, etc. Among them, as the herbicide diquat The demand for main raw material intermediates is huge. Therefore, the development of efficient 2,2'-bipyridine production technology is the key to reducing the production cost of diquat, and direct dehydrocoupling of pyridine is the greenest and safest production route for the synthesis of 2,2'-bipyridine. Therefore, it is of great economic value and market prospect to develop a catalyst with high yield, low cost, low pollution and no risk of operation to catalyze the dire...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/80B01J27/24B01J33/00B01J35/00B01J37/08B01J37/10B01J37/16C07D213/127C07D213/22
CPCB01J23/80B01J27/24B01J33/00B01J37/082B01J37/10B01J37/16C07D213/22C07D213/127B01J35/393
Inventor 周钰明汪嘉祺鲍杰华张一卫卜小海张泽武刘文奇王泳娟
Owner SOUTHEAST UNIV