Aluminum silicon carbide material and preparation method thereof
A technology of aluminum silicon carbide and silicon carbide, which is applied in the field of aluminum silicon carbide materials and its preparation, can solve the problems of low thermal conductivity of aluminum silicon carbide materials, low strength of silicon carbide prefabricated parts, and difficulty in meeting electronic packaging, so as to improve the strength , Reduce the formation of silica, improve the effect of thermal conductivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] The present invention also provides a preparation method of aluminum silicon carbide material, the preparation method comprises the following steps:
[0022] S1, the silicon carbide particles of 100 parts by weight, the metal nitrates of 1-10 parts by weight and the binder of 1-10 parts by weight are mixed to obtain a mixture;
[0023] S2, carrying out drying and molding treatment to the mixture to obtain a green body;
[0024] S3, sintering the green body to obtain a silicon carbide preform;
[0025] S4, performing aluminizing treatment on the silicon carbide preform to obtain an aluminum silicon carbide material.
[0026] In the present invention, preferably, the silicon carbide particles in the step S1 include coarse silicon carbide particles and fine silicon carbide particles; the D50 of the coarse silicon carbide particles is 90-150 μm, and the D50 of the fine silicon carbide particles is 10-20μm. Preferably, the coarse silicon carbide particles and the fine sil...
Example Embodiment
[0034] Example 1
[0035] The preparation method of the aluminum silicon carbide material of the present embodiment is:
[0036] (1) Mix 100 parts by weight of coarse silicon carbide particles (D50=146 μm) and fine silicon carbide particles (D50=16 μm) in a weight ratio of 2:1, then add 1 weight part of aluminum nitrate aqueous solution and 2 The phenolic resin ethanol solution in parts by weight is continuously mixed to obtain a mixture.
[0037] (2) Dry the mixture at 80°C for 1 hour, and after cooling to room temperature, pass it through a granulator through an 80-mesh sieve to obtain granules, wherein the humidity is controlled at 2%.
[0038] (3) Fill the pellets into a steel mold, and shape under a pressure of 18 MPa, and the molding time is 30 s to obtain a green body.
[0039](4) The green body is cured at 200°C for 4h.
[0040] (5) Sinter the solidified green body at 1200° C. for 2 hours to obtain a silicon carbide preform S01.
[0041] (6) Put the silicon carbide...
Example Embodiment
[0042] Example 2
[0043] The preparation method of the aluminum silicon carbide material in this example is the same as that in Example 1, except that 5 parts by weight of aluminum nitrate aqueous solution and 3 parts by weight of phenolic resin ethanol solution are added in step (1). The aluminum silicon carbide material S2 is also obtained.
PUM
Property | Measurement | Unit |
---|---|---|
D50 | aaaaa | aaaaa |
D50 | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap