Compound for positive electrode

A compound, positive electrode technology, applied in the field of positive electrode compounds

Active Publication Date: 2020-10-30
TANAKA CHEM
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, phosphorus element has room for improvement in terms of improving the performance of the storage battery, especially the utilization rate and conductivity in the initial characteristics after storage at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound for positive electrode
  • Compound for positive electrode
  • Compound for positive electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0072] Next, examples of the present invention will be described, but the present invention is not limited to the above examples unless the gist of the present invention is exceeded.

[0073] The manufacture method of the positive electrode compound of Examples 1-2

[0074] Preparation of Nickel Composite Hydroxide Particles

[0075] In a reaction tank equipped with a stirrer, ammonium sulfate aqueous solution and hydroxide The sodium aqueous solution is stirred at 520rpm by a propeller-type stirrer with a stirring blade of 250mm while maintaining the reaction temperature at 45.0°C and the reaction pH at 40°C as a liquid temperature reference of 12.1 in a reaction tank with a reaction volume of 500L. Stirring is performed continuously at rotational speed. The generated hydroxide was taken out by overflowing the overflow pipe of the reaction tank. Each treatment of washing with water, dehydration, and drying was performed on the hydroxide taken out, thereby obtaining nickel ...

Embodiment 3

[0123] The manufacture method of the positive electrode compound of embodiment 3

[0124] The nickel composite hydroxide particle of comparative example 7 prepared in the above manner is further directly implemented electroless pure nickel plating treatment, thus manufactures embodiment 3, has nickel-plated film as the nickel composite hydroxide (with Nickel-plated film as the coating layer of nickel-cobalt-manganese composite hydroxide), that is, nickel-coated nickel composite hydroxide. More specifically, nickel composite hydroxide having a nickel-plated film was produced as follows.

[0125] First, nickel composite hydroxide particles having a particle diameter of 10 μm were used as substrate particles, and the substrate particles were stirred for 10 minutes with a cationic surfactant in order to modify the surface of the substrate particles. Then, after filtering and washing with water, stirring treatment was carried out in the palladium ion catalyst solution for 10 minut...

Embodiment 4

[0126] The manufacture method of the positive electrode compound of embodiment 4

[0127] Weigh the dry powder and lithium carbonate powder containing the nickel-coated nickel composite hydroxide of Example 3 obtained in the above manner, and they are mixed so that Li / (Ni+Co+Mn)=1.03, then, The primary firing was carried out at a temperature of 740° C. for 8.4 hours in an air atmosphere to obtain a lithium-nickel-containing coated nickel composite oxide as a primary firing powder. Thereafter, the primary fired powder was pulverized, and secondary firing was performed at a temperature of 940° C. for 8.4 hours in an air atmosphere. As a secondary firing powder, the lithium-nickel-containing coated nickel composite oxide of Example 4 was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The purpose of the present invention is to provide a highly electroconductive compound for a positive electrode, the compound exhibiting an excellent utilization rate after a high temperature standingand an excellent initial characteristic utilization rate. This compound for a positive electrode has: a core which is secondary particles resulting from aggregation of primary particles and which contains a nickel composite hydroxide; and a coating layer disposed on the surface of the core, containing elemental nickel, 500 ppm or less of elemental cobalt and 10 ppm or less of elemental phosphorus. The elemental nickel content in the coating layer is 6-20 parts by mass with respect to 100 parts by mass of the core, and the volume resistivity of the compound is 1.5 x 10 [omega].cm or less.

Description

technical field [0001] The present invention relates to a compound for a positive electrode of a storage battery, and particularly relates to a compound for a positive electrode having high conductivity and excellent utilization rate after being left at a high temperature. Background technique [0002] In order to improve the performance of the compound for the positive electrode of the storage battery, a coating layer containing a metal element may be formed on the surface of the metal hydroxide as a core. For example, surface-modified nickel hydroxide in which the surface of nickel hydroxide as a core is coated with cobalt oxide has been proposed as a positive electrode active material for alkaline storage batteries with high positive electrode utilization and improved cycle characteristics (Patent Document 1). [0003] However, in Patent Document 1, the positive electrode active material whose surface is coated with cobalt oxide on the surface of nickel hydroxide can obta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/52C01G53/00H01M4/50H01M4/505H01M4/525
CPCH01M4/505H01M4/525H01M4/50H01M4/52C01G53/00Y02E60/10H01M4/366C01G53/006C01G53/42H01M10/345H01M10/052H01M2300/0014H01M2300/0025
Inventor 田中聪花村直也畑未来夫
Owner TANAKA CHEM