Environment-friendly rock wool heat-insulation board production process

A production process and thermal insulation board technology, which is applied in the field of thermal insulation materials, can solve the problems of high production temperature of energy-saving thermal insulation materials, high uniformity of mixed raw materials, and reduction of slag formation, so as to reduce production requirements, reasonable proportioning, and improve water repellency rate effect

Active Publication Date: 2020-11-06
安徽瑞联节能科技股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the above-mentioned technical problems, the object of the present invention is to provide a production process of environmentally friendly rock wool insulation board: preheating after mixing and crushing basalt, white rock, slag, and coke, and then maintaining the temperature in the cupola, Liquid oxygen is added when the raw material is melted and burned, so that the production does not require too high a heating temperature, and the ratio is reasonable to ensure that the various components are fused with each other after combustion, and the obtained molten raw material liquid has a uniform composition. After being centrifuged into fibers, it becomes fibrous, and the phenolic resin is sprayed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly rock wool heat-insulation board production process
  • Environment-friendly rock wool heat-insulation board production process
  • Environment-friendly rock wool heat-insulation board production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] see Figure 1-6 As shown, the present embodiment is a production process of an environmentally friendly rock wool insulation board, comprising the following steps:

[0035] Step 1, raw material crushing: mix basalt, white rock, slag and coke, put the mixture of basalt, white rock, slag and coke into the feed box 103 from the feeding port 104 of the raw material crushing equipment, and drop it into the crushing bin 102 In the inner cavity, the rotating crushing roller 117 cuts and crushes the basalt, white rock, slag, and coke mixture through several crushing blades 120 to form a mixture powder, and the mixture powder whose particle size is smaller than the sieving hole diameter passes through the sieving plate 116 Discharge from the bottom end of the hopper 101 to obtain mixed raw materials;

[0036] Step 2, heating up and melting: Preheat the mixed raw materials at a temperature of 500°C for 2 hours, then add the mixed raw materials into the cupola after preheating, k...

Embodiment 2

[0046] see Figure 1-6 As shown, the present embodiment is a production process of an environmentally friendly rock wool insulation board, comprising the following steps:

[0047] Step 1, raw material crushing: mix basalt, white rock, slag and coke, put the mixture of basalt, white rock, slag and coke into the feed box 103 from the feeding port 104 of the raw material crushing equipment, and drop it into the crushing bin 102 In the inner cavity, the rotating crushing roller 117 cuts and crushes the basalt, white rock, slag, and coke mixture through several crushing blades 120 to form a mixture powder, and the mixture powder whose particle size is smaller than the sieving hole diameter passes through the sieving plate 116 Discharge from the bottom end of the hopper 101 to obtain mixed raw materials;

[0048] Step 2, heating up and melting: Preheat the mixed raw materials at 500°C for 2 hours, add the mixed raw materials into the cupola after preheating, keep the temperature in...

Embodiment 3

[0058] see Figure 1-6 As shown, the raw material crushing equipment in this embodiment includes a receiving hopper 101, a crushing bin 102, a feed box 103, a first support frame 107, a second support frame 109, a screening plate 116, and a crushing roller 117. A hopper 101 is installed on a support frame 107, a crushing bin 102 is installed on the top of the hopper 101, and a feeding box 103 is installed on the top of the crushing bin 102; Port 104, crushing rollers 117 are arranged in the inner cavity of the crushing bin 102, and a screening plate 116 is installed on the top of the inner cavity of the receiving hopper 101, and several screening holes are opened on the screening plate 116, and the crushing The roller 117 is located in the inner cavity of the screening plate 116, and the two ends of the crushing roller 117 are sleeved with bearing seats 105, and the two bearing seats 105 are installed on the two mounting frames 106 respectively, and the two mounting frames 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Fiber average diameteraaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly rock wool heat-insulation board production process. According to the invention, raw materials are mixed, crushed and preheated, the temperature in a cupola furnace is kept, and liquid oxygen is added when the raw materials are melted and combusted, so that too high heating temperature is not needed during production, the production requirement is reduced, energy is saved, the proportion is reasonable, and it is ensured that the obtained melted raw material liquid is uniform in component; the melted raw material liquid becomes fibrous through centrifugal fiber forming, and a phenolic resin is sprayed in the centrifugal process, so that the generation of slag balls can be greatly reduced; according to the production process, raw materials are crushed through raw material crushing equipment, a mixture is cut and crushed through a crushing roller rotating at high speed, and powder with small particle size is screened out through a screening plate and discharged, so that the obtained mixed raw material is high in uniformity and good in mixing effect, the difficulty of subsequent heating melting and material fibration processes is reduced,the production temperature of the environment-friendly rock wool heat-insulation board is further easily achieved, and the content of slag balls in the environment-friendly rock wool heat-insulation board is reduced.

Description

technical field [0001] The invention relates to the field of thermal insulation materials, in particular to a production process for an environmentally friendly rock wool thermal insulation board. Background technique [0002] The thermal insulation material can collect excess heat and release it in a timely and stable manner, with small gradient changes, which can effectively reduce the loss. The room temperature can be trended and the winter heat preservation can play a balancing role. Patent No. 201010222393.2 discloses a preparation method of rock wool fiber energy-saving thermal insulation material. Bonding agent and anti-dust oil, and then heated and cured to obtain rock wool fiber energy-saving thermal insulation material products. The key to the inventive method is to recycle the carbon monoxide produced by burning coke in the cupola, and then incinerate it with natural gas to generate a large amount of heat and send it into the cupola again, and then add oxygen to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B30/02C04B14/46C03C13/06C03B37/04
CPCC04B30/02C04B14/46C03C13/06C03B37/04C04B2201/20C04B2111/27C04B2201/50
Inventor 范伟王壮文礼冯家玉王永回徐成沈佳佳张应东
Owner 安徽瑞联节能科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products