Cosmetic glass bottle processing method

A processing method and glass bottle technology, applied in glass blowing, glass production, glass molding, etc., can solve the problems that the mechanical impact resistance of glass bottles needs to be further improved, and achieve good melting performance, high temperature resistance and alkali resistance Good, good defoaming effect

Inactive Publication Date: 2020-11-17
广州市泓苼玻璃制品有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although this method reduces the production cost of the glass bottle to a certain extent, the mechanical shock resistance of the glass bottle needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example

[0046] The components and proportions of the glass defoamers in Preparation Examples 1-5 are shown in Table 2 below.

preparation example 1

[0050] A kind of glass defoamer, its preparation method is as follows:

[0051] S1. Weigh simethicone oil and allyl polyether according to the ratio in Table 2 above, stir and mix, then raise the temperature to 65°C until the mixture of the two becomes a transparent liquid, and then mature for 1 hour to obtain Modified silicone oil;

[0052] S2. Weigh op-10 and ethanol according to the ratio in the above table 2, then add modified silicone oil and op-10 to ethanol, stir with a high-shear disperser at a speed of 2000r / min for 30min, you can get Glass defoamer.

preparation example 2

[0054] A kind of glass defoamer, its preparation method is as follows:

[0055] S1. Weigh simethicone oil and allyl polyether according to the ratio in Table 2 above, stir and mix, then raise the temperature to 60°C until the mixture of the two becomes a transparent liquid, and ripen for 1.5h. Obtain modified silicone oil;

[0056] S2. Weigh op-10 and ethanol according to the ratio in the above table 2, then add modified silicone oil and op-10 to ethanol, stir with a high-shear disperser at a speed of 2000r / min for 25min to obtain Glass defoamer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a processing method of a glass bottle for cosmetics, and belongs to the technical field of glass bottle processing. The method comprises the following steps: material preparing: crushing quartz sand and cullet; cleaning: cleaning the cullet with a cleaning solution, then washing with water to remove the cleaning solution attached to the cullet, and then drying the cullet toobtain purified cullet; material mixing: weighing quartz sand, the cullet, limestone, borax and soda ash according to a ratio, and uniformly mixing to obtain a pre-mixture; melting: preparing the pre-mixture into a molten state, uniformly stirring, adding a glass defoamer, and uniformly stirring to obtain molten glass; mold passing: transferring the molten glass into a forming mold to prepare a glass bottle blank; bottle blowing: carrying out bottle blowing on the glass bottle blank to obtain a preformed glass bottle; and molding: cooling the preformed glass bottle to obtain the glass bottlefor cosmetics. According to the invention, the glass bottle has the advantage of environmental protection, and the prepared glass bottle has good mechanical shock resistance.

Description

technical field [0001] The invention relates to the technical field of glass bottle processing, in particular to a method for processing glass bottles for cosmetics. Background technique [0002] With the development of society, people have more and more demand for cosmetics out of the pursuit of beauty. However, since cosmetics are chemical substances, they are easily oxidized if they are directly exposed to the air. Therefore, it is very important to seal the cosmetics. At present, there are two kinds of plastic bottles and glass bottles for packaging cosmetics. [0003] Among them, plastic bottles have low density, light weight, good corrosion resistance and impact resistance, and have high mechanical strength, are easy to shape, and have low production loss. However, the disadvantages of plastic bottles are also more obvious. First of all, the degradation time of plastic bottles is long or cannot be degraded, which is easy to cause white pollution. Secondly, when the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C6/02C03B1/00C03B5/18C03B5/225C03B9/00C03C1/00C03C1/02
CPCC03C1/002C03C1/02C03B1/00C03B5/225C03B5/18C03C1/004C03C1/00C03B9/00Y02P40/50
Inventor 许楚欣
Owner 广州市泓苼玻璃制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com