A water-reducing agent with high cement compatibility

A technology of water reducing agent and compatibility, which is applied in the field of water reducing agent with high compatibility of cement. capacitive, fluidity-enhancing effect

Active Publication Date: 2022-04-22
ZHUZHOU HONGXIN TECH DEV CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, when the mud content of the concrete aggregate is too high, the dispersion performance of the water reducing agent will be greatly reduced or even completely ineffective. Practice has found that simply relying on the improvement or improvement of the preparation process of the water reducing agent cannot completely solve the problems of poor concrete workability and rapid collapse.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A water-reducing agent with high cement compatibility

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A water reducing agent with high compatibility for cement, comprising component A and component B, the component A is mixed from the following raw materials: prenol polyoxyethylene ether, reducing agent, acrylic acid, hydroxyethyl methacrylate Ester, chain transfer agent, polyethylene glycol diacrylate, oxidizing agent and water.

[0021] The preparation method of the component B is:

[0022] (1) The mixed powder of calcium aluminum silicate and calcium sulfate is ball-milled at a ratio of calcium aluminum silicate / calcium sulfate=10:3 by mixed mass ratio, passed through a 1000-mesh sieve, and the sieved powder is collected for subsequent use;

[0023] (2) configure the aqueous solution of sodium borate and sodium phosphate, the mass percentage of each component in the aqueous solution of described sodium borate and sodium phosphate is sodium borate 1%, sodium phosphate 6%, and the rest are water; The powder is heated to 1200~1250℃, kept for 1 hour, then immersed in th...

Embodiment 2

[0030] A water reducing agent with high compatibility for cement, comprising component A and component B, the component A is mixed from the following raw materials: prenol polyoxyethylene ether, reducing agent, acrylic acid, hydroxyethyl methacrylate Ester, chain transfer agent, polyethylene glycol diacrylate, oxidizing agent and water.

[0031] The preparation method of the component B is:

[0032] (1) The mixed powder of calcium aluminum silicate and calcium sulfate is ball-milled at a ratio of calcium aluminum silicate / calcium sulfate=10:5 by mixed mass, passed through a 1000-mesh sieve, and the sieved powder is collected for subsequent use;

[0033] (2) configure the aqueous solution of sodium borate, sodium phosphate, the mass percentage of each component in the aqueous solution of described sodium borate, sodium phosphate is sodium borate 2%, sodium phosphate 8%, and the rest are water; The powder is heated to 1200~1250℃, kept for 1 hour, then immersed in the aqueous so...

Embodiment 3

[0040] A water reducing agent with high compatibility for cement, comprising component A and component B, the component A is mixed from the following raw materials: prenol polyoxyethylene ether, reducing agent, acrylic acid, hydroxyethyl methacrylate Ester, chain transfer agent, polyethylene glycol diacrylate, oxidizing agent and water.

[0041] The preparation method of the component B is:

[0042] (1) Ball-milling the mixed powder of calcium aluminum silicate and calcium sulfate according to the ratio of the mixed mass ratio of calcium aluminum silicate / calcium sulfate=10:6, passing through a 1000-mesh sieve, and collecting the sieved powder for later use;

[0043] (2) configure the aqueous solution of sodium borate and sodium phosphate, the mass percentage of each component in the aqueous solution of described sodium borate and sodium phosphate is sodium borate 2%, sodium phosphate 10%, and the rest are water; The powder is heated to 1200~1250℃, kept for 2 hours, then imme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water reducing agent with high cement compatibility, which comprises component A and component B, and the raw materials of component A are: isopentenol polyoxyethylene ether, reducing agent, acrylic acid, hydroxyethyl methacrylate, Chain transfer agent, polyethylene glycol diacrylate, oxidizing agent and water; the preparation method of component B is: (1) ball mill the mixed powder of calcium aluminum silicate and calcium sulfate, and sieve; (2) configure sodium borate, phosphoric acid Sodium aqueous solution, heat the sieved powder to 1200-1250°C, keep it warm for 1-2h, then immerse it in the solution and water-cool it to room temperature, take it out after cooling, repeat the heating and keeping warm, soaking process twice; finally solid-phase washing, drying, Obtain solid phase A; (3) configure the aqueous solution of maleic acid and N,N-dimethylformamide in the container, soak solid phase A wherein, heat, keep warm, air-cool, filter, wash, dry, obtain Component B. The invention improves the compatibility between the concrete and the water reducing agent, reduces the hydration speed, improves the fluidity, and has very good use effect.

Description

technical field [0001] The invention belongs to the technical field of concrete admixtures, in particular to a water-reducing agent with high cement compatibility. Background technique [0002] High-performance concrete has excellent characteristics such as high fluidity, high durability and high strength. The addition of high-performance water reducer and mineral admixture is the most important technical way to achieve high performance of concrete. However, the poor compatibility of high-performance water-reducing admixture with cement leads to excessive loss of fluidity and slump of high-performance concrete, which seriously affects the production and application of high-performance concrete. High-performance water reducers have poor compatibility with cement, which is related to the chemical composition and properties of cement. For example, when the mud content of the concrete aggregate is too high, the dispersion performance of the water-reducing agent will be greatly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/32C08F283/06C08F220/06C08F220/20C08F222/14C04B103/30
CPCC04B40/0039C08F283/065C04B2103/302C08F220/06C08F220/20C08F222/1063C04B24/32C04B24/283C04B24/02C04B22/068C04B24/04C04B24/045C04B24/16C04B22/143C04B22/08
Inventor 王伟龙威
Owner ZHUZHOU HONGXIN TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap