Straw wood ceramic root irrigation pipe as well as preparation method and application thereof

A technology for wood ceramics and root irrigation pipes, applied in ceramic products, botanical equipment and methods, applications, etc., can solve the problems of high cost of wood ceramics, achieve the effects of improving strength, increasing porosity, and good environmental coordination

Active Publication Date: 2020-11-24
NORTHWEST A & F UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the deficiencies in the prior art, the purpose of the present invention is to provide a straw wooden ceramic root irrigation pipe and its preparation method and application, which overcomes the difficulty in preparing wooden root irrigation pipes with complex shapes by traditional molding techniques, and other processes The cost of wood ceramics is too high. This method first dissolves phenolic resin in alcohol, then adds straw for ultrasonic impregnation, and after drying, it is ball milled with clay and dextrin at a low speed, then adds silica sol and carbon fiber, and stirs to form a ceramic slurry. Inject into a stainless steel mold, dry and demould to form an underground root irrigation tube blank, and finally sinter under the protection of a static atmosphere to prepare an underground root irrigation tube with a complex shape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Straw wood ceramic root irrigation pipe as well as preparation method and application thereof
  • Straw wood ceramic root irrigation pipe as well as preparation method and application thereof
  • Straw wood ceramic root irrigation pipe as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] A method for preparing a straw wood ceramic root irrigation pipe, comprising the following steps:

[0038] Step 1: According to the formula quantity, add phenolic resin with a particle size of 200 mesh into 90% alcohol to make a solidification solution, put the solidification solution in a sealed beaker, stir at a low speed for 10 minutes to fully dissolve, and prepare a solution;

[0039] Step 2: In order to avoid the interference of impurities such as soil particles on the straw, the straw is washed with water and then dried, and then the straw of the formula is crushed into particles with a particle size of 50 mesh by a pulverizer, and the straw is dipped into the solution obtained in step 1, and dipped into The time is 1h; after the impregnation is completed, place it in a blast drying oven at 65°C to dry to remove alcohol and form a solidified block;

[0040] Step 3, put the solidified block obtained in step 2, the clay and dextrin in the formula amount into a ball...

Embodiment 1

[0048] The present embodiment provides a straw wood ceramic root irrigation pipe, which comprises the following raw materials in terms of mass percentage: 10% phenolic resin, 20% alcohol, 10% straw, 7% clay, 3% dextrin, 48% silica sol and Carbon Fiber 2%. The preparation method of straw wood ceramic root irrigation pipe comprises the following steps:

[0049] Step 1: According to the formula quantity, add phenolic resin with a particle size of 200 mesh into 90% alcohol to make a solidification solution, put the solidification solution in a sealed beaker, stir at a low speed for 10 minutes to fully dissolve, and prepare a solution;

[0050] Step 2: In order to avoid the interference of impurities such as soil particles on the straw, the straw is washed with water and then dried, and then the straw of the formula is crushed into particles with a particle size of 50 mesh by a pulverizer, and the straw is dipped into the solution obtained in step 1, and dipped into The time is 1h...

Embodiment 2

[0056] This embodiment provides a kind of stalk wooden ceramic root irrigation pipe, which comprises the following raw materials in terms of mass percentage: 13% phenolic resin, 19% alcohol, 10% straw, 7% clay, 3% dextrin, 46% silica sol and Carbon Fiber 2%. The preparation method and condition parameters of straw wood ceramic root irrigation pipes are the same as those in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a straw wood ceramic root irrigation pipe and a preparation method and application thereof. The root irrigation pipe is prepared from the following raw materials: phenolic resin, alcohol, straw, clay, dextrin, silica sol and carbon fibers. A blank of a specific structure is prepared through casting molding, and the underground root irrigation pipe is prepared through nitrogen protection sintering. According to the method, underground root irrigation pipes with required shapes can be prepared according to actual requirements, the underground irrigation pipelines can be rapidly connected, and the preparation and installation cost is greatly reduced. Meanwhile, the root irrigation pipe has good environmental coordination, does not need to be recycled after reaching thedesigned service life, and can be directly crushed and returned to the field, so that the recycling cost is saved, and the soil structure can be effectively improved.

Description

technical field [0001] The invention belongs to the field of water-saving irrigation, and in particular relates to a recycling-free and easy-to-connect straw wood-ceramic underground root irrigation pipe and a preparation method and application thereof. Background technique [0002] At present, underground irrigation pipes are generally made of plastic or rubber products, and the recycling problem is more complicated. In order to achieve the purpose of easy recycling or no recycling, it is necessary to use pipeline products with low strength and no pollution to the environment. The patent "A Natural Mineral Modified Wood Ceramic and Its Preparation and Application" (application number: 201810163839.5) discloses a natural mineral modified wood ceramic and its Its preparation method has good adsorption effect, but the pore size range of the material is basically between 0.3-5.2um, and the pore size is too small; at the same time, the flexural strength is generally 8-9MPa, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06C04B35/80C04B35/52C04B35/622C04B35/64B28B21/16B05B1/20A01G25/06
CPCC04B38/0645C04B35/52C04B35/622C04B35/64B28B21/16A01G25/06B05B1/20C04B2235/349C04B2235/5248C04B2235/3418C04B35/806
Inventor 蔡耀辉吴普特张林朱德兰赵西宁葛茂生高晓东丁艳宏周伟聂一品
Owner NORTHWEST A & F UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com