A method for recovering vanadium-aluminum-molybdenum from spent catalyst

A waste catalyst, vanadium-aluminum technology, applied in the field of recycling vanadium-aluminum-molybdenum, can solve the problems of severe dust, long reaction time, high energy consumption, etc., and achieve the effects of strong oxidation, high extraction rate and good diffusion performance

Active Publication Date: 2022-01-11
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In summary, although there have been many studies on the recycling of various elements in spent catalysts, there are problems such as high energy consumption, long reaction time or serious dust, so it is necessary to develop a new method for recycling elements in spent catalysts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] The present embodiment provides a method for recovering vanadium-aluminum-molybdenum from spent catalysts, said method comprising the steps of:

[0059] (1) mix the spent catalyst containing vanadium, aluminum and molybdenum with the sodium hydroxide solution whose mass concentration is 20wt% by liquid-solid ratio 3:1, obtain reaction slurry; Contain vanadium, aluminum and molybdenum in the described spent catalyst; The waste catalyst is a waste hydrodesulfurization (HDS) aluminum-based petroleum catalyst, composed of V 2 o 5 : 10.51wt%, Al 2 o 3 : 22.15wt%, MoO 3 : 2.96wt%, NiO: 2.94wt%;

[0060] (2) The reaction slurry described in step (1) is placed in a reactor, and the reactor is equipped with a conventional down-pressing mechanical stirring paddle and an aerator, wherein the aerator is composed of a motor, a hollow stirring shaft and a hollow impeller;

[0061] The impeller of the aerator is located below the stirring paddle of the reactor, the diameter of th...

Embodiment 2

[0064] The present embodiment provides a method for recovering vanadium-aluminum-molybdenum from spent catalysts, said method comprising the steps of:

[0065] (1) mix the spent catalyst containing vanadium, aluminum and molybdenum with the sodium hydroxide solution whose mass concentration is 25wt% by liquid-solid ratio 4:1, obtain reaction slurry; Contain vanadium, aluminum and molybdenum in the described spent catalyst; The waste catalyst is a waste hydrodesulfurization (HDS) aluminum-based petroleum catalyst, composed of V 2 o 5 : 8.32wt%, Al 2 o 3 : 25.22wt%, MoO 3 : 3.07wt%, NiO: 2.35wt%;

[0066] (2) The reaction slurry described in step (1) is placed in a reactor, and the reactor is equipped with a conventional down-pressing mechanical stirring paddle and an aerator, wherein the aerator is composed of a motor, a hollow stirring shaft and a hollow impeller;

[0067] The impeller of the aerator is located below the stirring paddle of the reactor, the diameter of the...

Embodiment 3

[0070] The present embodiment provides a method for recovering vanadium-aluminum-molybdenum from spent catalysts, said method comprising the steps of:

[0071] (1) mix the spent catalyst containing vanadium, aluminum and molybdenum with the sodium hydroxide solution whose mass concentration is 30wt% according to the liquid-solid ratio of 5:1 to obtain a reaction slurry; the spent catalyst contains vanadium, aluminum and molybdenum; The waste catalyst is a waste hydrodesulfurization (HDS) aluminum-based petroleum catalyst, composed of V 2 o5 : 9.76%, Al 2 o 3 : 20.21%, MoO 3 : 2.32%, NiO: 3.23%;

[0072] (2) The reaction slurry described in step (1) is placed in a reactor, and the reactor is equipped with a conventional down-pressing mechanical stirring paddle and an aerator, wherein the aerator is composed of a motor, a hollow stirring shaft and a hollow impeller;

[0073] The impeller of the aerator is located under the stirring paddle of the reactor, the diameter of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for recovering vanadium, aluminum and molybdenum from waste catalysts. The method strengthens the oxidation leaching of alkali solution by adopting an aeration process, enhances the solubility of oxygen, improves the leaching rate of vanadium, aluminum and molybdenum, and shortens the The reaction time is shortened, thereby reducing the energy consumption of the reaction and the evaporation of the alkali solution; finally, the leaching solution containing vanadium, aluminum and molybdenum and the tailings enriched in other valuable elements can be obtained, realizing the resource utilization of spent catalysts.

Description

technical field [0001] The invention relates to the technical field of solid waste recovery, in particular to a method for recovering vanadium, aluminum and molybdenum from waste catalysts. Background technique [0002] Hydrodesulfurization (HDS) aluminum-based catalysts are widely used in the petroleum hydrodesulfurization process in the petroleum refining industry. During use, due to the deposition of carbon, sulfur, heavy metals and other substances and the loss or denaturation of active factors in the catalyst, the Catalyst deactivation. The service life of catalysts used for hydrodesulfurization of light crude oil is generally 1-3 years, while the service life of heavy oil HDS catalysts is only 0.5-1 year. According to statistics, about 800,000 tons of waste catalysts are produced in the world every year. Among them, there are about 120,000 tons of waste HDS aluminum-based catalysts. The content of valuable metals such as vanadium, molybdenum, cobalt, and nickel in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B7/00C22B21/00C22B34/22C22B34/34
CPCC22B7/006C22B34/225C22B34/345C22B21/003Y02P10/20
Inventor 王少娜杜浩刘彪王健璋吕页清陈东辉
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI