Waterproof isolation plate and preparation method thereof

A technology of isolation board and forming agent, which is applied in the field of building materials, can solve environmental pollution and other problems, and achieve the effect of improving strength, toughness and strength, and increasing density

Inactive Publication Date: 2020-12-22
唐山中陶纪元工程设计有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the partition board in the prior art has many limiting factors in the use process and there is also the problem of environmental pollution in the process of raw material collection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof isolation plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of waterproof isolation board, comprises following raw materials prepared by weight:

[0046] 65 parts of alkali residue,

[0047] 5 parts of aggregate forming agent,

[0048] 8 parts of white ash,

[0049] 3 parts of cellulose;

[0050] The aggregate forming agent comprises the following components by weight:

[0051] 15 parts of alkali residue,

[0052] 35 parts of steel slag,

[0053] 3 parts of waste plaster mold,

[0054] 30 parts of cement clinker.

[0055] The preparation method of above-mentioned waterproof isolation plate, comprises the following steps:

[0056] (1) Take alkali slag, dry at 680°C until the water content is below 8wt%, and grind to obtain alkali slag powder, the particle size of which is below 100 μm;

[0057] (2) Preparation of aggregate forming agent: take alkali slag, steel slag, waste gypsum mold, cement clinker respectively, pulverize, grind, sieve, obtain alkali slag powder, steel slag powder, waste gypsum mold powder and ge...

Embodiment 2

[0061] A kind of waterproof isolation board, comprises following raw materials prepared by weight:

[0062] 75 parts of alkali residue,

[0063] 10 parts of aggregate forming agent,

[0064] 12 parts of white ash,

[0065] 6 parts of cellulose;

[0066] The aggregate forming agent comprises the following components by weight:

[0067] 25 parts of alkali residue,

[0068] 45 parts of steel slag,

[0069] 6 parts of waste plaster mold,

[0070] 35 parts of gelling material,

[0071] 1.5 parts of additives;

[0072] The cementitious material is clinker cement,

[0073] The additives are enhancers.

[0074] The preparation method of above-mentioned waterproof isolation plate, comprises the following steps:

[0075] (1) Take alkali slag, dry at 720°C until the water content is below 8wt%, and grind to obtain alkali slag powder, the particle size of which is below 100 μm;

[0076] (2) Preparation of aggregate forming agent: get alkali slag, steel slag, waste gypsum mold, ...

Embodiment 3

[0080] A kind of waterproof isolation board, comprises following raw materials prepared by weight:

[0081] 70 parts of alkali residue,

[0082] 10 parts of aggregate forming agent,

[0083] 10 parts of white ash,

[0084] 5 parts of cellulose;

[0085] The aggregate forming agent comprises the following components by weight:

[0086] 20 parts of alkali residue,

[0087] 40 parts of steel slag,

[0088] 5 parts of waste plaster mold,

[0089] 34 parts of gelling material,

[0090] Additive 1 part;

[0091] The cementitious material is cement clinker;

[0092] The additive is a grinding aid.

[0093] The preparation method of above-mentioned waterproof isolation plate, comprises the following steps:

[0094] (1) Take alkali slag, dry at 700°C until the water content is below 8wt%, and grind to obtain alkali slag powder, the particle size of which is below 100 μm;

[0095] (2) Preparation of aggregate forming agent: get alkali slag, steel slag, waste gypsum mold, ceme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a waterproof isolation plate. The waterproof isolation plate uses industrial solid waste alkaline residues as a main raw material and achieves the purposes of excellent waterproof performance and high strength through the cooperation of the alkaline residues, an aggregate forming agent, lime and cellulose. The aggregate forming agent provided by the invention has a gelling property, and in the process of hardening, the strength of the alkaline residues is excited, and the strength of the obtained isolation plate is improved; the lime can improve the tensile strength of the alkaline residues and the aggregate forming agent, and can also react with a part of raw aluminum oxide or silicon oxide in the aggregate forming agent to generate substances with hydraulic performance so as to realize cementation, so the strength of the isolation plate is further improved; and the cellulose can improve the toughness and strength of the isolation plate. According to the waterproof isolation plate provided by the invention, through the interaction of all the components, the obtained waterproof isolation plate has good impact resistance, bending resistance, small drying shrinkage rate and good waterproof performance.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a waterproof isolation board and a preparation method thereof. Background technique [0002] Partition wall panels are prefabricated slats for walls used in non-load-bearing parts of buildings. Commonly used partition boards in the prior art include glass fiber reinforced cement strips, glass fiber reinforced lime hollow strips, pressurized aerated concrete strips, steel wire reinforced cement strips, light concrete strips, and composite sandwich lightweight Batten and more. Glass fiber reinforced cement lightweight porous partition wall panels are referred to as GRC lightweight partition wall panels. The hollow slats are made of glass fiber roving and its mesh cloth as reinforcing materials, light inorganic composite materials such as perlite and ceramsite as light aggregates, and external admixtures such as fly ash and slag. It has the characteristics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B22/00C04B18/14C04B111/27
CPCC04B28/142C04B22/0006C04B18/142C04B2111/27C04B2201/50C04B2201/20C04B7/00C04B22/064C04B24/383C04B2103/52C04B2103/0068Y02W30/91
Inventor 许凯军陈勇魏越任晓花王雪王刚
Owner 唐山中陶纪元工程设计有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com