OCA optical adhesive, and preparation method and application of OCA optical adhesive

A technology of optical glue and number of parts, applied in the direction of adhesives, films/sheets without carriers, adhesive types, etc., can solve problems such as pressure increase, uncontrollable polymer conversion rate, uncontrollable production process, etc.

Inactive Publication Date: 2021-01-08
世星科技股份有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most adhesives on the market are thermally polymerized by heating in a reactor. During the production heating process, accompanied by solvent reflux, pressure rise, etc., some of them are produced by UV ultraviolet light polymerization. Yes, but the production process cannot be controlled during the production process, and the polymer conversion rate during the polymerization process cannot be controlled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The preparation method of OCA optical glue, including OCA optical glue, also includes the following steps:

[0021] Step 1: Mixing 2-ethylhexyl acrylate, isobornyl acrylate, 2-hydroxyethyl acrylate, 1-hydroxycyclohexyl benzophenone and dodecanethiol to obtain a monomer prepolymer;

[0022] Step 2: The monomer prepolymer obtained in step 1 is exposed to ultraviolet radiation and added with a photoinitiator and a crosslinking agent in a nitrogen-protected environment to obtain an OCA optical adhesive. The photoinitiator can be 11732-hydroxyl-2 -Methyl-1-phenylacetone, 1841-hydroxycyclohexyl phenyl ketone, 9072-methyl-2-(4-morpholinyl)-1-[4-(methylthio)phenyl]-1 - Acetone, TPO-2,4,6-trimethylbenzoyl-diphenylphosphine oxide, TPO-L ethyl 2,4,6-trimethylbenzoylphenylphosphonate, IHT-PI 910 2-Dimethylamino-2-benzyl-1-[4-(4-morpholinyl)phenyl]-1-butanone, 6592-hydroxy-2-methyl-1-[4-(2-hydroxy Ethoxy)phenyl]-1-propanone or MBF methyl benzoylformate.

[0023] On the basis of t...

Embodiment 1

[0031] OCA optical glue, including 65 parts of 2-ethylhexyl acrylate, 14.5 parts of isobornyl acrylate, 20 parts of 2-hydroxyethyl acrylate, 0.5 parts of 1-hydroxycyclohexyl benzophenone and 0.2 parts of molecular weight control agent ten dithiol.

[0032] The preparation method of OCA optical glue, including OCA optical glue, also includes the following steps:

[0033] Step 1: Mix 65 parts of 2-ethylhexyl acrylate, 14.5 parts of isobornyl acrylate, 20 parts of 2-hydroxyethyl acrylate, 0.5 parts of 1-hydroxycyclohexyl benzophenone and 0.2 parts of dodecanethiol Obtain monomer prepolymer;

[0034] Step 2: Add 11732-hydroxyl-2-methyl-1-phenylacetone and multifunctional cross-linking agent to the monomer prepolymer obtained in step 1 by exposing to ultraviolet radiation in a nitrogen-protected environment to make the monomer prepolymer The polymer is partially polymerized to obtain a prepolymer having a viscosity of about 300-10,000 centipoise.

[0035] On the basis of the abo...

Embodiment 2

[0045] OCA optical glue, including 45 parts of 2-ethylhexyl acrylate, 30 parts of isobornyl acrylate, 24.2 parts of 2-hydroxyethyl acrylate, 0.8 parts of 1-hydroxycyclohexyl benzophenone and 0.5 parts of molecular weight control agent ten dithiol.

[0046] The preparation method of OCA optical glue, including OCA optical glue, also includes the following steps:

[0047] Step 1: Mix 45 parts of 2-ethylhexyl acrylate, 30 parts of isobornyl acrylate, 24.2 parts of 2-hydroxyethyl acrylate, 0.8 parts of 1-hydroxycyclohexyl benzophenone and 0.5 parts of dodecanethiol Obtain monomer prepolymer;

[0048] Step 2: The monomer prepolymer obtained in step 1 is exposed to ultraviolet radiation and added with a 1841-hydroxycyclohexyl phenyl ketone photoinitiator and a trifunctional crosslinking agent under a nitrogen-protected environment to make the monomer prepolymer Partial polymerization, during the polymerization reaction, put a photometer for ultraviolet energy testing next to it, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an OCA optical adhesive, a preparation method and application of the OCA optical adhesive. The OCA optical adhesive comprises 2-ethylhexyl acrylate, isobornyl acrylate, 2-hydroxyethyl acrylate, 1-hydroxycyclohexyl benzophenone and a molecular weight control agent dodecanethiol. The preparation method of the OCA optical adhesive comprises the following steps of 1, mixing 2-ethylhexyl acrylate, isobornyl acrylate, 2-hydroxyethyl acrylate, 1-hydroxycyclohexyl benzophenone and dodecanethiol to obtain a monomer prepolymer, 2, exposing the monomer prepolymer to ultraviolet radiation in a nitrogen protection environment, and adding a photoinitiator and a cross-linking agent to obtain an OCA optical adhesive. The application of the OCA optical adhesive comprises the following steps of A, unwinding a release film, B, coating the release film with OCA optical adhesive to obtain the release film coated with the OCA optical adhesive, C, curing the release film coated with the OCA optical adhesive under illumination to obtain a cured optical adhesive film, and D, winding the cured optical adhesive film.

Description

technical field [0001] The invention relates to the field of adhesives, in particular to an OCA optical glue, a preparation method and application of the OCA optical glue. Background technique [0002] At present, most adhesives on the market are thermally polymerized by heating in a reactor. During the production heating process, accompanied by solvent reflux, pressure rise, etc., some of them are produced by UV ultraviolet light polymerization. Yes, but the production process cannot be controlled during the production process, and the polymer conversion rate during the polymerization process cannot be controlled. Contents of the invention [0003] The technical problem to be solved by the invention is to provide an OCA optical adhesive with controllable conversion rate, a preparation method and application of the OCA optical adhesive. [0004] The technical solution adopted by the present invention to solve its technical problems is: OCA optical glue, including 2-ethylh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/08C08F220/18C08F220/20C09J7/10
CPCC09J133/066C08F220/1808C09J7/10
Inventor 刘晓阳金成国
Owner 世星科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More