Flame-retardant terylene main yarn and preparation process thereof
A flame-retardant polyester and preparation technology, which is applied in the field of spinning, can solve the problems of difficult blocking, complex mechanism, and large degree of fiber damage during smoldering time, so as to achieve good flame-retardant effect, improve flame-retardant effect, and reduce coordination key effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] Embodiment 1: A kind of flame-retardant polyester mother silk,
[0041] It is prepared from polyester fiber masterbatch and 2,4,6-tribromophenyl zinc borate. The polyester fiber masterbatch is polyethylene terephthalate masterbatch, 2,4,6-tribromophenyl zinc borate is made from 2,4,6-tribromophenylboronic acid and zinc oxide, 2,4 , The mass ratio of 6-tribromophenylboronic acid to zinc oxide is 3:1. The specific components and their corresponding dosages used in the flame-retardant polyester mother silk are shown in Table 1.
[0042] The above-mentioned flame-retardant polyester mother silk is prepared by the following process:
[0043]S1: Weigh 15kg of 2,4,6-tribromophenylboronic acid and dissolve it in 8L of ethanol, then add 5kg of zinc oxide to the system, heat at 95°C and condense to reflux, react for 10 hours and filter while hot A solid crystal was obtained, which was washed with water to obtain 2,4,6-tribromophenyl zinc borate.
[0044] S2: Weigh the amount ...
Embodiment 2-5
[0047] Embodiment 2-5: a kind of flame-retardant polyester mother silk,
[0048] The difference from Example 1 is that the amounts of polyester fiber masterbatch and 2,4,6-tribromophenyl zinc borate are different, and the specific amounts are shown in Table 1 below.
Embodiment 6
[0049] Embodiment 6: A kind of flame-retardant polyester mother silk,
[0050] The difference from Example 1 is that the raw material also includes 40 kg of phosphoric acid ester, and the phosphoric acid ester is specifically selected from tricresyl phosphate.
[0051] Prepared by the following process:
[0052] S1: Weigh 15kg of 2,4,6-tribromophenylboronic acid and dissolve it in 8L of ethanol, then add 5kg of zinc oxide to the system, heat at 95°C and condense to reflux, react for 10 hours and filter while hot Obtain solid crystals, and obtain 2,4,6-tribromophenyl zinc borate after washing with water;
[0053] S2: Weigh the amount of 2,4,6-tribromophenyl zinc borate in Table 1, mix it with polyethylene terephthalate masterbatch in a stirring tank, and then send the mixture into the screw for extrusion In the machine, the mixture is heated and melted at a temperature of 300°C;
[0054] S3: Spinning the melt-mixed mixture through a spinneret, and obtaining primary fibers af...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com