A technology for decorative panels and thermosetting resins, applied in the field of home decoration materials, can solve the problem that the surface protective layer cannot penetrate, and achieve the effects of good anti-pollution, improved wear resistance, and increased surface density and hardness

Pending Publication Date: 2021-01-22
广东和丰创美新型材料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels, which solves the problem that the existing surface protection layer cannot penetrate into the interior of the floor or home decoration panels to protect the floor or home decoration panels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels and preparation method thereof
  • Paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels and preparation method thereof
  • Paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: This embodiment provides a paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels, which is prepared from the following components in parts by weight: 80 parts of thermosetting resin solution, nanometer 5 parts of infrared ceramic solution, 8 parts of nano-flame retardant, 0.5 part of surface treatment agent, 0.2 part of anti-UV and anti-yellowing additive, 0.5 part of penetrating agent, 0.1 part of antioxidant, 2 parts of negative oxygen ion additive, 0.1 part of mold antibacterial agent, the nano-far-infrared ceramic solution is mixed by nano-alumina and nano-zirconia in a ratio of 1:1, and the nano-flame retardant is 3 parts of nano-Mg(OH) 2 , 3 parts of nano-Al(OH) 3 and 2 parts of zinc borate, the penetrant is a mixture of 0.3 parts of isooctyl alcohol polyoxyethylene ether phosphate and 0.2 parts of sodium alkylaryl sulfonate, the antioxidant is sodium sulfite, and the anti-mildew The antibacterial...

Embodiment 2

[0031] Embodiment 2: This embodiment provides a paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels, which is prepared from the following components in parts by weight: 83 parts of thermosetting resin solution, nanometer 8 parts of infrared ceramic solution, 7 parts of nano-flame retardant, 0.8 parts of surface treatment agent, 0.3 parts of anti-UV and anti-yellowing additives, 0.6 parts of penetrating agent, 0.2 parts of antioxidant, 3 parts of negative oxygen ion additives, 0.1 part of mold antibacterial agent, the nano-far-infrared ceramic solution is mixed by nano-alumina, nano-zirconia and nano-silicon dioxide in a ratio of 3:2:3, and the nano-flame retardant is 4 parts Nano Mg(OH) 2 , 1 nanometer Al(OH) 3It is mixed with 1 part of ammonium polyphosphate plus 1 part of melamine phosphate, the penetrant is a mixture of 0.4 part of isooctyl alcohol polyoxyethylene ether phosphate and 0.2 part of sodium alkylaryl sulfon...

Embodiment 3

[0032] Embodiment 3: This embodiment provides a paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels, which is prepared from the following components in parts by weight: 88 parts of thermosetting resin solution, nanometer 8 parts of infrared ceramic solution, 7 parts of nano-flame retardant, 1.0 part of surface treatment agent, 0.5 parts of anti-UV and anti-yellowing additives, 0.9 parts of penetrating agent, 0.3 parts of antioxidant, 6 parts of negative oxygen ion additives, 0.5 part of mildew antibacterial agent, the nano far-infrared ceramic solution is mixed by nano aluminum oxide and nano silicon dioxide in a ratio of 1:1, and the nano flame retardant is 2 parts of nano Mg(OH) 2 , 2 parts of nano-Al(OH) 3 , 2 parts of expanded graphite and 1 part of triglycidyl isocyanurate, the penetrating agent is 0.5 part of isooctyl polyoxyethylene ether phosphate, 0.2 part of alkyl sodium sulfate and 0.2 part of alkyl aryl sulfona...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels and a preparation method thereof. The resin is prepared from the following components in parts by weight: 80-100 parts of a thermosetting resin solution, 5-25 parts of a nano far-infrared ceramic solution or nano far-infrared ceramic powder, 2-8 parts of a nano flame retardant, 0.5-3 parts of a surface treating agent, 0.2-2.0 parts of an anti-UV and anti-yellowing aid, 0.5-2.8 parts of a penetrating agent, 0.1-0.6 part of an antioxidant, 2-10 parts of a negative oxygen ion aid and 0.1-2.5 parts of a mildew-antibacterial agent. By adding the penetrant, the prepared paint-free multifunctional permeable thermosetting nano resin can permeate into a floor or a homedecoration panel when being coated on the floor or the home decoration panel, and not only stays on the surface, but also can effectively protect the floor or the home decoration panel after a protective layer on the surface is abraded; the problem that the surface protection layer cannot protect the floor or the home decoration panel is solved.

Description

【Technical field】 [0001] The invention relates to the technical field of home decoration materials, in particular to a paint-free multifunctional permeable thermosetting nano resin applied to floors and home decoration panels and a preparation method thereof. 【Background technique】 [0002] Floor and home decoration panels are products that are often used in people's lives. The surface of existing floor and home decoration panels is generally coated with a layer of waterproof, wear-resistant and anti-corrosion surface protection layer to protect floors or home decoration. panel. The surface protection layer is generally made of resin materials mixed with other functional additives. The existing surface protection layer can only be bonded to the surface of solid wood or composite wood flooring or home decoration panels, and will not penetrate into the floor or home decoration panels. Inside, the floor or home improvement panels cannot be protected after the protective layer ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L61/28C08L71/02C08K13/02C08K3/22C08K3/36C08K5/3475C09D161/28C09D5/14C09D7/61C09D7/63C09D7/65
CPCC08L61/28C09D161/28C09D5/14C09D7/61C09D7/63C09D7/65C08K2201/011C08L2201/08C08K2003/2227C08K2003/2244C08L71/02C08K13/02C08K3/22C08K3/36C08K5/3475
Inventor 王灿义张晓峰杨创会钟启新
Owner 广东和丰创美新型材料有限公司